Silicone paper release compositions

Claim 2

A paper release coating emulsion composition comprising (A) 100 parts by weight of a vinyl-containing polymer of the formula, ##STR4## where Vi is vinyl, R is an aliphatically saturated monovalent hydrocarbon radical, R' is a monovalent hydrocarbon radical and x and y vary such that the polymer has a viscosity ranging from 1,500 to 24,000 centipoise at 25° C. in which the polymer has a silanol content that varies from 650 to 2,400 parts per million and a vinyl content that varies from 0.1 to 2% by weight; (B) from 1 part per million to 2 parts by weight of a catalyst selected from the class consisting of platinum catalyst and tin soaps of carboxylic acids; (C) from 1 to 30 parts by weight of a hydride polysiloxane crosslinking agent; (D) from 50 to 300 parts of water, and (E) from 5 to 80 parts by weight of emulsifying agents.

Claim 3

The composition of claim 1 wherein the vinyl-containing polymer has a vinyl content that varies from 0.1 to 2% by weight and a silanol content that varies from 650 to 2400 parts per million.

Claim 4

The composition of claim 1 wherein the catalyst is a platinum catalyst at a concentration of 1 to 200 parts per million.

Claim 5

The composition of claim 3 wherein the platinum catalyst is platinum complexed with hydrocarbon compounds selected from the class consisting of alcohols, aldehydes and ethers.

Claim 6

The composition of claim 3 wherein the platinum catalyst is platinum complexed with a vinyl siloxane wherein the platinum complex is substantially free of chemically combined chlorine.

Claim 7

The composition of claim 1 wherein the hydride polysiloxane has the formula, ##STR5## where R 2 is selected from hydrogen and monovalent hydrocarbon radicals and s, t vary such that the viscosity of the polymer varies from 1 to 250 centipoise at 25° C.

Claim 8

The composition of claim 6 wherein the polymer has a viscosity of 5-50 centipoise at 25° C., and a hydride content varying from 0.3 to 1.6% by weight.

Claim 9

The composition of claim 1 wherein the hydride polysiloxane is composed of H(R 2 ) 2 SiO 0 .5 units and SiO 2 units, where the H+R 2 to Si ratio varies from 1.0 to 2.7 and R 2 is a monovalent hydrocarbon radical.

Claim 10

The composition of claim 1 wherein the hydride polysiloxane is composed of H(R 2 ) 2 SiO 0 .5 units, SiO 2 units, and H(R 2 )SiO units where the ratio of R 2 +H to Si varies from 1.0 to 2.7 and R 2 is a monovalent hydrocarbon radical.

Claim 11

The composition of claim 1 wherein the emulsifying agent is polyvinyl alcohol.

Claim 12

The composition of claim 1 wherein the hydride polysiloxane is first emulsified before it is added to the mixture.

Claim 13

The composition of claim 11 wherein the hydride polysiloxane is first emulsified in water and as the emulsifying agent an alkylphenoxypolyoxyethyleneethanol where the alkyl group has from 1 to 15 carbon atoms.

Claim 14

The composition of claim 1 wherein the catalyst is a tin soap of a carboxylic acid and is dibutyl tin dilaurate and is present at a concentration of 0.1 to 20 parts by weight as tin.

Claim 15

The composition of claim 1 wherein the catalyst is a mercapto tin soap of a carboxylic acid and is di(N-octyl)tin S,S'-bis-(isooctylmercaptoacetate) and is present at a concentration of 0.1 to 2 parts by weight as tin.

Claim 16

A process for forming a silicone paper coating comprising (1) emulsifying a mixture of (A) 100 parts by weight of a vinyl-containing polymer of the formula, ##STR6## where Vi is vinyl, R is an aliphatically saturated monovalent hydrocarbon radical, R' is a monovalent hydrocarbon radical and x, y vary such that the polymer has a viscosity varying from 1,500 to 24,000 centipoise at 25° C. in which the polymer has a silanol content that varies from 650 to 2,400 parts per million and a vinyl content that varies from 0.1 to 2% by weight; (B) from 1 part per million to 2 parts by weight of a catalyst selected from the class consisting of platinum catalysts and tin soaps of carboxylic acids; (C) from 50 to 300 parts of water; and (D) from 5 to 80 parts by weight of emulsifying agents, (2) emulsifying a hydride polysiloxane; (3) adding the emulsion of the hydride polysiloxane to the emulsion of the vinyl-containing polymer such that there is present from 1 to 30 parts by weight of the hydride polysiloxane per 100 parts of the vinyl-containing polymer; and (4) allowing the composition to cure.

Claim 17

A process for forming a silicone paper coating comprising (1) emulsifying a mixture of (A) 100 parts by weight of a vinyl-containing polymer of the formula, ##STR6## where Vi is vinyl, R is an aliphatically saturated monovalent hydrocarbon radical, R' is a monovalent hydrocarbon radical and x, y vary such that the polymer has a viscosity varying from 1,500 to 24,000 centipoise at 25° C. in which the polymer has a silanol content that varies from 650 to 2,400 parts per million and a vinyl content that varies from 0.1 to 2% by weight; (B) from 1 part per million to 2 parts by weight of a catalyst selected from the class consisting of platinum catalysts and tin soaps of carboxylic acids; (C) from 50 to 300 parts of water; and (D) from 5 to 80 parts by weight of emulsifying agents, (2) emulsifying a hydride polysiloxane; (3) adding the emulsion of the hydride polysiloxane to the emulsion of the vinyl-containing polymer such that there is present from 1 to 30 parts by weight of the hydride polysiloxane per 100 parts of the vinyl-containing polymer; and (4) allowing the composition to cure.

Claim 18

The process of claim 15 wherein the vinyl-containing polymer has a vinyl content that varies from 0.1 to 2% by weight and a silanol content that varies from 650 to 2400 parts per million.

Claim 19

The process of claim 15 wherein the catalyst is a platinum catalyst at a concentration of 1 to 200 parts per million.

Claim 20

The process of claim 17 wherein the platinum catalyst is a platinum complexed with a hydrocarbon compound selected from the class consisting of alcohols, aldehydes and ethers.

Claim 21

The process of claim 17 wherein the platinum catalyst is platinum complexed with a vinyl siloxane wherein the platinum complex is substantially free of chemically combined chlorine.

Claim 22

The process of claim 15 wherein the hydride polysiloxane has the formula, ##STR7## where R 2 is selected from hydrogen and monovalent hydrocarbon radicals, and s, t vary such that the viscosity of the polymer varies from 1 to 250 centipoise at 25° C.

Claim 23

The process of claim 20 wherein the hydride polysiloxane has a viscosity of 5-50 centipoise at 25° C., and a hydride content varying from 0.3 to 1.6% by weight.

Claim 24

The process of claim 15 wherein the hydride polysiloxane is composed of H(R 2 ) 2 SiO 0 .5 units and SiO 2 units where the R 2 +H to Si ratio varies from 1.0 to 2.7 and R 2 is a monovalent hydrocarbon radical.

Claim 25

The process of claim 15 wherein the hydride polysiloxane is composed of H(R 2 ) 2 SiO 0 .5 units, SiO 2 units, and H(R 2 )SiO units where the ratio of R 2 +H to Si varies from 1.0 to 2.7 and R 2 is a monovalent hydrocarbon radical.

Claim 26

The process of claim 15 wherein the emulsifying agent is polyvinyl alcohol.

Claim 27

The process of claim 15 wherein the hydride polysiloxane is emulsified in water and as the emulsifying agent there is used an alkylphenoxypolyoxyethyleneethanol where the alkyl group has from 1 to 15 carbon atoms.

Claim 28

The process of claim 15 wherein the catalyst is a tin soap of a carboxylic acid and is dibutyl tin dilaurate and is present at a concentration of 0.1 to 2 parts by weight as tin.

Claim 29

The process of claim 15 wherein the catalyst is a mercapto tin soap of a carboxylic acid and is di(N-octyl)tin S,S'-bis-(isooctylmercaptoacetate) and is present at a concentration of 0.1 to 2 parts by weight as tin.

Claim 30

A process for coating paper with a silicone paper release coating with excellent release properties to pressure sensitive adhesives comprising (1) emulsifying a mixture of (A) 100 parts by weight of a vinyl-containing polymer of the formula, ##STR8## where Vi is vinyl, R is aliphatically saturated monovalent hydrocarbon radical, R' is a monovalent hydrocarbon radical and x, y vary such that the polymer has a viscosity varying from 1500 to 24,000 centipoise at 25° C. in which the polymer has a silanol content that varies from 650 to 2,400 parts per million and a vinyl content that varies from 0.1 to 2% by weight; (B) from 1 part per million to 2 parts by weight of a catalyst selected from the class consisting of platinum catalysts and tin soaps of carboxylic acids; (C) from 50 to 300 parts of water; and (D) from 5 to 80 parts by weight of emulsifying agents; (2) emulsifying a hydride polysiloxane; (3) adding the emulsion of the hydride polysiloxane to the emulsion of the vinyl-containing polymer such that there is present from 1 to 30 parts by weight of the hydride polysiloxane for 100 parts of the vinyl-containing polymer to form an emulsion mixture; (4) applying the emulsion mixture to paper; and (5) allowing the foregoing emulsion mixture to cure.

Claim 31

A process for coating paper with a silicone paper release coating with excellent release properties to pressure sensitive adhesives comprising (1) emulsifying a mixture of (A) 100 parts by weight of a vinyl-containing polymer of the formula, ##STR8## where Vi is vinyl, R is aliphatically saturated monovalent hydrocarbon radical, R' is a monovalent hydrocarbon radical and x, y vary such that the polymer has a viscosity varying from 1500 to 24,000 centipoise at 25° C. in which the polymer has a silanol content that varies from 650 to 2,400 parts per million and a vinyl content that varies from 0.1 to 2% by weight; (B) from 1 part per million to 2 parts by weight of a catalyst selected from the class consisting of platinum catalysts and tin soaps of carboxylic acids; (C) from 50 to 300 parts of water; and (D) from 5 to 80 parts by weight of emulsifying agents; (2) emulsifying a hydride polysiloxane; (3) adding the emulsion of the hydride polysiloxane to the emulsion of the vinyl-containing polymer such that there is present from 1 to 30 parts by weight of the hydride polysiloxane for 100 parts of the vinyl-containing polymer to form an emulsion mixture; (4) applying the emulsion mixture to paper; and (5) allowing the foregoing emulsion mixture to cure.