Method for the manufacture of tools, machines or parts thereof by composite sintering
Assignee: Thyssen Stahl AG
•
Filing: 1978-04-20
•
Granted: 1980-04-15
•
Expires: 1998-04-20
Abstract
Abstract Described herein is a method for the manufacture of materials such as tools, machines or parts thereof composed of at least two sections joined together by composite sintering from sintered alloys with an iron, nickel or cobalt base wherein at least two powdered metallic mixtures having differing metal carbide contents are separately prepared and poured, one after the other, into a mold and then formed into a pressed body; the pressed body is then sintered at the lowest temperature sufficient to cause alloy formation in the mixture having the lowest sintering temperature, and then hot-pressed to complete alloy formation in the pressed body and achieve maximum density.
Inventors
- 👤 Fritz Frehn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:39
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/06; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12146
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
132 words
A method for the manufacture of tools, machines or parts thereof adapted to exhibit both resistance to wear and toughness, said method comprising: (a) separately preparing at least two metallic powder mixtures, each mixture comprised of a base metal selected from the group consisting of iron, nickel, cobalt and mixture thereof, said mixtures having dissimilar weight contents of metal carbide; (b) admitting said mixtures, one after the other into a mold and forming the mixtures into a pressed body; (c) sintering said pressed body in a vacuum at the lowest temperature sufficient to cause alloy formation in the mixture having the lowest sintering temperature; and (d) hot-pressing the partially sintered pressed body of (c) to cause alloy formation in the unsintered sections thereof and thereby achieve maximum density of said pressed body.
Claim 2
Independent Claim
132 words
A method for the manufacture of tools, machines or parts thereof adapted to exhibit both resistance to wear and toughness, said method comprising: (a) separately preparing at least two metallic powder mixtures, each mixture comprised of a base metal selected from the group consisting of iron, nickel, cobalt and mixture thereof, said mixtures having dissimilar weight contents of metal carbide; (b) admitting said mixtures, one after the other into a mold and forming the mixtures into a pressed body; (c) sintering said pressed body in a vacuum at the lowest temperature sufficient to cause alloy formation in the mixture having the lowest sintering temperature; and (d) hot-pressing the partially sintered pressed body of (c) to cause alloy formation in the unsintered sections thereof and thereby achieve maximum density of said pressed body.
Claim 3
Dependent Claim
56 words
The method according to claim 1 wherein first and second metallic powder mixtures are utilized, said first mixture having a metal carbide content in the range of from about 25 to about 80% by weight and said second mixture having a metal carbide content from 0% to an amount less than that of said first mixture.
Claim 4
Dependent Claim
42 words
The method according to claim 2 wherein the metal carbide content of said first mixture is from about 50% to about 80% by weight and the metal carbide content of said second mixture is from about 0 to about 33% by weight.
Claim 5
Independent Claim
17 words
The method according to any of claims 2 or 3 wherein said metal carbide comprises titanium carbide.
Claim 6
Independent Claim
37 words
The method according to any of claims 2 or 3 wherein said metal carbide comprises titanium carbide and one or more carbides of a metal selected from the group consisting of chromium, vanadium, niobium, tantalum and zirconium.
Claim 7
Dependent Claim
23 words
The metal according to claim 5 wherein said titanium carbide comprises at least 50% by weight of the total content of metal carbide.
Claim 8
Dependent Claim
40 words
The method according to claim 1 wherein first, second and third powder mixtures are utilized; said mixtures having, respectively, metal carbide contents in the range of about 50% to about 80%; 20% to 35%; and 0%, all percents by weight.
Claim 9
Dependent Claim
57 words
The method according to claim 1 wherein said hot-pressing takes place in an inert gas at a pressure in the range of from about 1000 to about 2000 and a temperature in the range of from about 100° to about 300° C. lower than the lowest temperature at which the mixture having the lowest sintering temperature sinters.
References Cited (Backward Citations)
US2899338A
Cited
US2175899A
Cited
US2313227A
Cited
US2582231A
Cited
US2769611A
Cited
US2950523A
Cited
US3010196A
Cited
US3311507A
Cited
US3165822A
Cited
US3697261A
Cited
US3761257A
Cited
US3837068A
Cited
US3836341A
Cited
US3999954A
Cited
US4049876A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-15 | 1983-10-15 | 1984-04-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-15 | 1987-10-15 | 1988-04-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-15 | 1991-10-15 | 1992-04-15 | $7700.00 | Window Closed / Lapsed |