Process for forming novolak resin compositions into molding granules

Claim 2

A process for forming a novolak resin composition into molding granules, which comprises: (a) homogenizing the novolak resin composition at a temperature above the melting point of the novolak resin; (b) feeding the homogenized composition, at a temperature at which the said composition shows plasticity, but lower than the melting point of the novolak resin, between at least one pair of internally cooled rollers rotating in opposite directions with respect to each other with a peripheral speed of 0.15 to 0.30 m/sec., and having external surfaces separated from one another by a distance of 0.6 to 2 cm, so as to produce a coherent sheet by calendering; (c) rolling said coherent sheet between a pair of internally cooled rollers, at least one of which has a plurality of indentations, rotating in opposite direction with respect to each other with a peripheral speed of 0.3 to 0.8 m/sec. and having external surfaces separated from each other by a distance of 0.02 to 0.5 cm, so as to produce a coherent embossed sheet; (d) fracturating the said coherent embossed sheet and separating the granules having substantially the shape of the embossments from the fine and coarse fractions; (e) mixing said granules with a liquid coating material comprising from 0.3 to 3 wt.%, with respect to the weight of the granules, of at least one coating agent selected from the group consisting of substituted phenols; polyphenols; products of the condensation, in an acid or alkaline medium, of phenol, substituted phenols or polyphenols with an aldehyde; and mixtures of said substituted phenols, polyphenols and condensation products with phenol; and (f) heat-treating the coated granules thus obtained by flowing through the latter a stream of inert gas having a temperature not exceeding 130° C.

Claim 3

The process of claim 1, in which stage (a) is carried out by extruding the composition, maintaining in the initial part of the extruder a temperature above the melting point of the novolak resin and a temperature of the order of 20° C. below the melting point of the novolak resin at the outlet of the extruder.

Claim 4

The process of claim 1, in which stage (b) is carried out with a peripheral speed of the rollers of from 0.15 to 0.2 m/sec and with a distance between the rotating surfaces of about 1 cm.

Claim 5

The process of claim 1, in which stage (c) is carried out with a peripheral speed of the rollers of from 0.6 to 0.7 m/sec and with a distance between the rotating surfaces of 0.05 to 0.2 cm.

Claim 6

The process of claim 1, in which the indentations are of hemispherical, semi-cylindrical or semi-lenticular form, with dimensions such as to obtain granules of from 1 to 9 mm in size.

Claim 7

The process of claim 1, in which stage (c) is carried out with two rollers having indentations of identical form and dimensions, the indentations of one roller being complementary to those of the other roller under the conditions of rotation of the said two rollers.

Claim 8

The process of claim 1, in which said aldehyde is formaldehyde.

Claim 9

The process of claim 1, in which said mixtures with phenol contain from 20 to 50 wt.% of phenol.

Claim 10

The process of claim 1, in which said substituted phenol is para-phenylphenol.

Claim 11

The process of claim 1, in which said substituted phenol is para-tert-butylphenol.

Claim 12

The process of claim 1, in which said substituted phenol is para-cumylphenol.

Claim 13

The process of claim 1, in which said substituted phenol is the para substituted phenol obtained by reacting phenol with styrene in an acid medium.

Claim 14

The process of claim 1, in which stage (e) is carried out at ambient temperature and for a period of from 5 to 30 minutes.

Claim 15

The process of claim 1, in which stage (f) is carried out for a period of from 1 to 10 minutes, using a stream of gas having a temperature of from 90° to 120° C.

Claim 16

A process for forming a novolak resin composition into molding granules, which comprises: (a) homogenizing the novolak resin composition at a temperature above the melting point of the novolak resin; (b) feeding the homogenized composition, at a temperature at which the said composition shows plasticity, but lower than the melting point of the novolak resin, between at least one pair of internally cooled rollers rotating in opposite directions with respect to each other with a peripheral speed of 0.15 to 0.30 m/sec., and having external surfaces separated from one another by a distance of 0.6 to 2 cm, so as to produce a coherent sheet by calendering; (c) rolling said coherent sheet between a pair of internally cooled rollers, at least one of which has a plurality of indentations, rotating in opposite direction with respect to each other with a peripheral speed of 0.3 to 0.8 m/sec. and having external surfaces separated from each other by a distance of 0.02 to 0.5 cm, so as to produce a coherent embossed sheet; (d) fracturating the said coherent embossed sheet and separating the granules having substantially the shape of the embossments from the fine and coarse fractions, (e) mixing said granules with a liquid coating material comprising from 0.3 to 3 wt.%, with respect to the weight of the granules, of at least one coating agent selected from the group consisting of (a) alkyl phenols, aryl phenols, bisphenols, trisphenols and natural phenolic resins; (b) products of the condensation of phenol and/or compounds (a) with formaldehyde in an acid or alkaline medium and in a molar ratio of formaldehyde to phenol and/or compounds (a) of from 0.2:1 to 0.5:1; and (c) mixtures of said compounds (a) and products (b) with phenol; (f) heat-treating the coated granules thus obtained by flowing through the latter a stream of inert gas having a temperature not exceeding 130° C.

Claim 17

A process for forming a novolak resin composition into molding granules, which comprises: (a) homogenizing the novolak resin composition at a temperature above the melting point of the novolak resin; (b) feeding the homogenized composition, at a temperature at which the said composition shows plasticity, but lower than the melting point of the novolak resin, between at least one pair of internally cooled rollers rotating in opposite directions with respect to each other with a peripheral speed of 0.15 to 0.30 m/sec., and having external surfaces separated from one another by a distance of 0.6 to 2 cm, so as to produce a coherent sheet by calendering; (c) rolling said coherent sheet between a pair of internally cooled rollers, at least one of which has a plurality of indentations, rotating in opposite direction with respect to each other with a peripheral speed of 0.3 to 0.8 m/sec. and having external surfaces separated from each other by a distance of 0.02 to 0.5 cm, so as to produce a coherent embossed sheet; (d) fracturating the said coherent embossed sheet and separating the granules having substantially the shape of the embossments from the fine and coarse fractions, (e) mixing said granules with a liquid coating material comprising from 0.3 to 3 wt.%, with respect to the weight of the granules, of at least one coating agent selected from the group consisting of (a) alkyl phenols, aryl phenols, bisphenols, trisphenols and natural phenolic resins; (b) products of the condensation of phenol and/or compounds (a) with formaldehyde in an acid or alkaline medium and in a molar ratio of formaldehyde to phenol and/or compounds (a) of from 0.2:1 to 0.5:1; and (c) mixtures of said compounds (a) and products (b) with phenol; (f) heat-treating the coated granules thus obtained by flowing through the latter a stream of inert gas having a temperature not exceeding 130° C.

Claim 18

The process of claim 1 in which the internally cooled rollers lower the temperature of said coherent sheet to about 20° to 70° C.

Claim 19

The process of claim 1 in which the rolling in step (c) reduces the overall thickness of said embossed sheet including embossments to less than the thickness of the sheet as it enters said rollers.

Claim 20

The process of claim 1 in which the ratio of the overall thickness of said embossed sheet to the thickness of the calendared sheet prior to embossing is less than about 1:2.

Claim 21

The process of claim 1 in which said heat-treated granules are free flowing and free from a tendency to release dust.