Process for making a ceramic article having a dense integral outer barrier layer and a high degree of porosity and crushability characteristics
Assignee: General Electric Co
•
Filing: 1977-10-06
•
Granted: 1980-02-05
•
Expires: 1997-10-06
Abstract
Abstract A method for simultaneously forming an integral barrier layer on selected external surfaces of a fired alumina-based compound ceramic article and for increasing the porosity and crushability characteristics thereof embodies the sintering of a ceramic compact comprising a reactant fugitive filler material and the alumina-based compound ceramic material in a controlled atmosphere.
Inventors
- 👤 Charles D. Greskovich
- 👤 Frederic J. Klug
- 👤 Wayne D. Pasco
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:18
CPC Classifications
B; B22; B22C; B22C1/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
191 words
A method for increasing the porosity and crushability characteristics of cores and molds for investment casting including the process steps of (a) preparing a material composition consisting essentially of a reactant fugitive filler material which is one selected from the group consisting of carbon, aluminum, aluminum carbide, aluminum oxycarbide, boron and boron carbide and an alumina-based ceramic compound material having the general formula MO.NAl 2 O 3 wherein M is Na 2 , Ca, Sr, or Ba N is from 9 to 11 when M is Na 2 , and N is 6 when M is Ca, Sr, or Ba; (b) working a portion of the material composition to produce a preform of a predetermined shape; (c) sintering the preform in a controlled furnace atmosphere to cause a reaction between at least the alumina-based compound material and the reactant fugitive filler material to produce at least one or more suboxides of alumina to produce an alumina ceramic article having a predetermined continuous porosity content and crushability characteristics, and (d) oxidizing at least a portion of the suboxides of alumina to form a dense integral barrier layer of alumina at the surface.
Claim 2
Independent Claim
191 words
A method for increasing the porosity and crushability characteristics of cores and molds for investment casting including the process steps of (a) preparing a material composition consisting essentially of a reactant fugitive filler material which is one selected from the group consisting of carbon, aluminum, aluminum carbide, aluminum oxycarbide, boron and boron carbide and an alumina-based ceramic compound material having the general formula MO.NAl 2 O 3 wherein M is Na 2 , Ca, Sr, or Ba N is from 9 to 11 when M is Na 2 , and N is 6 when M is Ca, Sr, or Ba; (b) working a portion of the material composition to produce a preform of a predetermined shape; (c) sintering the preform in a controlled furnace atmosphere to cause a reaction between at least the alumina-based compound material and the reactant fugitive filler material to produce at least one or more suboxides of alumina to produce an alumina ceramic article having a predetermined continuous porosity content and crushability characteristics, and (d) oxidizing at least a portion of the suboxides of alumina to form a dense integral barrier layer of alumina at the surface.
Claim 3
Dependent Claim
196 words
The method of claim 1 wherein the reactant fugitive filler material is a form of carbon, the controlled furnace atmosphere has a partial pressure of oxygen equivalent to that of hydrogen gas having a dewpoint of from about -5° F. to no greater than +25° F., the preform of the material composition is heated at a rate of at least 100° C. per hour through a first predetermined range of temperature to about 900° C. while retaining the reactant fugitive filler material therein, the preform is heated at a rate of greater than 200° C. per hour to a second predetermined temperature range of from about 1650° C. to about 1900° C. to prevent excess oxidation of the reactant fugitive filler material, the preform is isothermally heated within the second predetermined temperature range for a sufficient time to chemically react substantially all of the reactant filler material with the alumina-based ceramic material to form suboxides of alumina, and vapor transporting at least some of the suboxides of alumina of the fired ceramic article to obtain the desired level of porosity, the grain morphology and the dense integral barrier layer of alumina in the fired ceramic article.
Claim 4
Dependent Claim
37 words
The method of claim 2 wherein the preform is heated in the second predetermined temperature range in a controlled atmosphere of a gas which is one selected from the group consisting of argon, helium, neon, and hydrogen.
Claim 5
Dependent Claim
26 words
The method of claim 2 wherein the alumina-based ceramic compound material after firing is α-alumina, and the material of the dense integral barrier layer is α-alumina.
Claim 6
Dependent Claim
21 words
The method of claim 4 wherein the average particle size of the ceramic and filler material is less than 100 microns.
Claim 7
Dependent Claim
16 words
The method of claim 5 wherein the average particle size is from 1 to 50 microns.
Claim 8
Dependent Claim
27 words
The method of claim 6 wherein the gas in the controlled atmosphere is hydrogen, and the dewpoint of the gas is from 0° F. to +25° F.
Claim 9
Dependent Claim
23 words
The method of claim 7 wherein the mol ratio of carbon to the alumina in the ceramic material is from 0.1 to 1.0.
References Cited (Backward Citations)
US2593507A
Cited
US3538202A
Cited
US4031177A
Cited
US3903225A
Cited
US3969124A
Cited
US4013477A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-04 | 1983-08-06 | 1984-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-04 | 1987-08-06 | 1988-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-04 | 1991-08-06 | 1992-02-05 | $7700.00 | Window Closed / Lapsed |