Reinforced polyarylene esters
Assignee: Monsanto Co
•
Filing: 1978-07-14
•
Granted: 1980-04-22
•
Expires: 1998-07-14
Abstract
Abstract Molding resins are disclosed which comprise a polyarylene ester containing recurring units derived from 1,2-bis(4-hydroxyphenyl)ethane, an inorganic reinforcing agent and a thermoplastic vinyl addition polymer. The reinforcing agent preferably comprises capsules in which glass fiber strands are encapsulated in collimated array within the thermoplastic vinyl addition polymer.
Inventors
- 👤 Massimo Baer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:58
CPC Classifications
C; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/14; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/16; C08G63/18; C08G63/19; C08G63/193; C08K3/00; C08K3/40; C08K9/00; C08K9/04; C08L; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08L67/00; C08L67/02; C08L67/03
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
147 words
A molding resin comprising an intimate blend of a polyacrylene ester, a reinforcing agent and a vinyl addition polymer wherein the polyarylene ester consists essentially of units derived from 1,2-bis(4-hydroxyphenyl)ethane and at least one C 8 to C 25 aromatic dicarboxylic acid, wherein the inherent viscosity of the polyarylene ester at 30° C. determined at a concentration of 0.5 grams polyester per 100 ml solution in a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of sym-tetrachloroethane is at least about 0.5, the melting point is less than about 350° C. and the rate of crystallization is at least about 0.2 minutes -1 , and wherein the reinforcing agent is present in an amount effective to reinforce the polyarylene ester and the vinyl addition polymer is present in an amount effective to reduce the melt viscosity of the reinforced polyarylene ester.
Claim 2
Dependent Claim
147 words
A molding resin comprising an intimate blend of a polyacrylene ester, a reinforcing agent and a vinyl addition polymer wherein the polyarylene ester consists essentially of units derived from 1,2-bis(4-hydroxyphenyl)ethane and at least one C 8 to C 25 aromatic dicarboxylic acid, wherein the inherent viscosity of the polyarylene ester at 30° C. determined at a concentration of 0.5 grams polyester per 100 ml solution in a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of sym-tetrachloroethane is at least about 0.5, the melting point is less than about 350° C. and the rate of crystallization is at least about 0.2 minutes -1 , and wherein the reinforcing agent is present in an amount effective to reinforce the polyarylene ester and the vinyl addition polymer is present in an amount effective to reduce the melt viscosity of the reinforced polyarylene ester.
Claim 3
Dependent Claim
36 words
The molding resin of claim 1 wherein the vinyl addition polymer has a glass transition temperature of at least 70° C. and a number average molecular weight in the range of about 10,000 to about 200,000.
Claim 4
Dependent Claim
26 words
The molding resin of claim 2 wherein the vinyl addition polymer has a number average molecular weight in the range of about 20,000 to about 80,000.
Claim 5
Dependent Claim
43 words
The molding resin of claims 2 or 3 wherein the vinyl addition polymer is selected from the group consisting of homopolymers and copolymers of styrene, homopolymers and copolymers of α-methylstyrene, homopolymers and copolymers of methyl methacrylate, copolymers of acrylonitrile and copolymers of methacrylonitrile.
Claim 6
Dependent Claim
64 words
The molding resin of claim 4 comprising an intimate blend of from about 36 to about 93 parts by weight of polyarylene ester, from about 5 to about 60 parts by weight of reinforcing agent and from about 2 to about 9 parts by weight of vinyl addition polymer wherein the weight ratio of polyarylene ester to vinyl addition polymer is at least 10:1.
Claim 7
Dependent Claim
13 words
The molding resin of claim 5 wherein the reinforcing agent is glass fiber.
Claim 8
Dependent Claim
52 words
The molding resin of claim 6 comprising an intimate blend of the polyarylene ester and glass fiber capsules wherein the glass fiber capsules contain the vinyl addition polymer as the encapsulating agent and the weight ratio of glass to vinyl addition polymer is in the range of about 1:1 to about 9:1.
Claim 9
Dependent Claim
47 words
The molding resin of claim 5 wherein the aromatic dicarboxylic acid is selected from the group consisting of isophthalic acid, terephthalic acid, t-butyl-isophthalic acid, 3,3'-, 3,4'- and 4,4'-bibenzoic acids and bis(carboxyphenyl)ethers, bis(carboxyphenyl)sulfides, bis(carboxyphenyl)sulfones, bis(carboxyphenyl)methanes, 1,2-bis(carboxyphenyl)ethanes, and 2,2-bis(4-carboxyphenyl)propanes, wherein the carboxy groups are in the 3- or 4-positions.
Claim 10
Dependent Claim
48 words
The molding resin of claim 7 wherein the aromatic dicarboxylic acid is selected from the group consisting of isophthalic acid, terephthalic acid, t-butyl-isophthalic acid, 3,3'-, 3,4'- and 4,4'-bibenzoic acids and bis(carboxyphenyl)ethers, bis(carboxyphenyl)sulfides, bis(carboxyphenyl)sulfones, bis(carboxyphenyl)methanes, 1,2-bis(carboxyphenyl)ethanes, and 2,2-bis(4-carboxyphenyl)propanes, wherein the carboxy groups are in the 3- or 4- positions.
Claim 11
Dependent Claim
20 words
The molding resin of claim 5 wherein the polyarylene ester consists essentially of recurring units represented by the formula ##STR2##
Claim 12
Dependent Claim
20 words
The molding resin of claim 7 wherein the polyarylene ester consists essentially of recurring units represented by the formula ##STR3##
Claim 13
Dependent Claim
11 words
A molded article formed from the molding resin of claim 1.
Claim 14
Dependent Claim
11 words
A molded article formed from the molding resin of claim 5.
Claim 15
Dependent Claim
11 words
A molded article formed from the molding resin of claim 7.
Claim 16
Dependent Claim
11 words
A molded article formed from the molding resin of claim 10.
Claim 17
Dependent Claim
11 words
A molded article formed from the molding resin of claim 11.
Claim 18
Dependent Claim
127 words
A process of preparing a reinforced molding resin comprising intimately melt blending a polyarylene ester and a reinforcing amount of a glass fiber reinforcing agent encapsulated in a vinyl addition polymer, wherein the polyarylene ester consists essentially of units derived from 1,2-bis(4-hydroxyphenyl)ethane and at least one C 8 to C 25 aromatic dicarboxylic acid, wherein the inherent viscosity of the polyarylene ester at 30° C. determined at a concentration of 0.5 grams polyester per 100 ml solution in a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of sym-tetrachloroethane is at least about 0.5 and the melting point is less than about 350° C. and wherein the weight ratio of polyarylene ester to vinyl addition polymer is at least about 10:1.
Claim 19
Dependent Claim
127 words
A process of preparing a reinforced molding resin comprising intimately melt blending a polyarylene ester and a reinforcing amount of a glass fiber reinforcing agent encapsulated in a vinyl addition polymer, wherein the polyarylene ester consists essentially of units derived from 1,2-bis(4-hydroxyphenyl)ethane and at least one C 8 to C 25 aromatic dicarboxylic acid, wherein the inherent viscosity of the polyarylene ester at 30° C. determined at a concentration of 0.5 grams polyester per 100 ml solution in a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of sym-tetrachloroethane is at least about 0.5 and the melting point is less than about 350° C. and wherein the weight ratio of polyarylene ester to vinyl addition polymer is at least about 10:1.
Claim 20
Dependent Claim
40 words
The process of claim 17 wherein the vinyl addition polymer is selected from the group consisting of homopolymers and copolymers of styrene, homopolymers and copolymers of α-methylstyrene, homopolymers and copolymers of methyl methacrylate, copolymers of acrylonitrile and copolymers of methacrylonitrile.
Claim 21
Dependent Claim
37 words
The process of claim 18 wherein the glass fiber capsules comprise glass strands having a length in the range of from about 0.8 mm to about 20 mm in substantially collimated array within the vinyl addition polymer.
Claim 22
Dependent Claim
70 words
The process of claim 19 wherein the weight ratio of glass fiber to vinyl addition polymer is in the range of about 1:1 to about 9:1 and the resulting reinforced molding resin comprises from about 36 to about 93 parts by weight polyarylene ester, from about 5 to about 60 parts by weight of glass fiber and from about 2 to about 9 parts by weight of vinyl addition polymer.
References Cited (Backward Citations)
US3635879A
Cited
US3647921A
Cited
US3792118A
Cited
US4064196A
Cited
US4102864A
Cited
US4127557A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |