Method for improving the durability of spontaneous NaF opal glassware
Assignee: Corning Glass Works
•
Filing: 1978-05-08
•
Granted: 1980-02-05
•
Expires: 1998-05-08
Abstract
Abstract Spontaneous sodium fluoride opal glassware is treated to improve surface durability against aqueous attack by controlled sodium depletion and subsequent heat consolidation of the glass surface. The method comprises extracting surface sodium ions using water or dilute aqueous acidic solutions and subsequently consolidating by heat the surface to produce a glossy surface without any migration of sodium ions.
Inventors
- 👤 Kun-Er Lu
- 👤 Walter H. Tarcza
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:11
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/005; C03C21/00; C03C21/001; C03C23/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
138 words
A method for improving the durability of a spontaneous sodium fluoride opal glass article against surface attack by water which comprises the steps of: (a) contacting the glass article with a Na 2 O-extracting medium comprising water at a temperature in the range of about 50°-100° C. for a time sufficient to deplete the Na 2 O content of the surface layer but insufficient to remove all of the extractable Na 2 O therefrom; and thereafter (b) heating the glass article to a temperature in the range of about 200°-500° C. for a time sufficient to consolidate the Na 2 O-depleted surface layer but insufficient to permit the migration of additional Na 2 O from the interior of the glass article to the surface thereof, thus to provide a surface free from microcracking and with good surface gloss.
Claim 2
Independent Claim
138 words
A method for improving the durability of a spontaneous sodium fluoride opal glass article against surface attack by water which comprises the steps of: (a) contacting the glass article with a Na 2 O-extracting medium comprising water at a temperature in the range of about 50°-100° C. for a time sufficient to deplete the Na 2 O content of the surface layer but insufficient to remove all of the extractable Na 2 O therefrom; and thereafter (b) heating the glass article to a temperature in the range of about 200°-500° C. for a time sufficient to consolidate the Na 2 O-depleted surface layer but insufficient to permit the migration of additional Na 2 O from the interior of the glass article to the surface thereof, thus to provide a surface free from microcracking and with good surface gloss.
Claim 3
Dependent Claim
46 words
A method in accordance with claim 1 wherein the sodium fluoride opal glass article is composed of a sodium aluminosilicate glass having a composition comprising in weight percent, about 71-78% SiO 2 , 5-9% Al 2 O 3 , 8-13% Na 2 O and 3-6% F.
Claim 4
Dependent Claim
41 words
A method in accordance with claim 2 wherein the glass further comprises up to about 10% total of optional constituents selected from the group consisting of SrO, BaO, CaO, B 2 O 3 , K 2 O and Li 2 O.
Claim 5
Independent Claim
129 words
A method for improving the durability of a spontaneous sodium fluoride opal glass article against surface attack by water which comprises the steps of: (a) contacting the glass article with a Na 2 O-extracting medium selected from the group consisting of water and dilute aqueous acidic solutions at a temperature in the range of about 50°-100° C. for a time in the range of about 1/4-15 minutes; and thereafter (b) heating the glass article to a temperature in the range of about 200°-500° C. for a time in the range of about 1-60 minutes but insufficient to permit the migration of additional Na 2 O from the interior of the glass article to the surface thereof, thus to provide a surface free from microcracking and with good surface gloss.
Claim 6
Independent Claim
129 words
A method for improving the durability of a spontaneous sodium fluoride opal glass article against surface attack by water which comprises the steps of: (a) contacting the glass article with a Na 2 O-extracting medium selected from the group consisting of water and dilute aqueous acidic solutions at a temperature in the range of about 50°-100° C. for a time in the range of about 1/4-15 minutes; and thereafter (b) heating the glass article to a temperature in the range of about 200°-500° C. for a time in the range of about 1-60 minutes but insufficient to permit the migration of additional Na 2 O from the interior of the glass article to the surface thereof, thus to provide a surface free from microcracking and with good surface gloss.
Claim 7
Dependent Claim
38 words
A method in accordance with claim 4 wherein the Na 2 O-extracting medium is a dilute aqueous acidic solution composed of water and an organic or inorganic acid in a concentration of up to about 0.5% by weight.
References Cited (Backward Citations)
US2261691A
Cited
US2464851A
Cited
US3451796A
Cited
US3653864A
Cited
US3948629A
Cited
US4026692A
Cited
US4019884A
Cited
US4086074A
Cited
US4107388A
Cited
US4038448A
Cited
US4080188A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-04 | 1983-08-06 | 1984-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-04 | 1987-08-06 | 1988-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-04 | 1991-08-06 | 1992-02-05 | $7700.00 | Window Closed / Lapsed |