Foamed radiation-crosslinked high density polyethylenes
Assignee: Dow Chemical Co
•
Filing: 1977-12-14
•
Granted: 1980-01-29
•
Expires: 1997-12-14
Abstract
Abstract Foamed radiation-crosslinked high density polyethylenes having substantially closed cells and uniform structure are made from radiation-crosslinked high density polyethylene compositions comprising thermosensitive foaming agents by heating such compositions while excluding molecular oxygen from contact therewith during that heating and foaming step. Oxygen is excluded by providing an oxygen-free inert gas atmosphere or by submerging the foamable material beneath the surface of a body of liquid heat transfer medium during the heating and foaming step.
Inventors
- 👤 Louis C. Rubens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:42
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08J9/10; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; Y; Y10; Y10S; Y10S521/00; Y10S521/915
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
156 words
A method which comprises the steps of (a) intimately mixing together a mixture comprising high density polyethylene and thermosensitive chemical foaming agent which decomposes to form a gas at a decomposing temperature above the softening point temperature of the polyethylene to form a non-cellular foamable composition, (b) shaping the resulting composition into a non-cellular foamable shape at a temperature below the decomposing temperature of the foaming agent, (c) subjecting the resulting non-cellular foamable shape to high energy radiation to effect crosslinking of the polyethylene therein, and (d) foaming the resulting radiation-crosslinked high density polyethylene-containing foamable shape by heating the same in at least one substantially oxygen-free medium selected from the group consisting of inert gasses and molten low-melting salts to a temperature above the decomposing temperature of the thermosensitive foaming agent in the composition of the foamable shape, thereby making a foamed radiation-crosslinked high density polyethylene foam product having substantially closed and uniform fine-celled foam structure.
Claim 2
Independent Claim
156 words
A method which comprises the steps of (a) intimately mixing together a mixture comprising high density polyethylene and thermosensitive chemical foaming agent which decomposes to form a gas at a decomposing temperature above the softening point temperature of the polyethylene to form a non-cellular foamable composition, (b) shaping the resulting composition into a non-cellular foamable shape at a temperature below the decomposing temperature of the foaming agent, (c) subjecting the resulting non-cellular foamable shape to high energy radiation to effect crosslinking of the polyethylene therein, and (d) foaming the resulting radiation-crosslinked high density polyethylene-containing foamable shape by heating the same in at least one substantially oxygen-free medium selected from the group consisting of inert gasses and molten low-melting salts to a temperature above the decomposing temperature of the thermosensitive foaming agent in the composition of the foamable shape, thereby making a foamed radiation-crosslinked high density polyethylene foam product having substantially closed and uniform fine-celled foam structure.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein the inert gas is nitrogen gas.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the molten low-melting salt comprises potassium nitrate and sodium nitrite.
Claim 5
Dependent Claim
79 words
The method of claim 3 wherein the foaming agent in the starting mixture is azobisformamide in amount such that the foam density of the resulting foam product is from about 0.024 to about 0.24 g/cc, the non-cellular foamable shape is a sheet and is irradiated with high energy electrons to dosage from about 3 to about 7 mrads, and the temperature of the molten low-melting salt in the foaming step (d) is from about 215° to about 300° C.
Claim 6
Dependent Claim
50 words
As a new manufacture, foamed radiation-crosslinked high density polyethylene having substantially closed fine cells, uniform structure, compressive strength under compression load at 25% deflection from about 0.4 to about 520 kg/cm 2 , and foam density from about 0.024 to about 0.5 g/cc, made by the method of claim 1.
Claim 7
Dependent Claim
51 words
As a new manufacture, foamed radiation-crosslinked high density polyethylene sheet having substantially closed fine cells, uniform structure, compressive strength under compression load at 25% deflection from about 0.4 to about 260 kg/cm 2 , and foam density from about 0.024 to about 0.24 g/cc, made by the method of claim 4.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-28 | 1983-07-30 | 1984-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-28 | 1987-07-30 | 1988-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-28 | 1991-07-30 | 1992-01-29 | $7700.00 | Window Closed / Lapsed |