US4191718A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thick section compression molded composites
Assignee: Ford Motor Co
•
Filing: 1977-12-19
•
Granted: 1980-03-04
•
Expires: 1997-12-19
Abstract
Abstract Mechanical properties of compression molded composites having thick sections and made from molding compounds comprising thermosetting resin and reinforcing fiber in a thickened dispersion are improved by a preheating stage and mold cycle times that are longer than the time necessary to reach the highest peak exotherm temperature of the composite during molding. Slow post cooling allows for development of properties especially when mold opening times are shorter than that required for removal of all thermal gradients.
Inventors
- 👤 Pankaj K. Mallick
- 👤 Narasimhan Raghupathi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 23:15
CPC Classifications
F; F02; F02F; F02F7/00; B; B29; B29C; B29C35/00; B29C35/02; B29C35/0288; B29C43/00; B29C43/32; B29C43/52; B29C2791/00; B29C2791/001; B29K; B29K2101/00; B29K2101/10; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/10; B29K2105/12; F02F2200/00; F02F2200/06
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
229 words
A method of compression molding of layered compounds comprising reinforcing glass fiber, thermosetting ester or epoxy resin and catalyst in a thickened dispersion wherein heat and pressure are applied to form structural thermosets having thick sections above about one quarter inch, which method comprises: (A) dielectrically preheating the molding compound or portion thereof to a temperature at least about 100° F. and up to about 200° F. for less than about 2 minutes and without pregelling; (B) introducing the preheated molding compound into a mold which is maintained at a temperature in excess of about 220° F. but below that which causes premature gelling of the molding compound and so as to cover at least about 50% of the area of the lower mold surface; (C) applying a peak pressure of at least about 200 psi to the molding compound in the mold sufficient to cause its flow and filling of the mold to form a molded object; (D) maintaining the molded object in the mold at elevated pressure and temperature for a time in excess of that at which the peak internal exotherm occurs; (E) removing the molded object from the mold; (F) optionally, post-treating the molded object by allowing it to cool after removal from the mold at an average rate in a range of up to about 15° F. per minute for the first five minutes.
Claim 2
Independent Claim
229 words
A method of compression molding of layered compounds comprising reinforcing glass fiber, thermosetting ester or epoxy resin and catalyst in a thickened dispersion wherein heat and pressure are applied to form structural thermosets having thick sections above about one quarter inch, which method comprises: (A) dielectrically preheating the molding compound or portion thereof to a temperature at least about 100° F. and up to about 200° F. for less than about 2 minutes and without pregelling; (B) introducing the preheated molding compound into a mold which is maintained at a temperature in excess of about 220° F. but below that which causes premature gelling of the molding compound and so as to cover at least about 50% of the area of the lower mold surface; (C) applying a peak pressure of at least about 200 psi to the molding compound in the mold sufficient to cause its flow and filling of the mold to form a molded object; (D) maintaining the molded object in the mold at elevated pressure and temperature for a time in excess of that at which the peak internal exotherm occurs; (E) removing the molded object from the mold; (F) optionally, post-treating the molded object by allowing it to cool after removal from the mold at an average rate in a range of up to about 15° F. per minute for the first five minutes.
Claim 3
Dependent Claim
19 words
The method in accordance with claim 1, wherein the layered molding compound comprises about 30-70% by weight glass fiber.
Claim 4
Dependent Claim
17 words
The method in accordance with claim 2, wherein the reinforcing fiber comprises randomly oriented chopped glass fiber.
Claim 5
Dependent Claim
17 words
The method in accordance with claim 2, wherein the reinforcing fiber comprises long or continuous glass fibers.
Claim 6
Dependent Claim
33 words
The method in accordance with claim 2, wherein the molded object is post treated after removal from the mold to allow its cooling at an average rate of about 5° to 10° F./min.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-04 | 1983-09-03 | 1984-03-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-04 | 1987-09-03 | 1988-03-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-04 | 1991-09-03 | 1992-03-04 | $7700.00 | Window Closed / Lapsed |