Process for producing polyesters having a high degree of polymerization
Assignee: Teijin Ltd
•
Filing: 1978-07-11
•
Granted: 1980-04-01
•
Expires: 1998-07-11
Abstract
Abstract An improved process for producing a linear polyester having a high degree of polymerization which comprises first preparing a prepolymer of polyester and then polycondensing the prepolymer. In the first step, a prepolymer having an intrinsic viscosity of at least 0.2 is prepared, and the subsequent polycondensation is carried out in the presence of an organic boron compound of the formula ##STR1## wherein R 1 , R 2 , R 3 and R 4 represent an alkyl, aralkyl or aryl group having 6 to 20 carbon atoms, and M represents a monovalent metal. According to this method, the polycondensation can be performed at atmospheric pressure, and a substantially linear polyester having an intrinsic viscosity of at least 0.5 and superior thermal stability can be obtained rapidly.
Inventors
- 👤 Shizuo Azuma
- 👤 Noritsugu Saiki
- 👤 Shoji Kawase
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 03:53
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G63/82; C08G63/84
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
206 words
A process for producing a polyester having a high degree of polymerization with an intrinsic viscosity, measured at 35° C. in o-chlorophenol, of at least 0.5, which comprises melt polymerizing at least one dicarboxylic or hydroxycarboxylic acid or its ester-forming derivative with at least one dihydric alcohol or its ester-forming derivative to form a linear polyester prepolymer having an intrinsic viscosity, measured at 35° C. in o-chlorophenol, of at least 0.2, and further polycondensing the prepolymer; wherein the polycondensation of the prepolymer is carried out in the presence of at least one organic boron compound selected from compounds of the general formula ##STR3## wherein R 1 , R 2 and R 3 are identical or different, and each represents an alkyl group having 6 to 20 carbon atoms, an aralkyl group having 6 to 20 carbon atoms, or an aryl group having 6 to 20 carbon atoms, and compounds of the general formula ##STR4## wherein R 1 , R 2 , R 3 and R 4 are identical or different, and each represent an alkyl group having 6 to 20 carbon atoms, an aralkyl group having 6 to 20 carbon atoms, or an aryl group having 6 to 20 carbon atoms, M represent a monovalent metal.
Claim 2
Dependent Claim
206 words
A process for producing a polyester having a high degree of polymerization with an intrinsic viscosity, measured at 35° C. in o-chlorophenol, of at least 0.5, which comprises melt polymerizing at least one dicarboxylic or hydroxycarboxylic acid or its ester-forming derivative with at least one dihydric alcohol or its ester-forming derivative to form a linear polyester prepolymer having an intrinsic viscosity, measured at 35° C. in o-chlorophenol, of at least 0.2, and further polycondensing the prepolymer; wherein the polycondensation of the prepolymer is carried out in the presence of at least one organic boron compound selected from compounds of the general formula ##STR3## wherein R 1 , R 2 and R 3 are identical or different, and each represents an alkyl group having 6 to 20 carbon atoms, an aralkyl group having 6 to 20 carbon atoms, or an aryl group having 6 to 20 carbon atoms, and compounds of the general formula ##STR4## wherein R 1 , R 2 , R 3 and R 4 are identical or different, and each represent an alkyl group having 6 to 20 carbon atoms, an aralkyl group having 6 to 20 carbon atoms, or an aryl group having 6 to 20 carbon atoms, M represent a monovalent metal.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein the amount of the organic boron compound is 0.05 to 10 mole% based on the dicarboxylic or hydroxycarboxylic acid or its ester-forming derivative constituting the polyester.
Claim 4
Dependent Claim
46 words
The process of claim 1 wherein the organic boron compound is selected from the group consisting of tricyclohexyl boron, tribenzyl boron, trinaphthyl boron, trimesityl boron, triphenyl boron, lithium tetraphenyl boron, sodium tetraphenyl boron, potassium tetraphenyl boron, copper tetraphenyl boron, sodium tetrabenzyl boron, and sodium tetracyclohexyl boron.
Claim 5
Dependent Claim
29 words
The process of claim 1 wherein the polycondensation of the prepolymer is carried out by heating it in the molten state at atmospheric pressure or at an elevated pressure.
Claim 6
Dependent Claim
126 words
A polyester composition stabilized against oxidation at high temperatures, said composition comprising (1) 100 parts by weight of a linear polyester having an intrinsic viscosity, measured at 35° C. in o-chlorophenol, of at least 0.5, said polyester being prepared by melt polymerizing of at least one dicarboxylic or hydroxycarboxylic acid or its ester-forming derivative with at least one dihydric alcohol or its ester-forming derivative, and (2) 0.001 to 5.0 parts by weight of an organic boron compound of the following formula ##STR5## wherein R 1 , R 2 and R 3 are identical or different, and each represents an alkyl group having 6 to 20 carbon atoms, an aralkyl group having 6 to 20 carbon atoms, or an aryl group having 6 to 20 carbon atoms.
Claim 7
Dependent Claim
126 words
A polyester composition stabilized against oxidation at high temperatures, said composition comprising (1) 100 parts by weight of a linear polyester having an intrinsic viscosity, measured at 35° C. in o-chlorophenol, of at least 0.5, said polyester being prepared by melt polymerizing of at least one dicarboxylic or hydroxycarboxylic acid or its ester-forming derivative with at least one dihydric alcohol or its ester-forming derivative, and (2) 0.001 to 5.0 parts by weight of an organic boron compound of the following formula ##STR5## wherein R 1 , R 2 and R 3 are identical or different, and each represents an alkyl group having 6 to 20 carbon atoms, an aralkyl group having 6 to 20 carbon atoms, or an aryl group having 6 to 20 carbon atoms.
References Cited (Backward Citations)
US3328355A
Cited
US3391123A
Cited
US3530098A
Cited
US3644217A
Cited
US3904707A
Cited
US4116931A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-01 | 1983-10-01 | 1984-04-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-01 | 1987-10-01 | 1988-04-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-01 | 1991-10-01 | 1992-04-01 | $7700.00 | Window Closed / Lapsed |