Oxygen concentration detecting element and method of producing the same
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1978-04-20
•
Granted: 1980-02-05
•
Expires: 1998-04-20
Abstract
Abstract This invention provides an oxygen concentration detecting element and method of producing the same for use in detecting the oxygen concentration of gases such as exhaust gases from gasoline engines. The oxygen concentration detecting element is characterized by a shaped and sintered porous body consisting essentially of semiconductor materials and platinum particles dispersed at an average particle-to-particle spacing of no more than 10 mu throughout said element. The element has high durability and non-hysteresis characteristics, and can be used over a wide temperature range. The element is especially useful in detecting the oxygen concentration of an exhaust gas.
Inventors
- 👤 Hideaki Takahashi
- 👤 Takashi Takeuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:16
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/02; G01N27/04; G01N27/12; Y; Y10; Y10T; Y10T436/00; Y10T436/20; Y10T436/207497; Y10T436/208339
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
138 words
An oxygen concentration detecting element which is an electrical resistance element for the detection of oxygen concentration in the exhaust gases of internal combustion engines comprising a shaped molded and sintered porous body consisting essentially 70 to 99 weight percent of oxide-semiconductor material selected from the group consisting of titanium oxide, cerium oxide, niobium oxide, tantalum oxide, cobalt oxide and hafnium oxide and 1 to 30 weight percent of platinum particles sintered together with the powder form of said oxide semiconductor material, said platinum particles being dispersed substantially uniformly throughout said porous body thus obtained at an average particle-to-particle spacing of 0.1μ to 10μ, said element being so designed that a change in the resistance of the sintered porous body due to a change in oxygen concentration of gases in which the element is placed may be measured.
Claim 2
Dependent Claim
138 words
An oxygen concentration detecting element which is an electrical resistance element for the detection of oxygen concentration in the exhaust gases of internal combustion engines comprising a shaped molded and sintered porous body consisting essentially 70 to 99 weight percent of oxide-semiconductor material selected from the group consisting of titanium oxide, cerium oxide, niobium oxide, tantalum oxide, cobalt oxide and hafnium oxide and 1 to 30 weight percent of platinum particles sintered together with the powder form of said oxide semiconductor material, said platinum particles being dispersed substantially uniformly throughout said porous body thus obtained at an average particle-to-particle spacing of 0.1μ to 10μ, said element being so designed that a change in the resistance of the sintered porous body due to a change in oxygen concentration of gases in which the element is placed may be measured.
Claim 3
Dependent Claim
16 words
An oxygen concentration detecting element according to claim 1, wherein said oxide-semiconductor material is titanium oxide.
Claim 4
Dependent Claim
16 words
An oxygen concentration detecting element according to claim 1, wherein said oxide-semiconductor material is cerium oxide.
Claim 5
Dependent Claim
16 words
An oxygen concentration detecting element according to claim 1, wherein said oxide-semiconductor material is niobium oxide.
Claim 6
Dependent Claim
27 words
An oxygen concentration detecting element according to claim 1, wherein said oxide-semiconductor material is selected from the group consisting of tantalum oxide, cobalt oxide, and hafnium oxide.
Claim 7
Dependent Claim
22 words
An oxygen concentration detecting resistance element according to claim 1 wherein said molded and sintered porous body has lead wires connected thereto.
Claim 8
Dependent Claim
32 words
An element according to claim 6 which exhibits a sharp range in resistance at about the stoichiometric air to fuel ratio over a range of temperatures of about 400° to 900° C.
Claim 9
Dependent Claim
27 words
An element according to claim 1 wherein the platinum particles in the sintered body are characterized by a diameter substantially in the range of 0.1 to 0.3μ.
Claim 10
Dependent Claim
108 words
A process for producing an oxygen concentration detecting element which is an electrical resistance element comprising the steps of: mixing 1-30% by weight of platinum particles of average diameters falling within the range of 10 A to 100μ and 70 to 99% by weight of powdered oxide-semiconductor material selected from the group consisting titanium oxide, cerium oxide, niobium oxide, tantalum oxide, cobalt oxide, and hafnium oxide, press molding the mixture thus prepared into a given shape; and heating and sintering the thus shaped body at an elevated temperature in air until a particle to particle spacing of platinum particle in the range of 0.1 to 10μ is obtained.
Claim 11
Dependent Claim
108 words
A process for producing an oxygen concentration detecting element which is an electrical resistance element comprising the steps of: mixing 1-30% by weight of platinum particles of average diameters falling within the range of 10 A to 100μ and 70 to 99% by weight of powdered oxide-semiconductor material selected from the group consisting titanium oxide, cerium oxide, niobium oxide, tantalum oxide, cobalt oxide, and hafnium oxide, press molding the mixture thus prepared into a given shape; and heating and sintering the thus shaped body at an elevated temperature in air until a particle to particle spacing of platinum particle in the range of 0.1 to 10μ is obtained.
Claim 12
Dependent Claim
20 words
A process for producing an oxygen concentration detecting element according to claim 9, wherein said oxide-semiconductor material is titanium oxide.
Claim 13
Dependent Claim
20 words
A process for producing an oxygen concentration detecting element according to claim 9, wherein said oxide-semiconductor material is cerium oxide.
Claim 14
Dependent Claim
20 words
A process for producing an oxygen concentration detecting element according to claim 9, wherein said oxide-semiconductor material is niobium oxide.
Claim 15
Dependent Claim
31 words
A process for producing an oxygen concentration detecting element according to claim 9, wherein said oxide-semiconductor material is selected from the group consisting of tantalum oxide, cobalt oxide, and hafnium oxide.
Claim 16
Dependent Claim
30 words
A process for producing an oxygen concentration detecting element according to claim 9, wherein the average diameter of said powdered oxide-semiconductor material is in a range of 0.1 to 1μ.
Claim 17
Dependent Claim
30 words
A process for producing an oxygen concentration detecting element according to claim 14, wherein said thus shaped body is sintered at temperatures as high as 1000° C. to 1300° C.
Claim 18
Dependent Claim
39 words
A process according to claim 9 wherein the platinum particles mixed with the powdered oxide-semiconductor material is platinum black and the diameters of the platinum particles in the sintered body falls in the range of about 0.1 to 0.3μ.
Claim 19
Dependent Claim
107 words
A process for producing an oxygen concentration detecting element which is an electrical resistance element comprising the steps of: feeding the particles of oxide-semiconductor material coated with 1-30% by weight of platinum into a mold; molding said particles into a given shape; and then heating and sintering in air the thus shaped body into a porous body, at an elevated temperature of 1000° to 1300° C. until a particle to particle spacing of platinum particles within the range of 0.1μ to 10μ is obtained, the oxide-semiconductor material being selected from the group consisting of titanium oxide, cerium oxide, niobium oxide, tantalum oxide, cobalt oxide and hafnium oxide.
Claim 20
Dependent Claim
107 words
A process for producing an oxygen concentration detecting element which is an electrical resistance element comprising the steps of: feeding the particles of oxide-semiconductor material coated with 1-30% by weight of platinum into a mold; molding said particles into a given shape; and then heating and sintering in air the thus shaped body into a porous body, at an elevated temperature of 1000° to 1300° C. until a particle to particle spacing of platinum particles within the range of 0.1μ to 10μ is obtained, the oxide-semiconductor material being selected from the group consisting of titanium oxide, cerium oxide, niobium oxide, tantalum oxide, cobalt oxide and hafnium oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-04 | 1983-08-06 | 1984-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-04 | 1987-08-06 | 1988-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-04 | 1991-08-06 | 1992-02-05 | $7700.00 | Window Closed / Lapsed |