Process for applying a protective layer to shaped carbon bodies
Assignee: Siltronic AG
•
Filing: 1978-08-11
•
Granted: 1980-03-18
•
Expires: 1998-08-11
Abstract
Abstract The invention relates to the preparation of a material more favorably pri that the usual quartz crucible for use in the crucible-pulling of silicon according to Czochralski. To prevent reaction of the crucible wall with molten silicon, the surface of the shaped carbon body is coated by means of chemical vapor deposition first with a carbon-enriched silicon carbide layer and then with a carbon-enriched silicon nitride layer. The carbon-enriched silicon carbide layer is obtained by reacting a gaseous silicon compound with a gaseous carbon compound at a temperature of the shaped carbon body to be coated at 1250° to 1350° C. while the carbon-enriched silicon nitride layer is obtained by reacting a gaseous organosilicon compound with ammonia at a temperature of the shaped carbon body of 1000° to 1200° C.
Inventors
- 👤 Erhard Sirtl
- 👤 Heinz-Jorg Rath
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 01:15
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B01; B01L; B01L3/00; B01L3/04; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; C23; C23C; C23C16/00; C23C16/02; C23C16/0272; C23C16/22; C23C16/30; C23C16/32; C23C16/34; C23C16/345; C30; C30B; C30B15/00; C30B15/10
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
140 words
A process for applying a protective layer to shaped carbon bodies within a reactor, comprising the steps of: heating the shaped carbon bodies to a temperature of 1250° to 1350° C.; depositing by vapor deposition the reaction products of a gaseous admixture containing a carrier gas and a member selected from the group consisting of (a) a silicon- and carbon-containing gaseous compound and (b) a gaseous admixture including a silicon-containing gaseous compound and a carbon-containing gaseous compound onto the surface of the shaped carbon bodies so as to produce a silicon carbide layer; lowering the temperature of the carbon bodies to between 1000° and 1200° C.; and subsequently depositing by chemical vapor deposition from a carrier gas onto the shaped carbon body, the reaction product of a gaseous organosilicon compound and ammonia so as to produce a silicon nitride layer.
Claim 2
Dependent Claim
140 words
A process for applying a protective layer to shaped carbon bodies within a reactor, comprising the steps of: heating the shaped carbon bodies to a temperature of 1250° to 1350° C.; depositing by vapor deposition the reaction products of a gaseous admixture containing a carrier gas and a member selected from the group consisting of (a) a silicon- and carbon-containing gaseous compound and (b) a gaseous admixture including a silicon-containing gaseous compound and a carbon-containing gaseous compound onto the surface of the shaped carbon bodies so as to produce a silicon carbide layer; lowering the temperature of the carbon bodies to between 1000° and 1200° C.; and subsequently depositing by chemical vapor deposition from a carrier gas onto the shaped carbon body, the reaction product of a gaseous organosilicon compound and ammonia so as to produce a silicon nitride layer.
Claim 3
Dependent Claim
43 words
The process according to claim 1, wherein each deposition step includes introducing the carrier gas into the reactor in a quantity of 0.1 to 6 liters per hour per cm 2 of the surface to be coated, measured at standard temperature and pressure.
Claim 4
Dependent Claim
45 words
The process according to claim 1, wherein the silicon-containing gaseous compound is introduced into the reactor in admixture with excess hydrogen in quantities of 0.01 to 0.2 liters per hour per cm 2 of the surface to be coated, measured at standard temperature and pressure.
Claim 5
Dependent Claim
31 words
The process according to claim 1, wherein the silicon-containing gaseous compound of the first depositing step is introduced into the reactor in admixture with 85 to 95% by volume of hydrogen.
Claim 6
Dependent Claim
20 words
The process according to claim 1, wherein chlorosilanes are used as the silicon-containing gaseous compound of the first depositing step.
Claim 7
Dependent Claim
20 words
The process according to claim 1, wherein trichlorosilane is used as the silicon-containing gaseous compound in the first depositing step.
Claim 8
Dependent Claim
45 words
The process according to claim 1, wherein the carbon-containing gaseous compound is introduced into the reactor in admixture with excess hydrogen in quantities of 0.01 to 4 liters per hour per cm 2 of the surface to be coated, measured at standard temperature and pressure.
Claim 9
Dependent Claim
31 words
The process according to claim 1, wherein the carbon-containing gaseous compound of the first depositing step is introduced into the reactor in admixture with 85 to 95% by volume of hydrogen.
Claim 10
Dependent Claim
22 words
The process according to claim 1, wherein chlorinated hydrocarbons containing 1 to 2 carbon atoms are used as the carbon-containing gaseous compound.
Claim 11
Dependent Claim
22 words
The process according to claim 1, wherein the first depositing step is effected to a layer thickness of 5 to 100 μm.
Claim 12
Dependent Claim
48 words
The process according to claim 1, wherein the gaseous organosilicon compound of the second depositing step is introduced into the reactor with excess hydrogen in quantities of 0.01 to 0.2 liters per hour per cm 2 of the surface to be coated, measure at standard temperature and pressure.
Claim 13
Dependent Claim
26 words
The process according to claim 1, wherein the gaseous organosilicon compound is introduced into the reactor in admixture with 80 to 95% by volume of hydrogen.
Claim 14
Dependent Claim
15 words
The process according to claim 1, wherein tetramethylsilane is used as the gaseous organosilicon compound.
Claim 15
Dependent Claim
34 words
The process according to claim 1, wherein ammonia is introduced into the reactor in quantities of 0.1 to 6 liters per hour per cm 2 of deposition area, measured at standard temperature and pressure.
Claim 16
Dependent Claim
22 words
The process according to claim 1, wherein the second deposition step is effected to a layer thickness of 10 to 1500 μm.
References Cited (Backward Citations)
US2992127A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-18 | 1983-09-17 | 1984-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-18 | 1987-09-17 | 1988-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-18 | 1991-09-17 | 1992-03-18 | $7700.00 | Window Closed / Lapsed |