Reaction product of an epoxide and a polyalkylenepolyamine in bead form and a method for preparing same
Assignee: Dow Chemical Co
•
Filing: 1978-06-28
•
Granted: 1980-02-19
•
Expires: 1998-06-28
Abstract
Abstract The reaction product of an epoxide and a polyalkylenepolyamine is prepared in bead form by dispersing a blend of the epoxide and polyalkylenepolyamine in a concentrated aqueous solution of an alkali metal hydroxide and then curing the dispersed blend. For example, dispersing a blend of triethylenetetramine and diglycidyl ether of bisphenol A in an agitated aqueous solution of 50 weight percent NaOH and curing the dispersed blend produces normally solid beads which are useful as a weak base ion exchange resin.
Inventors
- 👤 Eldon L. Ward
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:42
CPC Classifications
B; B01; B01J; B01J39/00; B01J39/08; B01J39/16; B01J39/18; B01J39/20; C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/50
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
95 words
A method for preparing a normally solid reaction product of a polyamine of an aliphatic, alicyclic or aromatic hydrocarbon or an inertly substituted aliphatic, alicyclic or aromatic hydrocarbon having three or more reactive amino hydrogens and a polyfunctional epoxide, in the form of beads, the method comprising the steps of (1) dispersing a blend of the polyamine and the polyfunctional epoxide in a reaction medium of a concentrated aqueous solution of alkali metal hydroxide and (2) maintaining the dispersed blend at conditions sufficient to cure the blend to discrete, spheroidal beads of the reaction product.
Claim 2
Independent Claim
95 words
A method for preparing a normally solid reaction product of a polyamine of an aliphatic, alicyclic or aromatic hydrocarbon or an inertly substituted aliphatic, alicyclic or aromatic hydrocarbon having three or more reactive amino hydrogens and a polyfunctional epoxide, in the form of beads, the method comprising the steps of (1) dispersing a blend of the polyamine and the polyfunctional epoxide in a reaction medium of a concentrated aqueous solution of alkali metal hydroxide and (2) maintaining the dispersed blend at conditions sufficient to cure the blend to discrete, spheroidal beads of the reaction product.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein the reaction medium further comprises an amount of suspending agent sufficient to reduce agglomeration of the dispersed blend.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein the reaction medium is at a temperature of between about 50° C. and 135° C.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein the reactant ratio of the polyamine and the polyfunctional epoxide is from about 0.1:1 to about 1:1.
Claim 6
Dependent Claim
30 words
The method of claim 1 wherein the volume of the reaction medium is from about 1 to about 15 times the volume of the blend of polyamine and polyfunctional epoxide.
Claim 7
Dependent Claim
46 words
The method of claim 1 wherein the alkali metal hydroxide is sodium hydroxide, lithium hydroxide or potassium hydroxide, and the reaction medium comprises at least 40 weight percent of the alkali metal hydroxide based on the total weight of the alkali metal hydroxide and the water.
Claim 8
Dependent Claim
46 words
The method of claim 2 wherein the reaction medium is at an initial reaction temperature from about 50° to about 90° C. and following partial cure of the dispersed blend the temperature of the reaction medium is increased to from about 70° to about 135° C.
Claim 9
Dependent Claim
26 words
The method of claim 2 wherein the volume of the reaction medium to the volume of the dispersed blend is from about 1:1 to about 5:1.
Claim 10
Dependent Claim
37 words
The method of claim 2 wherein the reaction medium comprises from about 0.01 to about 5 weight percent of the suspending agent based on the total weight of the polyamine and polyfunctional epoxide in the reaction medium.
Claim 11
Dependent Claim
22 words
The method of claim 2 wherein the suspending agent is a hydroxyalkyl cellulose, carboxylated methylcellulose, carboxymethylated methylcellulose, white dextrin or canary dextrin.
Claim 12
Dependent Claim
122 words
The method of claim 9 wherein the polyfunctional epoxide is an epoxide containing sufficient reactive functional groups to form a cross-linked network when reacted with the polyamide and the reactant ratio of the polyfunctional epoxide and the polyamine is from about 0.1:1 to about 1:1, the alkali metal hydroxide is sodium hydroxide or potassium hydroxide, the reaction medium comprises at least 50 weight percent of the alkali metal hydroxide based on the total weight of the alkali metal hydroxide and water, the reaction medium is at an initial reaction temperature from about 50° to about 90° C. and following the partial cure of the dispersed blend the temperature of the reaction medium is increased to from about 70° to about 135° C.
Claim 13
Dependent Claim
33 words
The method of claim 1 wherein the polyfunctional epoxide is diglycidyl ether of bisphenol A or bisphenol F; or a polyglycidyl ether of polyphenol-formaldehyde and the polyamine is triethylenetetraamine, bis(2-aminoethyl)sulfide, polyethyleneimine or 1,6-hexanediamine.
Claim 14
Dependent Claim
55 words
The cured reaction product of a polyamine of an aliphatic, alicyclic or aromatic hydrocarbon having three or more reactive functional amino hydrogens and a polyepoxide wherein the molar ratio of the reactants is from about 0.1:1 to about 1.5:1 moles of polyepoxide to moles of polyamine in the form of normally solid, discrete, spheroidal beads.
Claim 15
Dependent Claim
55 words
The cured reaction product of a polyamine of an aliphatic, alicyclic or aromatic hydrocarbon having three or more reactive functional amino hydrogens and a polyepoxide wherein the molar ratio of the reactants is from about 0.1:1 to about 1.5:1 moles of polyepoxide to moles of polyamine in the form of normally solid, discrete, spheroidal beads.
Claim 16
Dependent Claim
19 words
The cured reaction product of claim 13 wherein the polyamine is ethylenediamine, diethylenetriamine, triethylenetetraamine, 1,3-propanediamine, bis(2-aminoethyl)sulfide, 1,6-hexanediamine or polyethyleneimine.
Claim 17
Dependent Claim
21 words
The cured reaction product of claim 13 wherein the polyepoxide is an aromatic based epoxide or the polyglycidyl ether of polyphenol-formaldehyde.
Claim 18
Dependent Claim
33 words
The cured reaction product of claim 13 wherein the polyamine is diethylenetriamine or triethylenetetraamine and the polyepoxide is the diglycidyl ether of bisphenol A or bisphenol F; or the polyglycidyl ether of polyphenol-formaldehyde.
Claim 19
Dependent Claim
27 words
The cured reaction product of claim 13 wherein the reactant ratio of the reactants is from about 0.2:1 to about 0.8:1 epoxy equivalents to amino hydrogen equivalents.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-18 | 1983-08-20 | 1984-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-18 | 1987-08-20 | 1988-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-18 | 1991-08-20 | 1992-02-19 | $7700.00 | Window Closed / Lapsed |