Electrodeposition process for forming amorphous silicon
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-10-16
•
Granted: 1980-03-11
•
Expires: 1998-10-16
Abstract
Abstract A method for electroplating amorphous silicon from a non-aqueous solution containing a silicon solute wherein a heat treatment is requisite to producing stable coatings of photoconductive amorphous silicon.
Inventors
- 👤 Edward R. Bucker
- 👤 James A. Amick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:09
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/10; H10F71/103; C; C25; C25D; C25D5/00; C25D5/48; C25D5/50; C25D9/00; C25D9/04; C25D9/08; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S205/00; Y10S205/915
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
131 words
A method for producing a stabilized photoconducting semiconductor film of amorphous silicon containing hydrogen, said method comprising: electrolyzing a non-aqueous solution of a silicon solute selected from the group consisting of silane, halogenated silane, silicon halides or mixtures thereof dissolved in a liquid aprotic solvent, or a mixture of a liquid aprotic solvent and an aromatic solvent said solution further having a supporting ion additive electrolyte, soluable in said solution, and imparting sufficient conductivity thereto to permit the electro reduction of said solute; reducing said silicon solute to electroplate a film containing silicon onto a cathode body immersed in said solution; heat treating said film in an oxygen free ambient at a temperature ranging from above about 250° C. to about 350° C. for a period sufficient to stabilize said film.
Claim 2
Independent Claim
131 words
A method for producing a stabilized photoconducting semiconductor film of amorphous silicon containing hydrogen, said method comprising: electrolyzing a non-aqueous solution of a silicon solute selected from the group consisting of silane, halogenated silane, silicon halides or mixtures thereof dissolved in a liquid aprotic solvent, or a mixture of a liquid aprotic solvent and an aromatic solvent said solution further having a supporting ion additive electrolyte, soluable in said solution, and imparting sufficient conductivity thereto to permit the electro reduction of said solute; reducing said silicon solute to electroplate a film containing silicon onto a cathode body immersed in said solution; heat treating said film in an oxygen free ambient at a temperature ranging from above about 250° C. to about 350° C. for a period sufficient to stabilize said film.
Claim 3
Dependent Claim
35 words
The method set forth in claim 1 wherein the step of heat-treating includes heating the electrodeposited film at a temperature of about 350° C. for a period of about 30 minutes in a non-oxidizing atmosphere.
Claim 4
Dependent Claim
18 words
The method set forth in claim 2 wherein the nonoxidizing atmosphere comprises helium, hydrogen, or a mixture thereof.
Claim 5
Dependent Claim
29 words
The method set forth in claim 2 or 3 wherein the step of heat-treating includes adjusting the level of hydrogen within said amorphous silicon film to produce enhanced photoconductivity.
Claim 6
Dependent Claim
23 words
The method set forth in claim 1 wherein the steps of electrolyzing and reducing is accomplished under the cover of an inert gas.
Claim 7
Dependent Claim
15 words
The method set forth in claim 1 wherein said solution is at about 23° C.
Claim 8
Dependent Claim
20 words
The method set forth in claim 1 wherein said supportive electrolyte comprises a mixture of tetrabutylammonium perchlorate and tetrabutylammonium bromide.
Claim 9
Dependent Claim
18 words
The method set forth in claim 1 wherein the non-aqueous solution contains less than 5 ppm of water.
Claim 10
Dependent Claim
21 words
The method set forth in claim 1 wherein said mixture is selected from the group consisting of: tetrahydrofuran-benzene, tetrahydrofuran-toluene, 1,3-dioxolane-benzene, 1,3-dioxolane-toluene.
Claim 11
Dependent Claim
29 words
The method set forth in claim 1 wherein said silicon halide comprises a compound of the formula SiX 4 where X is Cl, Br, I or a mixture thereof.
Claim 12
Dependent Claim
38 words
The method set forth in claim 1 wherein said halogenated silane comprises a compound of the formula HySiXhd 4-y where X is Br, I, Cl or a mixture thereof and y is the integer 1, 2 or 3.
Claim 13
Independent Claim
166 words
A method for producing a photo voltaic solar cell having a body of amorphous silicon comprising: electrolyzing a non-aqueous solution of a silicon solute selected from the group consisting of silane, halogenated silane, silicon halide, or mixtures thereof being dissolved in a liquid aprotic solvent, or a mixture of a liquid aprotic solvent and an aromatic solvent, said solution further having a supportive ion additive electrolyte soluable in said solution and imparting sufficient conductivity thereto to permit the electro reduction of said solute; reducing said silicon solute to electroplate a silicon containing film onto a cathode body immersed in said solution wherein said cathode comprises a metal which forms an ohmic contact to amorphous silicon; heat treating said film at a temperature of about 350° C. in a non-oxidizing atmosphere containing hydrogen or helium, wherein said heat treating adjusts the hydrogen content of said film; depositing a pellucid layer of a high work function electrically conductive electrode onto said stabilized film to produce a photovoltaic device.
Claim 14
Independent Claim
166 words
A method for producing a photo voltaic solar cell having a body of amorphous silicon comprising: electrolyzing a non-aqueous solution of a silicon solute selected from the group consisting of silane, halogenated silane, silicon halide, or mixtures thereof being dissolved in a liquid aprotic solvent, or a mixture of a liquid aprotic solvent and an aromatic solvent, said solution further having a supportive ion additive electrolyte soluable in said solution and imparting sufficient conductivity thereto to permit the electro reduction of said solute; reducing said silicon solute to electroplate a silicon containing film onto a cathode body immersed in said solution wherein said cathode comprises a metal which forms an ohmic contact to amorphous silicon; heat treating said film at a temperature of about 350° C. in a non-oxidizing atmosphere containing hydrogen or helium, wherein said heat treating adjusts the hydrogen content of said film; depositing a pellucid layer of a high work function electrically conductive electrode onto said stabilized film to produce a photovoltaic device.
Claim 15
Dependent Claim
16 words
The solar cell set forth in claim 12 wherein said ohmic contact comprises nichrome or molybdenum.
Claim 16
Dependent Claim
19 words
The solar cell set forth in claim 12 wherein said high work function metal comprises platinum, iridium or palladium.
Claim 17
Dependent Claim
12 words
A solar energy conversion cell produced by the method of claim 12.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-11 | 1983-09-10 | 1984-03-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-11 | 1987-09-10 | 1988-03-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-11 | 1991-09-10 | 1992-03-11 | $7700.00 | Window Closed / Lapsed |