Catalyst for oxidation of sulfur dioxide
Assignee: MECS Inc
•
Filing: 1979-01-11
•
Granted: 1980-03-18
•
Expires: 1999-01-11
Abstract
Abstract A catalytic material for oxidation of sulfur dioxide to sulfur trioxide at any temperature above 300 DEG C., comprising a catalyst which at reaction conditions is a melt including sulfatized vanadium ions as the active catalytic component and two different promoters and which is dispersed in an inert porous carrier. The first promoter comprises cesium ions, optionally in combination with ions of another alkali metal such as sodium, potassium or rubidium, known to promote vanadium catalysts. The second promoter comprises ions of a metal such as aluminum, magnesium, yttrium or lanthanum, which does not promote formation of inactive V4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in the heavily sulfatized environment of the melt.
Inventors
- 👤 John Villadsen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 03:59
CPC Classifications
C; C01; C01B; C01B17/00; C01B17/69; C01B17/74; C01B17/76; C01B17/78; C01B17/79; B; B01; B01J; B01J27/00; B01J27/02; B01J27/053; B01J27/055
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
142 words
A catalytic material for the oxidation of sulfur dioxide to sulfur trioxide at any temperature above 300° C. which comprises a catalyst whose active components are molten at reaction temperature and includes (1) sulfatized vanadium ions as the catalytically active component; (2) a first promoter comprising ions of at least one alkali metal said one alkali metal being cesium to stabilize the active vanadium species at temperatures below 420° C.; and (3) a second promoter comprising ions of at least one metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in the heavily sulfatized environment of the melt to increase the activity of the catalyst at any temperature; said catalyst being supported by an inert porous carrier.
Claim 2
Dependent Claim
142 words
A catalytic material for the oxidation of sulfur dioxide to sulfur trioxide at any temperature above 300° C. which comprises a catalyst whose active components are molten at reaction temperature and includes (1) sulfatized vanadium ions as the catalytically active component; (2) a first promoter comprising ions of at least one alkali metal said one alkali metal being cesium to stabilize the active vanadium species at temperatures below 420° C.; and (3) a second promoter comprising ions of at least one metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in the heavily sulfatized environment of the melt to increase the activity of the catalyst at any temperature; said catalyst being supported by an inert porous carrier.
Claim 3
Dependent Claim
14 words
A catalytic material according to claim 1 wherein said first promoter comprises cesium ions.
Claim 4
Dependent Claim
29 words
A catalytic material according to claim 1, wherein said first promoter comprises ions of cesium and another alkali metal selected from the group consisting of Na, K and Rb.
Claim 5
Dependent Claim
27 words
A catalytic material according to claim 1 wherein said second promoter comprises ions of a metal selected from the group consisting of Al, Mg, Y and La.
Claim 6
Dependent Claim
40 words
A catalytic material according to claim 1 wherein the first promoter is present in an atomic ratio of alkali metal to vanadium of from about 2:1 to about 6:1 the atomic ratio of cesium to vanadium being more than 1:1.
Claim 7
Dependent Claim
27 words
A catalytic material according to claim 1 wherein the second promoter is present in an atomic ratio relative to vanadium of from about 0.2:1 to about 1.5:1.
Claim 8
Dependent Claim
26 words
A catalytic material according to claim 1 wherein the second promoter is Al which is present in a ratio of about 0.5 atoms per atom V.
Claim 9
Dependent Claim
15 words
A catalytic material according to claim 1 wherein said carrier is an inactive silica support.
Claim 10
Dependent Claim
25 words
A catalytic material according to claim 8 wherein the carrier is selected from the group consisting of diatomaceous earth, silica gel and porous glass powder.
Claim 11
Dependent Claim
137 words
A process of preparing a catalytic material for the oxidation of sulfur dioxide to sulfur trioxide which comprises (a) preparing a solution of a suitable vanadium compound, a cesium salt, and a salt of a metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in a melt of sulfatized vanadium, in a suitable solvent; (b) impregnating a suitable porous carrier with said solution; (c) forming said impregnated carrier into pellets; (d) drying said pellets; and (e) subjecting the dried pellets to a stream of air containing an oxide of sulfur selected from the group consisting of SO 2 and SO 3 at a temperature above 400° C. to activate the catalytic material.
Claim 12
Dependent Claim
137 words
A process of preparing a catalytic material for the oxidation of sulfur dioxide to sulfur trioxide which comprises (a) preparing a solution of a suitable vanadium compound, a cesium salt, and a salt of a metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in a melt of sulfatized vanadium, in a suitable solvent; (b) impregnating a suitable porous carrier with said solution; (c) forming said impregnated carrier into pellets; (d) drying said pellets; and (e) subjecting the dried pellets to a stream of air containing an oxide of sulfur selected from the group consisting of SO 2 and SO 3 at a temperature above 400° C. to activate the catalytic material.
Claim 13
Dependent Claim
25 words
A process according to claim 10 wherein said vanadium compound is selected from the group consisting of vanadyl sulfate, ammonium vanadate and alkali metal vanadates.
Claim 14
Dependent Claim
24 words
A process according to claim 10 wherein said cesium salt is selected from the group comprising the sulfate, carbonate, phosphate, hydroxide, nitrite and nitrate.
Claim 15
Dependent Claim
30 words
A process according to claim 10 wherein a salt of another alkali metal selected from the group consisting of Na, K and Rb is also included in the starting solution.
Claim 16
Dependent Claim
25 words
A process according to claim 13 wherein said alkali metal salt is selected from the group consisting of sulfates, carbonates, phosphates, hydroxides, nitrites and nitrates.
Claim 17
Dependent Claim
72 words
A process according to claim 10 wherein said salt of a metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in a melt of sulfatized vanadium is selected from the group consisting of the sulfates, phosphates, carbonates, hydroxides, nitrites and nitrates of Al, Mg, Y and La.
Claim 18
Dependent Claim
30 words
A process according to claim 10 wherein at least one of the salts included in the starting solution is phosphate in an amount below 0.5 mole per mole of vanadium.
Claim 19
Dependent Claim
14 words
A process according to claim 10 wherein said carrier is an inactive silica support.
Claim 20
Dependent Claim
24 words
A process according to claim 17 wherein the carrier is selected from the group consisting of diatomaceous earth, silica gel and porous glass powder.
Claim 21
Dependent Claim
139 words
A process of preparing a catalytic material for the oxidation of sulfur dioxide to sulfur trioxide which comprises (a) preparing a solution of a suitable vanadium compound, a cesium salt, a salt of a metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in a melt of sulfatized vanadium, and a suitable salt of silicic acid in a suitable solvent; (b) precipitating the silicic meterial; (c) forming said precipitated material into pellets; (d) drying said pellets; and (e) subjecting the dried pellets to a stream of air containing an oxide of sulfur selected from the group consisting of SO 2 and SO 3 at a temperature above 400° C. to activate the catalytic material.
Claim 22
Dependent Claim
139 words
A process of preparing a catalytic material for the oxidation of sulfur dioxide to sulfur trioxide which comprises (a) preparing a solution of a suitable vanadium compound, a cesium salt, a salt of a metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in a melt of sulfatized vanadium, and a suitable salt of silicic acid in a suitable solvent; (b) precipitating the silicic meterial; (c) forming said precipitated material into pellets; (d) drying said pellets; and (e) subjecting the dried pellets to a stream of air containing an oxide of sulfur selected from the group consisting of SO 2 and SO 3 at a temperature above 400° C. to activate the catalytic material.
Claim 23
Dependent Claim
25 words
A process according to claim 19 wherein said vanadium compound is selected from the group consisting of vanadyl sulfate, ammonium vanadate and alkali metal vanadates.
Claim 24
Dependent Claim
24 words
A process according to claim 19 wherein said cesium salt is selected from the group comprising the sulfate, carbonate, phosphate, hydroxide, nitrite and nitrate.
Claim 25
Dependent Claim
30 words
A process according to claim 19 wherein a salt of another alkali metal selected from the group consisting of Na, K and Rb is also included in the starting solution.
Claim 26
Dependent Claim
25 words
A process according to claim 22 wherein said alkali metal salt is selected from the group consisting of sulfates, carbonates, phosphates, hydroxides, nitrites and nitrates.
Claim 27
Dependent Claim
72 words
A process according to claim 19 wherein said salt of a metal which does not promote formation of inactive V 4 species and the oxide of which has a heat of formation greater than 100 kcal per oxygen atom and is at least partly soluble in a melt of sulfatized vanadium is selected from the group consisting of the sulfates, phosphates, carbonates, hydroxides, nitrites and nitrates of Al, Mg, Y and La.
Claim 28
Dependent Claim
30 words
A process according to claim 19 wherein at least one of the salts included in the starting solution is phosphate in an amount below 0.5 mole per mole of vanadium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-18 | 1983-09-17 | 1984-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-18 | 1987-09-17 | 1988-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-18 | 1991-09-17 | 1992-03-18 | $7700.00 | Window Closed / Lapsed |