Coating compositions for architectural use
Assignee: Kowa Chemical Industry Co Ltd
•
Filing: 1978-10-13
•
Granted: 1980-02-19
•
Expires: 1998-10-13
Abstract
Abstract Novel coating compositions for architectural use are provided, which include a quaternary ammonium silicate having a silica content of 10 to 60% by weight and a liquid epoxide resin, besides the conventional ingredients, such as pigments, fillers, aggregates and water, and which are particularly capable of producing films having excellent adherency to mortar or concrete surfaces. If a stabilized silica sol is added to the compositions, films produced therefrom have much improved resistance to water at low temperatures as well as freeze-thaw stability.
Inventors
- 👤 Kiyoshi Kikuchi
- 👤 Takeo Okano
- 👤 Yukio Terakawa
- 👤 Akira Nishihara
- 👤 Koji Kono
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:04
CPC Classifications
C; C09; C09D; C09D163/00; C08; C08K; C08K3/00; C08K3/34; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31525; Y10T428/31942
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
86 words
A coating composition for architectural use comprising (a) a quaternary ammonium silicate having a silica content of from 10 to 60% by weight, (b) a liquid epoxide resin, (c) pigments and fillers and (d) water, the amount of component (b) being in the range of from 2 to 30 parts by weight as calculated on the basis of a solid content of 50% by weight per 100 parts by weight of component (a) as calculated on the basis of a silica content of 30% by weight.
Claim 2
Dependent Claim
86 words
A coating composition for architectural use comprising (a) a quaternary ammonium silicate having a silica content of from 10 to 60% by weight, (b) a liquid epoxide resin, (c) pigments and fillers and (d) water, the amount of component (b) being in the range of from 2 to 30 parts by weight as calculated on the basis of a solid content of 50% by weight per 100 parts by weight of component (a) as calculated on the basis of a silica content of 30% by weight.
Claim 3
Dependent Claim
120 words
A coating composition for architectural use comprising (a) a quaternary ammonium silicate having a silica content of 10 to 60% by weight, (b) a liquid epoxide resin, (c) a silica sol, (d) pigments and fillers and (e) water, the amount of component (b) being in the range of from 2 to 30 parts by weight as calculated on the basis of a solid content of 50% by weight and that of component (c) being in the range of from 10 to 100 parts by weight as calculated on the basis of a silica content of 30% by weight, both per 100 parts by weight of component (a) as calculated on the basis of a silica content of 30% by weight.
Claim 4
Dependent Claim
120 words
A coating composition for architectural use comprising (a) a quaternary ammonium silicate having a silica content of 10 to 60% by weight, (b) a liquid epoxide resin, (c) a silica sol, (d) pigments and fillers and (e) water, the amount of component (b) being in the range of from 2 to 30 parts by weight as calculated on the basis of a solid content of 50% by weight and that of component (c) being in the range of from 10 to 100 parts by weight as calculated on the basis of a silica content of 30% by weight, both per 100 parts by weight of component (a) as calculated on the basis of a silica content of 30% by weight.
Claim 5
Dependent Claim
32 words
The coating composition as claimed in claim 2 wherein the silica sol is stabilized by adding at least one dihydric alcohol having 3 or more carbon atoms and a water-soluble melamine resin.
Claim 6
Dependent Claim
94 words
A coating composition, according to claim 1, wherein said quaternary ammonium silicate has the general formula X(NR 1 R 2 R 3 R 4 ) 2 O.YSiO 2 .ZH 2 O wherein X is 1, Y is the number from 0.5 to 20, Z is the number from 0 to 99, N is a nitrogen atom and R 1 and R 2 , R 3 and R 4 each are a hydrogen atom, an alkyl group, or an alkoxy group, with the alkyl group and alkoxy group containing from 1 to 20 carbon atoms.
Claim 7
Dependent Claim
44 words
A coating composition according to claim 4, wherein said quaternary ammonium silicate is chosen from the group consisting of: tetraethanol ammonium silicate, tetraethyl ammonium silicate, tetramethyl ammonium silicate, diethyldimethanol ammonium silicate, dimethyldiethanol ammonium silicate, monomethyltripropanol ammonium silicate, dimethylpropanol ammonium silicate, and monoethylpropanol ammonium silicate.
Claim 8
Dependent Claim
37 words
A coating composition according to claim 1, wherein said epoxy resin has at least one epoxy end group and is chosen from the group consisting of bisphonol A epichlorohydrin compounds, glycidyl phthalate compounds, and alicyclic epoxide resins.
Claim 9
Dependent Claim
11 words
A coating according to claim 1, further including a curing agent.
Claim 10
Dependent Claim
37 words
A coating according to claim 7, wherein said curing agent is chosen from the group consisting of imidazole ring-containing aliphatic polyamines, aromatic polyamines, alicyclic polyamines, polyamidoamines, tertiary amines, fatty acids and their anhydrides, and modified aliphatic polyamines.
Claim 11
Dependent Claim
31 words
A coating composition according to claim 2, wherein said silica sol has a molar ratio of 20 to 400:1, and contains water or a hydrophilic organic solvent as a dispersion medium.
Claim 12
Dependent Claim
35 words
A coating composition according to claim 1, wherein said pigments are chosen from the group consisting of rutile titanium dioxide, anatase titanium dioxide, inorganic and organic pigments which are adaptable for forming a water-based paint.
Claim 13
Dependent Claim
28 words
A coating composition according to claim 1, wherein said fillers are chosen from the group consisting of calcium carbonate, powder of siliceous stones, white marble and silica sand.
Claim 14
Dependent Claim
92 words
A method of forming a coating composition according to claim 1 comprising the steps of adding a quaternary ammonium silicate to stable silica sol, fillers, and water to form a mixture, exposing the mixture to high-speed mixing to form a homogeneous mixture, adding an epoxide resin and a thickening agent to said homogeneous mixture to form a mixture with additives, agitating said mixture with additives until the epoxide resin and the thickening agent become completely dispersed in the mixture with additives, and adding a curing agent to the resulting mixture with additives.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-18 | 1983-08-20 | 1984-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-18 | 1987-08-20 | 1988-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-18 | 1991-08-20 | 1992-02-19 | $7700.00 | Window Closed / Lapsed |