US4187350A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Porous catalyzed electrode provision and technique
Assignee: Dow Chemical Co
•
Filing: 1978-09-05
•
Granted: 1980-02-05
•
Expires: 1998-09-05
Abstract
Abstract A porous electrode, possessed of good physical qualities, containing size optimized electrocatalyst-bearing pores ensuring suitability for electrochemical reaction promotion, including the electroreduction of oxygen in alkaline media, is comprised of the compressed and compacted product of a pre-catalyzed, volumetrically reduced pre-form structure that, prior to densification, was characterizable in being laced with precursive interstitial passageways that are larger than electrode body pore size and which are comparably of a more open catalyst-applicating accessibility which passageways had been pre-provided on their wall surfaces with effective quantity deposits of catalytic agent.
Inventors
- 👤 James A. McIntyre
- 👤 Robert F. Phillips
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 11:49
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/88; H01M4/8878; H01M4/8896; C; C25; C25B; C25B11/00; H01M4/8605; H01M4/8621; H01M4/8825; H01M4/8853; H01M4/886; H01M4/90; H01M4/9041; H01M2004/8678; H01M2004/8689; H01M2300/00; H01M2300/0002; H01M2300/0014; H01M4/8803; H01M4/8807; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
145 words
Technique for the fabrication of a catalyzed porous electrode body that is copiously laced with a great multiplicity of body-traversing, internal pores having fine size pore measurements on the order of average nominal diameter or equivalent measure between about 0.1 and about 12 microns and a porosity of between about 30 and about 90 volume percent, based on the percentage of porulous void space in the total volume of the electrode body, said technique comprising taking as a pre-form a porous body of ductile, compressible, electroconductive material of construction having therein a plurality of interstitial precursor passageways that have a nominal average passageway diameter or equivalent measure greater than about 12 microns; then subjecting said pre-form to pressure adequate to densify same and reduce the size of said precursor passageways to an average nominal diameter or equivalent measure that is less than about 12 microns.
Claim 2
Dependent Claim
145 words
Technique for the fabrication of a catalyzed porous electrode body that is copiously laced with a great multiplicity of body-traversing, internal pores having fine size pore measurements on the order of average nominal diameter or equivalent measure between about 0.1 and about 12 microns and a porosity of between about 30 and about 90 volume percent, based on the percentage of porulous void space in the total volume of the electrode body, said technique comprising taking as a pre-form a porous body of ductile, compressible, electroconductive material of construction having therein a plurality of interstitial precursor passageways that have a nominal average passageway diameter or equivalent measure greater than about 12 microns; then subjecting said pre-form to pressure adequate to densify same and reduce the size of said precursor passageways to an average nominal diameter or equivalent measure that is less than about 12 microns.
Claim 3
Dependent Claim
48 words
The technique of claim 1 and including, in addition thereto and in combination therewith: the preliminary step of depositing an electrocatalytic agent substance in effective laid quantities on the interior wall surfaces of said precursor interstitial passageways of said pre-form prior to subjecting said pre-form to compacting pressure.
Claim 4
Dependent Claim
26 words
A technique in accordance with the technique of claim 2, wherein the said size of said precursor passageways is between about 20 and about 100 microns.
Claim 5
Dependent Claim
34 words
A technique in accordance with the technique of claim 2, wherein said material of construction is comprised of a metal selected from the group consisting of nickel, iron, stainless steel alloys, copper and titanium.
Claim 6
Dependent Claim
17 words
A technique in accordance with the technique of claim 2, wherein said material of construction is nickel.
Claim 7
Dependent Claim
22 words
A technique in accordance with the technique of claim 2, wherein the deposition of the electrocatalytic agent is done by silver plating.
Claim 8
Dependent Claim
27 words
A technique in accordance with the technique of claim 2, wherein the deposition of the electrocatalytic agent is done by a coating application of a catalytically-active substance.
Claim 9
Dependent Claim
30 words
A technique in accordance with the technique of claim 2, wherein said pre-form is a relatively flat body which is subject to pressure in a face-to-face direction across its thickness.
Claim 10
Dependent Claim
39 words
A technique in accordance with the technique of claim 2, wherein said pre-form is a flat, sheet-like body which is subjected to squeezing pressure by passage between the nip of at least one stand of a compacting roller arrangement.
Claim 11
Dependent Claim
33 words
A technique in accordance with the technique of claim 2, wherein said pre-form is subjected to enough pressure to reduce its face-to-face thickness by between about 20 and about 70 percent in measure.
Claim 12
Dependent Claim
33 words
A technique in accordance with the technique of claim 2, wherein said pre-form is subjected to enough pressure to reduce its face-to-face thickness by between about 30 and about 60 percent in measure.
Claim 13
Dependent Claim
137 words
A catalyzed porous electrode body having a structure comprising: an electroconductive material of construction shaped into electrode body form; said electrode body form containing a great multiplicity of fine pores traversing said body that have an average nominal diameter size or equivalent measure of between about 0.1 and 12 microns; said electrode body form also having a porosity of between about 30 and about 90 volume percent, based on the volume of porulous void space in the total volume of the electrode body; said body being further characterizable as the physically compressed and densified remains of a porous pre-form of a preliminary body of the same material of construction copiously laced with interstitial passageways that were precursors of said fine pores and which had an average nominal diameter or equivalent measure in excess of about 12 microns.
Claim 14
Dependent Claim
137 words
A catalyzed porous electrode body having a structure comprising: an electroconductive material of construction shaped into electrode body form; said electrode body form containing a great multiplicity of fine pores traversing said body that have an average nominal diameter size or equivalent measure of between about 0.1 and 12 microns; said electrode body form also having a porosity of between about 30 and about 90 volume percent, based on the volume of porulous void space in the total volume of the electrode body; said body being further characterizable as the physically compressed and densified remains of a porous pre-form of a preliminary body of the same material of construction copiously laced with interstitial passageways that were precursors of said fine pores and which had an average nominal diameter or equivalent measure in excess of about 12 microns.
Claim 15
Dependent Claim
34 words
The electrode body of claim 12 and including, in addition thereto and in combination therewith, a deposit in effective quantity of an electrocatalytically-active substance laid on the interior wall surfaces of said fine pores.
Claim 16
Dependent Claim
25 words
An electrode body in accordance with that of claim 13, wherein said fine pores have an average size between about 3 and about 8 microns.
Claim 17
Dependent Claim
25 words
An electrode body in accordance with that of claim 13, wherein the porosity of said electrode body is between about 30 and about 90 percent.
Claim 18
Dependent Claim
35 words
An electrode body in accordance with that of claim 13, wherein said material of construction is comprised of a ductile metal selected from the group consisting of nickel, iron, stainless steel alloys, copper and titanium.
Claim 19
Dependent Claim
17 words
An electrode body in accordance with that of claim 13, wherein said material of construction is nickel.
Claim 20
Dependent Claim
16 words
An electrode body in accordance with that of claim 13, wherein said electrocatalytically-active deposit is silver.
Claim 21
Dependent Claim
42 words
An electrode body in accordance with that of claim 13, wherein said electrocatalytically-active deposit is in an application load level laid down in a quantity of between about 0.005 and 7.5 milligrams of catalyst per cubic centimeter of porous electrode body volume.
Claim 22
Dependent Claim
42 words
An electrode body in accordance with that of claim 13, wherein said electrocatalytically-active deposit is in an application load level laid down in a quantity of between about 1 and 2.5 milligrams of catalyst per cubic centimeter of porous electrode body volume.
Claim 23
Dependent Claim
25 words
An electrode body in accordance with that of claim 13, wherein the thickness of said electrode body is between about 5 and about 500 mils.
Claim 24
Dependent Claim
25 words
An electrode body in accordance with that of claim 13, wherein the thickness of said electrode body is between about 15 and about 100 mils.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-04 | 1983-08-06 | 1984-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-04 | 1987-08-06 | 1988-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-04 | 1991-08-06 | 1992-02-05 | $7700.00 | Window Closed / Lapsed |