Fabrication multiphase plastics from liquid suspension

Assignee: Individual
•
Filing: 1978-01-27
•
Granted: 1980-04-01
•
Expires: 1998-01-27
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A process is disclosed for fabricating a thermoplastic, which thermoplastic is either a thermoplastic ionomer or a multiphase graft or block copolymer of the ABA (AB) n , or ##STR1## wherein n is greater than 1 and wherein the polymer blocks, A and B, are each thermoplastic resins having softening points substantially above room temperature with the B block being present in at least about 30 wt. % of the total polymer. The thermoplastic composition is first suspended in finely divided form in a liquid medium in a sufficient amount such that the solids content of the resulting suspension is in the range of from about 15 to about 75 wt. %. The liquid medium must be nonvolatile and must be capable of plasticizing the B block (or the backbone if the ionomer is employed) of the thermoplastic composition above the softening point of that block but must not be capable of plasticizing the A block to a substantial extent. The suspension is then applied as a coating to any desired surface, e.g., to wire, textiles, the interior of a mold, etc., and that surface is heated to a temperature at least 5° above the softening point of either polymer block thereby solidifying the composition in the shape of said surface. The process is useful in wire coatings, coatings on textiles, preparation of leather-like upholstery, flexible sheets, toys, etc.

Inventors

  • 👤 Robert D. Lundberg
  • 👤 Henry S. Makowski

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-03 10:15
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/18; C08F; C08F297/00; C08F297/02; Y; Y10; Y10S; Y10S260/00; Y10S260/31

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 187 words
A process for fabricating an article from a thermoplastic composition, said thermoplastic composition being a thermoplastic ionomer, that is, a polymer having a backbone composed of a thermoplastic resin and having polar groups pendant to that backbone, which comprises the steps of: (a) suspending said thermoplastic composition in finely divided form in a liquid medium in such amount that solids content of the resulting suspension is in the range of from about 15 to about 75 wt. %; said liquid medium being nonvolatile and being capable of plasticizing the backbone near or above the softening point of that backbone; (b) applying said suspension to a surface; (c) heating said surface to a temperature at least approximately equal to that of the softening point of said backbone; (d) cooling said heated surface to a temperature below that of the softening point of said backbone to form said article in a gelled state; and (e) heating at a later time said article in said gelled state to a temperature of about equal to that of the higher softening point of said thermoplastic ionomer to cause curing of said article.
Claim 2
Dependent Claim 187 words
A process for fabricating an article from a thermoplastic composition, said thermoplastic composition being a thermoplastic ionomer, that is, a polymer having a backbone composed of a thermoplastic resin and having polar groups pendant to that backbone, which comprises the steps of: (a) suspending said thermoplastic composition in finely divided form in a liquid medium in such amount that solids content of the resulting suspension is in the range of from about 15 to about 75 wt. %; said liquid medium being nonvolatile and being capable of plasticizing the backbone near or above the softening point of that backbone; (b) applying said suspension to a surface; (c) heating said surface to a temperature at least approximately equal to that of the softening point of said backbone; (d) cooling said heated surface to a temperature below that of the softening point of said backbone to form said article in a gelled state; and (e) heating at a later time said article in said gelled state to a temperature of about equal to that of the higher softening point of said thermoplastic ionomer to cause curing of said article.
Claim 3
Dependent Claim 18 words
The process of claim 1 wherein said polar groups are temporarily plasticized during processing by a preferential plasticizer.
Claim 4
Dependent Claim 41 words
The process of claim 2 wherein said preferential plasticizer is dispersable in the ionomer, is liquid during processing of the ionomer and possesses at least one functional constituent which exhibits a bond moment whose absolute value is at least 0.6 debyes.
Claim 5
Dependent Claim 16 words
The process of claim 1 wherein the solids content is from 30 to 65 wt. %.
Claim 6
Dependent Claim 28 words
The process of claim 1 which additionally comprises the subsequent step of cooling said heated surface to a temperature below that of the softening point of said backbone.
Claim 7
Dependent Claim 35 words
The process of claim 1, wherein said polar groups are prepared by neutralizing acid groups selected from the group comprising carboxylic acid, sulfonic acid and phosphonic acid with base metal compounds or basic nitrogen compounds.
Claim 8
Dependent Claim 23 words
The process of claim 6, wherein said basic metal compounds are selected from the group comprising of alkali and alkaline earth metal compounds.
Claim 9
Dependent Claim 22 words
The process of claim 1, wherein said thermoplastic ionomer is selected from the group comprising sulfonated polystyrene, sulfonated poly-t-butylstyrene and copolymers thereof.

References Cited (Backward Citations)

US1249770A Cited
US3097961A Cited
US3642728A Cited
US4086296A Cited
US4053548A Cited
US3925280A Cited
US3947387A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1983-04-01 1983-10-01 1984-04-01 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1987-04-01 1987-10-01 1988-04-01 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1991-04-01 1991-10-01 1992-04-01 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag