Substantially amorphous polyolefins useful as pressure-sensitive adhesives
Assignee: Eastman Chemical Co
•
Filing: 1978-11-02
•
Granted: 1980-01-29
•
Expires: 1998-11-02
Abstract
Abstract The invention relates to a process for the treatment of substantially amorphous polyolefins to provide permanently tacky, low viscosity materials which have useful pressure-sensitive adhesive properties. These permanently tacky amorphous polyolefin homo- and copolymers, as well as blends of such amorphous polyolefins with crystalline polyolefins containing up to 20 weight percent crystalline polyolefin, are novel pressure-sensitive adhesives.
Inventors
- 👤 Robert R. Schmidt, III
- 👤 Jerry D. Holmes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 04:52
CPC Classifications
C; C09; C09J; C09J123/00; C09J123/02; C08; C08F; C08F8/00; C08F8/50
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
59 words
A process for preparing tacky modified amorphous polyolefin compositions useful as pressure-sensitive adhesives which comprises reacting substantially amorphous polyolefin having a melt viscosity of about 100 to 200,000 cp. at 190° C. with at least 1 weight percent of silica-alumina catalyst at a temperature of at least 250° C. to provide a low viscosity, permanently tacky hot-melt pressure-sensitive adhesive.
Claim 2
Dependent Claim
59 words
A process for preparing tacky modified amorphous polyolefin compositions useful as pressure-sensitive adhesives which comprises reacting substantially amorphous polyolefin having a melt viscosity of about 100 to 200,000 cp. at 190° C. with at least 1 weight percent of silica-alumina catalyst at a temperature of at least 250° C. to provide a low viscosity, permanently tacky hot-melt pressure-sensitive adhesive.
Claim 3
Dependent Claim
80 words
A process according to claim 1 wherein said substantially amorphous polyolefin is a member of the group selected from substantially amorphous homopolymers of 1-olefins containing 3 to 5 carbon atoms, substantially amorphous copolymers prepared from either ethylene and 1-olefins containing 3 to 5 carbon atoms or propylene and 1-butene, and amorphous propylene or 1-butene/higher 1-olefin copolymers containing less than 40 mole percent of at least one higher 1-olefin of the group consisting essentially of 1-hexene, 1-heptene, 1-octene, 1-nonene, and 1-decene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-28 | 1983-07-30 | 1984-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-28 | 1987-07-30 | 1988-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-28 | 1991-07-30 | 1992-01-29 | $7700.00 | Window Closed / Lapsed |