High strength extended leakage path ceramic tube wall for image intensifier and method of manufacture
Assignee: United States Department of the Army
•
Filing: 1978-07-05
•
Granted: 1980-03-11
•
Expires: 1998-07-05
Abstract
Abstract A high strength and serrated edge extended leakage path ceramic tube wall r high voltage tube device, such as a proximity focused image intensifier, and method of making same. The ceramic may be comprised of a ceramic particle slurry made of high density alumina in a glass binder wherein the slurry is ultrasonically compacted against ultrasmooth mold walls in the uncured state. The mold may be formed by using a highly polished preshaped, positive, made of a metal such as brass, and then removing the positive. The mold may be further processed by electrodepositing a metal, such as nickel or nickel alloys, onto the positive to produce an ultrasmooth surface. The mold may be made of a vinyl polymer type thermoplastic. The inside of the mold takes up the smooth surface characteristics of the positive that is, in turn, transferred to the uncured ceramic when sufficiently pressed and compacted by the ultrasonically compacting step. The uncured ceramic is then pre-baked at about 350° C. for some time to produce a green ceramic at which time the mold is removed from the green ceramic. The green ceramic may have milled sections produced therein. After the sections are milled, the green ceramic is fired in the temperature range of 1600°-1800° C for about 15 hours to cure.
Inventors
- 👤 Andrew J. Kennedy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:46
CPC Classifications
H; H01; H01J; H01J1/00; H01J1/02; H01J1/13; H01J1/20; H01J1/24; B; B28; B28B; B28B7/00; B28B7/34; H01B; H01B19/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49227
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
217 words
A method of producing a smooth surfaced extended leakage path ceramic tube wall for a high voltage tube device, the steps comprising: providing a highly polished preshaped positive for fabricating an ultrasmooth walled plastic mold having alternating convex and concave circular radius of curvatures of from 1/4 to 1/2 millimeter radii along the wall thereof setting plastic on said preshaped positive to form an ultrasmooth walled plastic mold for making a smooth surfaced extended leakage path for said ceramic tube wall; removing said preshaped positive from said plastic mold; filling said plastic mold with a ceramic particle slurry of a vacuum tube envelope quality alumina of 95% to 98% in a granular glass binder; compacting said ceramic particle slurry against the ultrasmooth plastic mold with ultrasonic agitation; prebaking the combined said ceramic particle slurry and said ultrasmooth walled plastic mold to produce a ring-shaped green ceramic tube wall; removing said plastic mold from said ring-shaped green ceramic tube wall; making a trough in at least one end of said ring-shaped green ceramic tube wall; high temperature firing said green ceramic tube wall to provide a cured ceramic tube wall; and metallizing each end and said trough in at least one end of said ring-shaped cured ceramic tube wall for electrical connection to said high voltage tube device.
Claim 2
Independent Claim
217 words
A method of producing a smooth surfaced extended leakage path ceramic tube wall for a high voltage tube device, the steps comprising: providing a highly polished preshaped positive for fabricating an ultrasmooth walled plastic mold having alternating convex and concave circular radius of curvatures of from 1/4 to 1/2 millimeter radii along the wall thereof setting plastic on said preshaped positive to form an ultrasmooth walled plastic mold for making a smooth surfaced extended leakage path for said ceramic tube wall; removing said preshaped positive from said plastic mold; filling said plastic mold with a ceramic particle slurry of a vacuum tube envelope quality alumina of 95% to 98% in a granular glass binder; compacting said ceramic particle slurry against the ultrasmooth plastic mold with ultrasonic agitation; prebaking the combined said ceramic particle slurry and said ultrasmooth walled plastic mold to produce a ring-shaped green ceramic tube wall; removing said plastic mold from said ring-shaped green ceramic tube wall; making a trough in at least one end of said ring-shaped green ceramic tube wall; high temperature firing said green ceramic tube wall to provide a cured ceramic tube wall; and metallizing each end and said trough in at least one end of said ring-shaped cured ceramic tube wall for electrical connection to said high voltage tube device.
Claim 3
Dependent Claim
38 words
A method as set forth in claim 1 wherein said highly polished preshaped positive is made of brass and said step of removing said preshaped positive from said plastic mold is by slipping the mold off the positive.
Claim 4
Dependent Claim
38 words
A method as set forth in claim 2 wherein said step of compacting with ultrasonic agitation is by mounting said plastic mold with said ceramic particle slurry therein on a platform and moving said platform by ultrasonic agitation.
Claim 5
Dependent Claim
26 words
A method as set forth in claim 3 wherein said step of prebaking is at 300° C. to 500° C. for a period of 4-5 hours.
Claim 6
Dependent Claim
25 words
A method as set forth in claim 4 wherein said step of high temperature firing is at 1600° C. to 1800° C. for 15 hours.
Claim 7
Dependent Claim
54 words
A method as set forth in claim 5 wherein said plastic material in said step of setting plastic on said highly polished preshaped positive for fabricating an ultrasmooth walled plastic mold is made of a vinyl polymer type thermoplastic with a surface smoothness on the order of molecular dimensions of 0.005 to 0.01 micrometers.
Claim 8
Dependent Claim
39 words
A method as set forth in claim 6 wherein the step of removing said plastic mold from said ring-shaped green ceramic tube wall is by peeling off the plastic mold that has lost its resiliency in said prebaking step.
References Cited (Backward Citations)
US1628417A
Cited
US2182185A
Cited
US2390354A
Cited
US2515017A
Cited
GB688312A
Cited
GB953705A
Cited
US3074143A
Cited
DE1201034B
Cited
US3234308A
Cited
US3355614A
Cited
US3988405A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-11 | 1983-09-10 | 1984-03-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-11 | 1987-09-10 | 1988-03-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-11 | 1991-09-10 | 1992-03-11 | $7700.00 | Window Closed / Lapsed |