Electroless tin and tin-lead alloy plating baths
Assignee: TE Connectivity Corp
•
Filing: 1977-12-05
•
Granted: 1980-03-25
•
Expires: 1997-12-05
Abstract
Abstract An aqueous bath useful in, and methods for, immersion plating of tin and tin-lead alloys which give greatly increased deposition rates and thicker coatings of better quality accomplished by incorporating into immersion plating tin bath compositions soluble plumbous salts in the amount from 0.5 grams per liter calculated on the basis of elemental lead to the maximum amount soluble in the bath and a sulphur-containing complexing agent for the tin and lead such as thiourea or a thiourea-type derivative; the bath solution contains stannous chloride, lead chloride, sodium hypophosphite (as a solubility enhancer) and with hydrochloric acid used as an agent for adjusting the pH in the resulting bath from 0.5 to 1.0.
Inventors
- 👤 Thomas F. Davis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 17:27
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/48; H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3473
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
181 words
An aqueous bath suitable for immersion deposition of essentially tin and tin-lead alloys onto copper or copper alloy substrates, said bath comprising: (a) a soluble plumbous salt in an amount from about 0.5 grams to about 25 grams per liter calculated on the basis of elemental lead including the maximum soluble in said bath; (b) tin as a soluble stannous salt in an amount of from about 5 to 150 grams per liter; (c) a thiourea as a sulfur containing complexing agent in an amount of from about 40 grams per liter to about 150 grams per liter; and (d) sufficient hydrochloric acid or hydrobromic acid to provide a pH for the bath in the range of 0.6 to 1.0; wherein, in said deposition of essentially tin, said plumbous salt is present in sufficient amount to act as a rate of deposition enhancer, and wherein said bath will deposit said essentially tin and tin-lead alloys onto copper or copper alloy substrates by immersion deposition at a rate of at least 85 microinches in 5 minutes at a temperature of 170° F.
Claim 2
Dependent Claim
181 words
An aqueous bath suitable for immersion deposition of essentially tin and tin-lead alloys onto copper or copper alloy substrates, said bath comprising: (a) a soluble plumbous salt in an amount from about 0.5 grams to about 25 grams per liter calculated on the basis of elemental lead including the maximum soluble in said bath; (b) tin as a soluble stannous salt in an amount of from about 5 to 150 grams per liter; (c) a thiourea as a sulfur containing complexing agent in an amount of from about 40 grams per liter to about 150 grams per liter; and (d) sufficient hydrochloric acid or hydrobromic acid to provide a pH for the bath in the range of 0.6 to 1.0; wherein, in said deposition of essentially tin, said plumbous salt is present in sufficient amount to act as a rate of deposition enhancer, and wherein said bath will deposit said essentially tin and tin-lead alloys onto copper or copper alloy substrates by immersion deposition at a rate of at least 85 microinches in 5 minutes at a temperature of 170° F.
Claim 3
Dependent Claim
20 words
A bath composition according to claim 1 which also includes a leveling agent and a solubility enhancer for said bath.
Claim 4
Dependent Claim
28 words
A bath composition according to claim 2 wherein said solubility enhancer is sodium hypophosphite and is present in an amount of about 10 to 100 grams per liter.
Claim 5
Dependent Claim
36 words
A bath composition according to claim 1 wherein said tin is present in said bath in the form of stannous chloride, the plumbous salt is present as lead chloride, and the solubility enhancer is sodium hypophosphite.
Claim 6
Dependent Claim
33 words
A bath composition according to claim 1 wherein the ratio of lead to tin dissolved in said bath ranges from 2% to 30% calculated on the basis of the weight of the metal.
Claim 7
Dependent Claim
31 words
A bath composition according to claim 1 wherein the concentration of lead in said bath is sufficiently low to limit the lead composition in the resulting deposit to less than 2%.
Claim 8
Dependent Claim
74 words
A bath composition according to claim 1 for the deposition of essentially tin comprising the following composition: ______________________________________
Component Grams/Liter
______________________________________
a. hydrous stannous chloride
from about 10 to about 150
(SnCl.sub. 2 . 2H.sub.2 O)
b. lead chloride from about 1 to about 12
(PbCl.sub.2)
c. sodium hypophosphite
from about 10 to about 100
(NaH.sub.2 PO.sub.2 . H.sub.2 O)
d. thiourea from about 40 to about 100.
(NH.sub.2 . (CS . NH.sub.2)
______________________________________
Claim 9
Dependent Claim
65 words
A bath composition according to claim 1 which comprises: ______________________________________
Component Grams/Liter
______________________________________
a. hydrous stannous chloride
from about 5 to about 100
(SnCl.sub.2 . 2H.sub.2 O)
b. lead chloride from about 2 to about 25
(PbCl.sub.2)
c. sodium hypophosphite
from about 60 to about 100
(NaH.sub.2 PO.sub.2 . H.sub.2 O)
d. thiourea from about 100 to about 150.
(NH.sub.2 . CS . NH.sub.2)
______________________________________
Claim 10
Dependent Claim
18 words
A bath composition as defined in claim 1 further comprising gelatin in the amount of about 0.1 grams/liter.
Claim 11
Dependent Claim
23 words
A bath composition as defined in claim 1 further comprising an alkyl phenoxy poly(oxyalkyl) ethanol surfactant in the amount of about 0.1 grams/liter.
Claim 12
Dependent Claim
60 words
An aqueous bath composition in accordance with claim 1, for the deposition of tin-lead alloys containing about 90-95% lead and 5-10% tin, said bath composition containing about 15-25 grams/liter of lead chloride, 6-10 grams/liter of tin chloride, 60-100 grams/liter of sodium hypophosphite, 100-150 grams/liter of thiourea and 50-100 ml/liter of hydrochloric acid, with a pH range of 0.5 to 1.0.
Claim 13
Dependent Claim
60 words
An aqueous bath composition in accordance with claim 1 for the deposition of alloys containing about 60% tin and 40% lead, said bath composition containing about 15-25 grams/liter of tin chloride dihydrate, 8-12 grams/liter of lead chloride, 60-100 grams/liter of sodium hypophosphite, 100-150 grams/liter of thiourea and 50-100 ml/liter of hydrochloric acid with a pH range of 0.5 to 1.0.
Claim 14
Dependent Claim
63 words
An aqueous bath composition in accordance with claim 1 for the deposition of alloys containing about 10% lead and 90% tin; said bath composition containing about 6 grams/liter of lead chloride, about 25 grams/liter of tin chloride dihydrate, about 60-100 grams/liter of sodium hypophosphite, about 100-150 grams/liter of thiourea, and 50-100 ml/liter of hydrochloric acid with a pH range of 0.5 to 1.0.
References Cited (Backward Citations)
US2369620A
Cited
US3050410A
Cited
US3303029A
Cited
US3409466A
Cited
US3689292A
Cited
JPS49106864A
Cited
SU455171A1
Cited
US3971861A
Cited
US4093466A
Cited
US4053372A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-25 | 1983-09-24 | 1984-03-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-25 | 1987-09-24 | 1988-03-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-25 | 1991-09-24 | 1992-03-25 | $7700.00 | Window Closed / Lapsed |