Heat sealable resin blends

Claim 2

A resin blend for producing a peelable heat seal between substrates on which it is carried, comprising: (a) about 50 to 90 weight percent of a copolymer of about 80 to 96 weight percent ethylene and about 20 to 4 weight percent of an ethylenically unsaturated ester; and (b) about 50 to 10 weight percent of a crystalline, isotactic polybutylene having a melt index of about 0.4 to 20, said blend having a heat sealing temperature of about 160° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3 pounds between resin blend layers heat sealed at said heat sealing temperatures.

Claim 3

The blend of claim 1 comprising about 60 to 80 weight percent of said copolymer and about 40 to 20 weight percent of polybutylene.

Claim 4

The blend of claim 2 wherein said heat sealing temperature is about 180° to 220° Fahrenheit, and said peel strength is about 0.5 to 1.5 pounds.

Claim 5

The blend of claim 1 wherein said ethylenically-unsaturated ester is selected from the group consisting of vinyl acetate and methyl acrylate.

Claim 6

The blend of claim 4 wherein said ethylenically-unsaturated ester is vinyl acetate.

Claim 7

The blend of claim 5 wherein said copolymer contains about 12 to 14 weight percent of vinyl acetate, and comprises about 80 to 85 weight percent of said blend.

Claim 8

The blend of claim 5 wherein said copolymer contains about 4.5 weight percent of vinyl acetate, said blend including a quantity of a graft copolymer of an unsaturated, fused ring, carboxylic acid anhydride upon high density polyethylene.

Claim 9

The blend of claim 4 wherein said copolymer is of about 80 weight percent ethylene and about 20 weight percent methyl acrylate.

Claim 10

The blend of claim 8 wherein said copolymer comprises about 80 to 85 weight percent of said blend.

Claim 11

The blend of claim 1 wherein said polybutylene is a high molecular weight, flexible, crystalline, isotactic polymer having a density of about 0.91 and a melt index of about 0.4 to 20.

Claim 12

The blend of claim 10 wherein said melt index is about 1.0.

Claim 13

A film adapted for producing a peelable heat seal, comprising a substrate and a resin blend carried thereon, said resin blend comprising (a) about 50 to 90 weight percent of a copolymer of about 80 to 96 weight percent of ethylene and about 20 to 4 weight percent of an ethylenically unsaturated ester; and (b) about 50 to 10 weight percent of a crystalline, isotactic polybutylene having a melt index of about 0.4 to 20, said blend having a heat sealing temperature of about 160° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3 pounds between resin blend layers of the substrate heat sealed at said heat sealing temperatures.

Claim 14

A film adapted for producing a peelable heat seal, comprising a substrate and a resin blend carried thereon, said resin blend comprising (a) about 50 to 90 weight percent of a copolymer of about 80 to 96 weight percent of ethylene and about 20 to 4 weight percent of an ethylenically unsaturated ester; and (b) about 50 to 10 weight percent of a crystalline, isotactic polybutylene having a melt index of about 0.4 to 20, said blend having a heat sealing temperature of about 160° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3 pounds between resin blend layers of the substrate heat sealed at said heat sealing temperatures.

Claim 15

The film of claim 12 comprising about 60 to 80 weight percent of copolymer and about 40 to 20 weight percent of polybutylene, said heat sealing temperature being about 180° to 220° Fahrenheit, and said peel strength being about 0.5 to 1.5 pounds.

Claim 16

The film of claim 12 wherein said ethylenically-unsaturated ester is selected from the group consisting of vinyl acetate and methyl acrylate.

Claim 17

The film of claim 14 wherein said copolymer contains about 12 to 14 weight percent of vinyl acetate, and comprises about 80 to 85 weight percent of said blend.

Claim 18

The film of claim 14 wherein said copolymer contains about 4.5 weight percent of vinyl acetate, said blend including a quantity of a graft copolymer of an unsaturated, fused ring, carboxylic acid anhydride upon high density polyethylene.

Claim 19

The film of claim 14 wherein said copolymer is of about 80 weight percent ethylene and about 20 weight percent methyl acrylate.

Claim 20

The film of claim 12 wherein said polybutylene is a high molecular weight, flexible, crystalline, isotactic polymer having a density of about 0.91 and a melt index of about 0.4 to 20.

Claim 21

The film of claim 14 wherein said substrate is of high density polyethylene.

Claim 22

The film of claim 16 wherein said substrate is of nylon.

Claim 23

The film of claim 14 wherein said film has an overall thickness of about 1.25 to 2.5 mils.

Claim 24

The film of claim 21 wherein said blend comprises about 10 to 30 percent of the thickness of said film.

Claim 25

The film of claim 14 wherein said film is a coextrudate of said blend and said substrate.

Claim 26

A resin blend for producing a peelable heat seal between substrates on which it is carried, comprising: (a) about 80 weight percent of a copolymer of about 88 to 80 weight percent ethylene and about 12 to 20 weight percent vinyl acetate; and (b) about 20 weight percent of a high molecular weight, crystalline, isotactic polybutylene resin having a density of about 0.91 and a melt index of about 1.0, said blend having a heat sealing temperature of about 215° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3.0 pounds between resin blend layers heat sealed at said heat sealing temperatures.

Claim 27

A resin blend for producing a peelable heat seal between substrates on which it is carried, comprising: (a) about 80 weight percent of a copolymer of about 88 to 80 weight percent ethylene and about 12 to 20 weight percent vinyl acetate; and (b) about 20 weight percent of a high molecular weight, crystalline, isotactic polybutylene resin having a density of about 0.91 and a melt index of about 1.0, said blend having a heat sealing temperature of about 215° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3.0 pounds between resin blend layers heat sealed at said heat sealing temperatures.

Claim 28

A resin blend for producing a peelable heat seal between substrates on which it is carried, comprising: (a) about 85 weight percent of an ethylene-vinyl acetate copolymer having a vinyl acetate content of about 4.5 weight percent and containing a quantity of a graft copolymer of an unsaturated, fused ring, carboxylic acid anhydride upon high density polyethylene, and (b) about 15 weight percent of a crystalline, isotactic polybutylene resin having a density of about 0.91 and a melt index of about 1.0; said blend having a heat sealing temperature of about 210° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to about 1.8 pounds between resin blend layers heat sealed at said heat sealing temperatures.

Claim 29

A resin blend for producing a peelable heat seal between substrates on which it is carried, comprising: (a) about 85 weight percent of an ethylene-vinyl acetate copolymer having a vinyl acetate content of about 4.5 weight percent and containing a quantity of a graft copolymer of an unsaturated, fused ring, carboxylic acid anhydride upon high density polyethylene, and (b) about 15 weight percent of a crystalline, isotactic polybutylene resin having a density of about 0.91 and a melt index of about 1.0; said blend having a heat sealing temperature of about 210° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to about 1.8 pounds between resin blend layers heat sealed at said heat sealing temperatures.

Claim 30

A resin blend for producing a peelable heat seal between substrates on which it is carried comprising: (a) about 80 weight percent of an ethylene-methyl acrylate copolymer having a methyl acrylate content of about 20 weight percent; and (b) about 20 weight percent of a crystalline, isotactic polybutylene having a melt index of about 1.0, said blend having a heat sealing temperature of about 215° to 250° Fahrenheit and affording a peel strength of about 0.3 to about 3 pounds between resin blend layers heat sealed at said heat sealing temperature.

Claim 31

A resin blend for producing a peelable heat seal between substrates on which it is carried comprising: (a) about 80 weight percent of an ethylene-methyl acrylate copolymer having a methyl acrylate content of about 20 weight percent; and (b) about 20 weight percent of a crystalline, isotactic polybutylene having a melt index of about 1.0, said blend having a heat sealing temperature of about 215° to 250° Fahrenheit and affording a peel strength of about 0.3 to about 3 pounds between resin blend layers heat sealed at said heat sealing temperature.

Claim 32

A film adapted for producing a peelable heat seal, said film being a coextrudate of a high density polyethylene resin and, as the heat sealing layer, a resin blend comprising (a) about 50 to 90 weight percent of a copolymer of about 80 to 96 weight percent ethylene and about 20 to 4 weight percent vinyl acetate or methyl acrylate; and (b) about 50 to 10 weight percent of a crystalline, isotactic polybutylene having a melt index of about 1.0, said blend layer having a heat sealing temperature of about 160° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3 pounds between resin blend layers of said film heat sealed at said heat sealing temperatures.

Claim 33

A film adapted for producing a peelable heat seal, said film being a coextrudate of a high density polyethylene resin and, as the heat sealing layer, a resin blend comprising (a) about 50 to 90 weight percent of a copolymer of about 80 to 96 weight percent ethylene and about 20 to 4 weight percent vinyl acetate or methyl acrylate; and (b) about 50 to 10 weight percent of a crystalline, isotactic polybutylene having a melt index of about 1.0, said blend layer having a heat sealing temperature of about 160° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 3 pounds between resin blend layers of said film heat sealed at said heat sealing temperatures.

Claim 34

A film adapted for producing a peelable heat seal, said film being a coextrudate comprising nylon and, as the heat sealing layer, a resin blend comprising (a) about 85 weight percent of an ethylene-vinylacetate copolymer having a vinyl acetate content of about 4.5 weight percent and containing a quantity of a graft copolymer of an unsaturated, fused ring, carboxylic acid anhydride upon high density polyethylene; and (b) about 15 weight percent of crystalline, isotactic polybutylene having a melt index of about 1.0, said blend layer having a heat sealing temperature of about 210° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 1.8 pounds between resin blend layers of said film heat sealed at said heat sealing temperatures.

Claim 35

A film adapted for producing a peelable heat seal, said film being a coextrudate comprising nylon and, as the heat sealing layer, a resin blend comprising (a) about 85 weight percent of an ethylene-vinylacetate copolymer having a vinyl acetate content of about 4.5 weight percent and containing a quantity of a graft copolymer of an unsaturated, fused ring, carboxylic acid anhydride upon high density polyethylene; and (b) about 15 weight percent of crystalline, isotactic polybutylene having a melt index of about 1.0, said blend layer having a heat sealing temperature of about 210° to 300° Fahrenheit, as determined at the sealing jaws, and affording a peel strength of about 0.3 to 1.8 pounds between resin blend layers of said film heat sealed at said heat sealing temperatures.