Electrochemical cell electrodes incorporating noble metal-base metal alloy catalysts
Assignee: RTX Corp
•
Filing: 1978-07-03
•
Granted: 1980-03-11
•
Expires: 1998-07-03
Abstract
Abstract A novel and improved fuel cell electrode includes a finely divided noble metal-base metal alloy catalyst. The catalytic activity of noble metal in the electrode is greater than the catalytic activity of the same unalloyed noble metal. Theoretically any base metal may be advantageously alloyed with the noble metal and will yield improved catalytic activity. Preferably the finely divided alloy is supported.
Inventors
- 👤 Vinod M. Jalan
- 👤 Douglas A. Landsman
- 👤 John M. Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:04
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/92; H01M4/928; B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J23/42; B01J23/54; B01J23/56; H01M4/925; H01M4/926; H01M2004/8678; H01M2004/8689; H01M2300/00; H01M2300/0002; H01M2300/0005; H01M2300/0008; H01M4/921; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
78 words
A fuel cell including phosphoric acid electrolyte and a cathode electrode, said electrode comprising an electrically conductive substrate and a layer of catalyst disposed on said substrate, said catalyst comprising a finely divided platinum-base metal alloy supported on conductive particles, said alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of supported platinum in unalloyed form, and a surface area of at least 30 m 2 /g of platinum in the alloy.
Claim 2
Dependent Claim
78 words
A fuel cell including phosphoric acid electrolyte and a cathode electrode, said electrode comprising an electrically conductive substrate and a layer of catalyst disposed on said substrate, said catalyst comprising a finely divided platinum-base metal alloy supported on conductive particles, said alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of supported platinum in unalloyed form, and a surface area of at least 30 m 2 /g of platinum in the alloy.
Claim 3
Dependent Claim
22 words
The fuel cell according to claim 1 wherein the conductive support particles are carbon and the base metal is a refractory metal.
Claim 4
Dependent Claim
27 words
The fuel cell according to claim 2 wherein the refractory metal is selected from the group consisting of tungsten, aluminum, titanium, silicon, cerium, strontium, and combinations thereof.
Claim 5
Dependent Claim
26 words
The fuel cell according to claim 1 wherein said alloy has a surface area of at least 50 m 2 /g of platinum in the alloy.
Claim 6
Dependent Claim
78 words
A fuel cell comprising an anode electrode spaced apart from a cathode electrode and having an electrolyte disposed therebetween, said cathode electrode comprising a finely divided catalyst uniformly dispersed on conductive carbon support particles, said catalyst consisting of a platinum-refractory metal alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of supported platinum in unalloyed form, and a surface area of at least 50 m 2 /g of platinum in the alloy.
Claim 7
Dependent Claim
78 words
A fuel cell comprising an anode electrode spaced apart from a cathode electrode and having an electrolyte disposed therebetween, said cathode electrode comprising a finely divided catalyst uniformly dispersed on conductive carbon support particles, said catalyst consisting of a platinum-refractory metal alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of supported platinum in unalloyed form, and a surface area of at least 50 m 2 /g of platinum in the alloy.
Claim 8
Independent Claim
53 words
A method for electrochemically reducing oxygen including the step of using, as a catalyst for said reduction, a finely divided noble metal-refractory metal alloy uniformly dispersed on support particles, said alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of the supported noble metal in unalloyed form.
Claim 9
Independent Claim
53 words
A method for electrochemically reducing oxygen including the step of using, as a catalyst for said reduction, a finely divided noble metal-refractory metal alloy uniformly dispersed on support particles, said alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of the supported noble metal in unalloyed form.
Claim 10
Dependent Claim
11 words
The method of claim 6 wherein the noble metal is platinum.
Claim 11
Independent Claim
64 words
The method for electrochemically reducing oxygen in a fuel cell to produce electricity including the step of using, as a catalyst in the cathode electrode of the fuel cell, a finely divided platinum-refractory metal alloy uniformly dispersed on carbon support particles, said alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of carbon supported platinum in unalloyed form.
Claim 12
Independent Claim
64 words
The method for electrochemically reducing oxygen in a fuel cell to produce electricity including the step of using, as a catalyst in the cathode electrode of the fuel cell, a finely divided platinum-refractory metal alloy uniformly dispersed on carbon support particles, said alloy having a catalytic activity for the reduction of oxygen greater than the catalytic activity of carbon supported platinum in unalloyed form.
Claim 13
Dependent Claim
25 words
The method of claim 8 wherein the refractory metal is selected from the group consisting of tungsten, aluminum, titanium, silicon, cerium, strontium, and combinations thereof.
Claim 14
Dependent Claim
17 words
The method of claim 8 or 9 wherein the fuel cell includes phosphoric acid as the electrolyte.
References Cited (Backward Citations)
US2384501A
Cited
US3341936A
Cited
US3340097A
Cited
US3424619A
Cited
US3380934A
Cited
US3506494A
Cited
US3414439A
Cited
US3989515A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-11 | 1983-09-10 | 1984-03-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-11 | 1987-09-10 | 1988-03-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-11 | 1991-09-10 | 1992-03-11 | $7700.00 | Window Closed / Lapsed |