Method for application of porous wash coats to low porosity refractory catalytic monoliths and the resulting support
Assignee: Motors Liquidation Co
•
Filing: 1975-03-27
•
Granted: 1980-04-22
•
Expires: 1995-03-27
Abstract
Abstract The method for obtaining a tightly adherent, uniformly dispersed porous wash coat by the use of dilute aqueous hydrofluoric acid, 1-5% HF, as an etchant for refractory low porosity catalytic monolith supports to produce substantial improvement of the adhesion, dispersion and uptake characteristics of such supports for porous wash coats. The application of an ultrasonic energy field to the etchant bath greatly accelerates the etching process.
Inventors
- 👤 Louis Hegedus
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:45
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J37/00; B01J37/02; B01J37/024; B01J37/34; B01J37/341; B01J37/343; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
178 words
In a process for production of a high strength and low porosity cordierite catalytic monolith support having an active alumina coating tightly adherent to and evenly dispersed on the surfaces of the thin walls thereof, the steps of immersing the low porosity support in an aqueous hydrofluoric acid bath containing 1-5% by weight acid at a temperature from ambient to about 100° C., etching the surfaces of said support for a period of time sufficient to produce a roughened surface with the removal of not more than about 3% of the weight of the original support, washing said etched support to remove all traces of acid and its water soluble salts, drying said support, immersing said support in a slurry of active alumina or alumina precursor to be applied to its surfaces, draining and air drying said support, and firing said coating support for a period of up to 2-3 hours in air, the strength of said support being substantially retained and said coating being picked-up in sufficient quantity to minimize the need for repeated dip coating operations.
Claim 2
Dependent Claim
178 words
In a process for production of a high strength and low porosity cordierite catalytic monolith support having an active alumina coating tightly adherent to and evenly dispersed on the surfaces of the thin walls thereof, the steps of immersing the low porosity support in an aqueous hydrofluoric acid bath containing 1-5% by weight acid at a temperature from ambient to about 100° C., etching the surfaces of said support for a period of time sufficient to produce a roughened surface with the removal of not more than about 3% of the weight of the original support, washing said etched support to remove all traces of acid and its water soluble salts, drying said support, immersing said support in a slurry of active alumina or alumina precursor to be applied to its surfaces, draining and air drying said support, and firing said coating support for a period of up to 2-3 hours in air, the strength of said support being substantially retained and said coating being picked-up in sufficient quantity to minimize the need for repeated dip coating operations.
Claim 3
Dependent Claim
22 words
A process as set forth in claim 1 wherein the acid concentration is about 2% and treatment is accomplished at ambient temperature.
Claim 4
Dependent Claim
23 words
A process as set forth in claim 1 wherein the acid is subjected to an ultrasonic field during the period of support treatment.
Claim 5
Dependent Claim
23 words
A process as set forth in claim 2 wherein the acid is subjected to an ultrasonic field during the period of support treatment.
Claim 6
Dependent Claim
20 words
A catalytic support monolith suitable for use in control of automotive exhaust emissions prepared by the process of claim 1.
Claim 7
Dependent Claim
20 words
A catalytic support monolith suitable for use in control of automotive exhaust emissions prepared by the process of claim 2.
Claim 8
Dependent Claim
20 words
A catalytic support monolith suitable for use in control of automotive exhaust emissions prepared by the process of claim 3.
Claim 9
Dependent Claim
20 words
A catalytic support monolith suitable for use in control of automotive exhaust emissions prepared by the process of claim 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |