Process for fabrication of fuse and interconnects
Assignee: Harris Corp
•
Filing: 1978-08-16
•
Granted: 1980-04-22
•
Expires: 1998-08-16
Abstract
Abstract Fuses and interconnects are fabricated by applying a metallic layer on a substrate and a fusible layer on the metallic layer. Portions of the fusible layer are removed to define discrete fuse elements having a necked portion. Portions of the metallic layer are removed to define interconnects. A portion of the metallic layer coextensive with the necked portion of the fuse elements is removed by selective side etching to form tapering portions separated by a gap without etching of the interconnects. The interconnects are protected from side etching by a separate mask layer or a mask layer used to form the interconnects may be heated to flow down over the sides of the interconnects.
Inventors
- 👤 Hugh C. Nicolay
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:57
CPC Classifications
H; H01; H01H; H01H69/00; H01H69/02; H01H69/022; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49107
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
95 words
A method for fabricating thin film fuses on a substrate comprising: applying a first layer of metallic material on said substrate; applying a second layer of fusible material on said first layer; first selectively removing portions of said second layer to define a fuse element; second selectively removing portions of said first layer, except for portions coextensive with said fuse element, to define interconnects; and third selectively removing a portion of said coextensive portion of said first layer between the ends of said fuse element by side etching without affecting said fuse element and interconnects.
Claim 2
Independent Claim
95 words
A method for fabricating thin film fuses on a substrate comprising: applying a first layer of metallic material on said substrate; applying a second layer of fusible material on said first layer; first selectively removing portions of said second layer to define a fuse element; second selectively removing portions of said first layer, except for portions coextensive with said fuse element, to define interconnects; and third selectively removing a portion of said coextensive portion of said first layer between the ends of said fuse element by side etching without affecting said fuse element and interconnects.
Claim 3
Dependent Claim
63 words
The method according to claim 1 wherein said second selective removal includes forming a mask layer on said substrate to define said interconnects with said fuse element exposed and etching through said mask and wherein said third selective removal includes heating said mask layer sufficiently to flow down over the edge of said interconnects and subsequently etching said portion of said coextensive portions.
Claim 4
Dependent Claim
48 words
The method according to claim 1 wherein said third selective removal includes forming a mask layer on said substrate to expose said fuse element and a portion of said coextensive portion of said first layer while protecting said interconnects and subsequently etching said portion of said coextensive portions.
Claim 5
Dependent Claim
50 words
The method according to claim 1 wherein a layer of positive photosensitive resist material is applied to said first layer and exposed to define said fuse element before the application of said second layer and said first removal includes removing said resist material and coextensive portion of said second layer.
Claim 6
Dependent Claim
31 words
The method according to claim 1 wherein said first layer is aluminum and said second layer is a nickel-chromium alloy and said second and third removals include etching with phosphoric acid.
Claim 7
Dependent Claim
54 words
The method according to claim 1 wherein said fuse element is defined to have a necked portion between its ends and said side etching performed to remove said coextensive portion of said first layer to form tapering portions of said first layer extending from opposed interconnects below said necked portion separated by a gap.
Claim 8
Independent Claim
120 words
A method of fabricating thin film fuses and interconnects on a substrate comprising: applying a first layer of metallic material on said substrate; applying a second layer of fusible material on said substrate; selectively removing portions of said second layer to define a discrete fuse element; applying a mask layer on said substrate to define interconnects with said fuse element exposed; etching through openings in said mask layer to form said interconnects; heating said mask layer sufficiently to flow down over the edges of said interconnects; and side etching exposed portion of said first layer coextensive with said fuse element to remove a sufficient portion of said exposed portion of said first layer to form a gap under said fuse.
Claim 9
Independent Claim
120 words
A method of fabricating thin film fuses and interconnects on a substrate comprising: applying a first layer of metallic material on said substrate; applying a second layer of fusible material on said substrate; selectively removing portions of said second layer to define a discrete fuse element; applying a mask layer on said substrate to define interconnects with said fuse element exposed; etching through openings in said mask layer to form said interconnects; heating said mask layer sufficiently to flow down over the edges of said interconnects; and side etching exposed portion of said first layer coextensive with said fuse element to remove a sufficient portion of said exposed portion of said first layer to form a gap under said fuse.
Claim 10
Dependent Claim
52 words
The method according to claim 7 wherein a layer of positive photosensitive resist material is applied to said first layer and exposed to define said fuse element before the application of said second layer and removal of said second layer includes removing said resist material and coextensive portion of said second layer.
Claim 11
Dependent Claim
55 words
The method according to claim 7 wherein said fuse element is defined to have a necked portion between its ends and said side etching is performed to remove said coextensive portion of said first layer to form tapering portions of said first layer extending between opposed interconnects below said necked portion separated by a gap.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |