Method for applying protective coating to metal pipes
Assignee: Ukrainsky Nauchno-Issle Inst Spetsialnykh Stalei Splavov I Ferro
•
Filing: 1978-12-21
•
Granted: 1980-04-08
•
Expires: 1998-12-21
Abstract
Abstract A method comprises diffusion metal coating of pipes carried out in a vacuum chamber which contains metal evaporators. Prior to coating process a metal is fed into the interior of each pipe with the melting temperature thereof being substantially below that of the pipe metal. The metal coating of pipes is effected at a temperature above the melting temperature of the metal disposed within the pipes which are continuously rotating about their axes while axially advancing through the metal evaporator.
Inventors
- 👤 Vladimir I. Savchenko
- 👤 Anatoly I. Plyshevsky
- 👤 Evgeny P. Ponomarenko
- 👤 Grigory D. Duply
- 👤 Georgy I. Khaustov
- 👤 Iosif J. Korobochkin
- 👤 Olga S. Vilyams
- 👤 Jury K. Belov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:48
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/24; C23C14/56; C23C14/562
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
112 words
A method for applying a protective coating to the external and internal surfaces of metal pipes, comprising disposing a metallizing agent in the interior of each pipe, said agent having a melting temperature below the melting temperature of the pipe, longitudinally advancing each pipe through a vacuum chamber while the pipes are rotating about their axis, coating by metal diffusion the external surface of the pipe in the vacuum chamber using a metal evaporator, utilizing the heat of the pipe during the metal coating of the external surface of the pipe to melt the metallizing agent disposed in the interior of the pipe thereby simultaneously coating the internal surface of each pipe.
Claim 2
Independent Claim
112 words
A method for applying a protective coating to the external and internal surfaces of metal pipes, comprising disposing a metallizing agent in the interior of each pipe, said agent having a melting temperature below the melting temperature of the pipe, longitudinally advancing each pipe through a vacuum chamber while the pipes are rotating about their axis, coating by metal diffusion the external surface of the pipe in the vacuum chamber using a metal evaporator, utilizing the heat of the pipe during the metal coating of the external surface of the pipe to melt the metallizing agent disposed in the interior of the pipe thereby simultaneously coating the internal surface of each pipe.
Claim 3
Dependent Claim
32 words
A method as claimed in claim 1, wherein the melting temperature of the metal being evaporated is above the melting temperature of the metal fed into the interior of each said pipe.
Claim 4
Dependent Claim
27 words
A method as claimed in claim 1, wherein the metal coating process is carried out at a temperature above the melting temperature of the metal being evaporated.
Claim 5
Dependent Claim
55 words
A method as claimed in claim 1, wherein in the course of the metal coating process the head portion of each said pipe is raised relative to the end portion thereof so that its longitudinal axis forms with horizontal plane an angle of not more than 15 deg in the traveling direction of said pipes.
Claim 6
Dependent Claim
17 words
A method as claimed in claim 1, wherein the speed of rotation of said pipes is variable.
References Cited (Backward Citations)
GB260491A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-08 | 1983-10-08 | 1984-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-08 | 1987-10-08 | 1988-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-08 | 1991-10-08 | 1992-04-08 | $7700.00 | Window Closed / Lapsed |