Method of forming corrosion-resistant glassceramic-to-metal seals

Claim 1

A method of making a hermetic plug seal having a metal pin electrode mounted by a corrosion-resistant, hermetic glassceramic-to-metal collar, the seal exhibiting corrosion resistance in an environment of potassium hydroxide, said method comprising the steps of: (a) positioning a glass composition preform, said glass composition having the property of sequentially fluidizing, sealing and ceraming in a single rapid heating step, between and in proximity to the pin and the collar, within an inert atmosphere enclosure, wherein the glass composition preform consists essentially of 25.0-32.0% by weight ZnO, 2.5-10.0% by weight Al 2 O 3 , 30.0-60.0% by weight SiO 2 , 0-10% by weight CaO, 0-14.5% by weight PbO, 0-2.5% by weight P 2 O 5 , 0-10.0% by weight LiO 2 , 0-3.0% by weight Na 2 O, 0-3.0% by weight K 2 O and 0-12.5% by weight ZrO 2 ; (b) rapidly heating in a single heating step the metal pin and collar to cause the glass preform to first heat, by conduction from the metal pin and the metal collar to the glass preform therebetween and radiation, to a temperature below the ceraming temperature of the glass and to fluidize the glass, so that the fluidized glass flows between and adheres to both the pin and collar to form a fluid seal therebetween, wherein the heating rate is sufficient to achieve sealing in a period of less than about 5 minutes while avoiding excessive oxidation of the metal pin and metal collar and to prevent excessive interaction of the glass composition at the glass/collar interface, and when the temperature of the glass reaches about 1000° C. ceraming of the seal occurs; (c) maintaining the temperature at about 1000° C. for about 3.5 to 12 minutes to effect ceraming of the seal; and thereafter (d) cooling the resulting plug seal within the inert atmosphere enclosure to room temperature.

Claim 2

A method of making a hermetic plug seal having a metal pin electrode mounted by a corrosion-resistant, hermetic glassceramic-to-metal collar, the seal exhibiting corrosion resistance in an environment of potassium hydroxide, said method comprising the steps of: (a) positioning a glass composition preform, said glass composition having the property of sequentially fluidizing, sealing and ceraming in a single rapid heating step, between and in proximity to the pin and the collar, within an inert atmosphere enclosure, wherein the glass composition preform consists essentially of 25.0-32.0% by weight ZnO, 2.5-10.0% by weight Al 2 O 3 , 30.0-60.0% by weight SiO 2 , 0-10% by weight CaO, 0-14.5% by weight PbO, 0-2.5% by weight P 2 O 5 , 0-10.0% by weight LiO 2 , 0-3.0% by weight Na 2 O, 0-3.0% by weight K 2 O and 0-12.5% by weight ZrO 2 ; (b) rapidly heating in a single heating step the metal pin and collar to cause the glass preform to first heat, by conduction from the metal pin and the metal collar to the glass preform therebetween and radiation, to a temperature below the ceraming temperature of the glass and to fluidize the glass, so that the fluidized glass flows between and adheres to both the pin and collar to form a fluid seal therebetween, wherein the heating rate is sufficient to achieve sealing in a period of less than about 5 minutes while avoiding excessive oxidation of the metal pin and metal collar and to prevent excessive interaction of the glass composition at the glass/collar interface, and when the temperature of the glass reaches about 1000° C. ceraming of the seal occurs; (c) maintaining the temperature at about 1000° C. for about 3.5 to 12 minutes to effect ceraming of the seal; and thereafter (d) cooling the resulting plug seal within the inert atmosphere enclosure to room temperature.

Claim 5

A method of making a hermetic plug seal for use in a Ni-Cd battery, the seal having a metal pin electrode mounted in and surrounded by a corrosion-resistant, hermetic glassceramic-to-metal seal in a surrounding metal collar, the seal exhibiting corrosion resistance under an environment of potassium hydroxide, said method including the successive steps of: (a) positioning a glass composition preform about said metal pin electrode and within said surrounding metal collar, said glass composition preform consisting essentially of, in percent by weight: ZnO: 25.0-32.0% Al 2 O 3 : 2.5-10.0% SiO 2 : 30.0-60.0% CaO: 0-10% PbO: 0-14.5% P 2 O 5 : 0-2.5% LiO 2 : 0-10% Na 2 O: 0-3% K 2 O: 0-3% Zr 2 O: 0-12.5%, said glass composition capable of sequentially fluidizing, sealing and ceraming in a single rapid heating step; (b) rapidly heating by R.F. induction in an inert atmosphere said metal pin electrode, glass preform and surrounding metal collar in a single heating step to a temperature initially below the ceraming temperature of the glass to sequentially fluidize, seal then ceram the glass preform, such that (i) the fluidized glass flows between and adheres to the electrode pin and surrounding collar to form a fluid seal therebetween while avoiding excessive oxidation of the metal pin and metal collar and to prevent excessive interaction of the glass composition at the glass/collar interface, the rate of heating sufficient to achieve sealing in a period of less than about 5 minutes, and (ii) ceraming of the seal occurs when the temperature of the glass reaches about 1000° C.; (c) maintaining the temperature at about 1000° C. for a period of about 3.5 to about 12 minutes to effect ceraming of the seal; and thereafter (d) cooling the resulting hermetic plug seal in said inert atmosphere to room temperature.

Claim 6

A method of making a hermetic plug seal for use in a Ni-Cd battery, the seal having a metal pin electrode mounted in and surrounded by a corrosion-resistant, hermetic glassceramic-to-metal seal in a surrounding metal collar, the seal exhibiting corrosion resistance under an environment of potassium hydroxide, said method including the successive steps of: (a) positioning a glass composition preform about said metal pin electrode and within said surrounding metal collar, said glass composition preform consisting essentially of, in percent by weight: ZnO: 25.0-32.0% Al 2 O 3 : 2.5-10.0% SiO 2 : 30.0-60.0% CaO: 0-10% PbO: 0-14.5% P 2 O 5 : 0-2.5% LiO 2 : 0-10% Na 2 O: 0-3% K 2 O: 0-3% Zr 2 O: 0-12.5%, said glass composition capable of sequentially fluidizing, sealing and ceraming in a single rapid heating step; (b) rapidly heating by R.F. induction in an inert atmosphere said metal pin electrode, glass preform and surrounding metal collar in a single heating step to a temperature initially below the ceraming temperature of the glass to sequentially fluidize, seal then ceram the glass preform, such that (i) the fluidized glass flows between and adheres to the electrode pin and surrounding collar to form a fluid seal therebetween while avoiding excessive oxidation of the metal pin and metal collar and to prevent excessive interaction of the glass composition at the glass/collar interface, the rate of heating sufficient to achieve sealing in a period of less than about 5 minutes, and (ii) ceraming of the seal occurs when the temperature of the glass reaches about 1000° C.; (c) maintaining the temperature at about 1000° C. for a period of about 3.5 to about 12 minutes to effect ceraming of the seal; and thereafter (d) cooling the resulting hermetic plug seal in said inert atmosphere to room temperature.