Production of amino-silicate compounds, condensation resinous products and foam
Assignee: Individual
•
Filing: 1978-10-27
•
Granted: 1980-01-22
•
Expires: 1998-10-27
Abstract
Abstract Poly(aldehyde amino silicate) foams are produced by mixing an amino compound, an aldehyde, a silicon oxide compound and a blowing agent; then a curing agent is added, thereby producing a rigid, porous product.
Inventors
- 👤 David H. Blount
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 10:41
CPC Classifications
C; C08; C08G; C08G12/00; C08G12/02; C08G12/04; C08G12/26; C08G12/30; C08G12/40
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
194 words
The foamed poly(aldehyde amino silicate) resinous product obtained by reacting a mixture of components: A. 0.5 to 2 mols of an oxidated silicon compound selected from the group consisting of hydrated silica, alkali metal silicates, natural silicates containing free silicic acid groups B. 1 mol of an amino compound selected from the group consisting of urea, melamine, thiourea, dicyandiamide, alkyl-substituted ureas, alkyl-substituted thioureas, aniline and mixtures thereof, and C. an aqueous solution of formaldehyde in the ration of 1 mol of amino silicate compound to 1 to 5 mols of formaldehyde; D. an inert liquid, boiling at temperatures from -25° C. to +50° C., is included in the reaction mixture as a blowing agent in the quantity of up to 50% by weight, and the reaction mixture is allowed to react to completion while foaming; E. a curing agent is added in sufficient amounts to adjust the pH to 4 to 8 or up to 95% by weight, based on the weight of the reactants, selected from the group consisting of mineral acids, hydrogen-containing acid salts, organic acids, acid alkyl phosphates, sulphonic acids, carboxylic acid chlorides, sulphonic acid chlorides, organic polyisocyanates and mixtures thereof.
Claim 2
Dependent Claim
194 words
The foamed poly(aldehyde amino silicate) resinous product obtained by reacting a mixture of components: A. 0.5 to 2 mols of an oxidated silicon compound selected from the group consisting of hydrated silica, alkali metal silicates, natural silicates containing free silicic acid groups B. 1 mol of an amino compound selected from the group consisting of urea, melamine, thiourea, dicyandiamide, alkyl-substituted ureas, alkyl-substituted thioureas, aniline and mixtures thereof, and C. an aqueous solution of formaldehyde in the ration of 1 mol of amino silicate compound to 1 to 5 mols of formaldehyde; D. an inert liquid, boiling at temperatures from -25° C. to +50° C., is included in the reaction mixture as a blowing agent in the quantity of up to 50% by weight, and the reaction mixture is allowed to react to completion while foaming; E. a curing agent is added in sufficient amounts to adjust the pH to 4 to 8 or up to 95% by weight, based on the weight of the reactants, selected from the group consisting of mineral acids, hydrogen-containing acid salts, organic acids, acid alkyl phosphates, sulphonic acids, carboxylic acid chlorides, sulphonic acid chlorides, organic polyisocyanates and mixtures thereof.
Claim 3
Dependent Claim
153 words
The foamed aldehyde-amino-silicate resinous product obtained by reacting a mixture of components: A. 0.5 to 4 mols of silica sol, mols being calculated on the silicon dioxide content, B. 1 mol of an amino compound selected from the group consisting of urea, thiourea, melamine, alkyl-substituted ureas, dicyandiamide, aniline, aliphatic and aromatic diamines and mixtures thereof C. 1 to 5 mols of an aqueous formaldehyde solution, D. an inert liquid, boiling at temperatures from -25° C. to +50° C., is included in the reaction mixture as a blowing agent in the quantity of up to 50% by weight, and the reaction is allowed to react to completion while foaming, E. a curing agent is added in sufficient amounts to adjust the pH to 4 to 6.5 and selected from the group consisting of mineral acids, hydrogen-containing acid salts, organic acids, acid alkyl phosphates, sulphonic acid, carboxylic acid chlorides, sulphonic acid chlorides, and mixtures thereof.
Claim 4
Dependent Claim
153 words
The foamed aldehyde-amino-silicate resinous product obtained by reacting a mixture of components: A. 0.5 to 4 mols of silica sol, mols being calculated on the silicon dioxide content, B. 1 mol of an amino compound selected from the group consisting of urea, thiourea, melamine, alkyl-substituted ureas, dicyandiamide, aniline, aliphatic and aromatic diamines and mixtures thereof C. 1 to 5 mols of an aqueous formaldehyde solution, D. an inert liquid, boiling at temperatures from -25° C. to +50° C., is included in the reaction mixture as a blowing agent in the quantity of up to 50% by weight, and the reaction is allowed to react to completion while foaming, E. a curing agent is added in sufficient amounts to adjust the pH to 4 to 6.5 and selected from the group consisting of mineral acids, hydrogen-containing acid salts, organic acids, acid alkyl phosphates, sulphonic acid, carboxylic acid chlorides, sulphonic acid chlorides, and mixtures thereof.
Claim 5
Dependent Claim
186 words
The foamed poly(aldehyde amino silicate) resinous product obtained by reacting a mixture of components: A. 2 to 50 parts by weight of an alkali metal silicate with a molar ratio of Me 2 OSiO 2 (Me=metal) of between 4 to 1 and 0.2 to 1 and is selected from the group consisting of sodium silicate, potassium silicate, lithium silicate, and mixtures thereof, B. 20 to 50 parts by weight of urea, C. 1 to 5 mols of an aqueous formaldehyde solution for each mol of urea, D. an inert liquid, boiling at temperatures from -25° C. to +50° C., is included in the reaction mixture as a blowing agent in the quantity of up to 50% by weight, and the reaction mixture is allowed to react to completion while foaming, E. a curing agent is added until the pH is 4 to 8 or up to 95% by weight, based on the weight of the reactants, and selected from the group consisting of mineral acid, hydrogen-containing acid salts, organic acids, acid alkyl phosphates, sulphonic acid, carboxylic acid chlorides, sulphonic acid chlorides, organic polyisocyanates and mixtures thereof.
Claim 6
Dependent Claim
186 words
The foamed poly(aldehyde amino silicate) resinous product obtained by reacting a mixture of components: A. 2 to 50 parts by weight of an alkali metal silicate with a molar ratio of Me 2 OSiO 2 (Me=metal) of between 4 to 1 and 0.2 to 1 and is selected from the group consisting of sodium silicate, potassium silicate, lithium silicate, and mixtures thereof, B. 20 to 50 parts by weight of urea, C. 1 to 5 mols of an aqueous formaldehyde solution for each mol of urea, D. an inert liquid, boiling at temperatures from -25° C. to +50° C., is included in the reaction mixture as a blowing agent in the quantity of up to 50% by weight, and the reaction mixture is allowed to react to completion while foaming, E. a curing agent is added until the pH is 4 to 8 or up to 95% by weight, based on the weight of the reactants, and selected from the group consisting of mineral acid, hydrogen-containing acid salts, organic acids, acid alkyl phosphates, sulphonic acid, carboxylic acid chlorides, sulphonic acid chlorides, organic polyisocyanates and mixtures thereof.
Claim 7
Dependent Claim
93 words
The foamed poly(aldehyde amino silicate) resinous product obtained by reacting a mixture of components: A. an amino silicate compound, C. furfural in the ratio of 1 mol of amino silicate compound to 1 to 5 mols of furfural, D. a blowing agent, a halogenated hydrocarbon with a boiling point below 100° C., E. a curing agent is added in the amount to adjust the pH to 4 to 6.5 and is selected from the group consisting of mineral acids, hydrogen-containing acid salts, organic acids, carboxylic acid chlorides, sulphonic acid chlorides and mixtures thereof.
Claim 8
Dependent Claim
93 words
The foamed poly(aldehyde amino silicate) resinous product obtained by reacting a mixture of components: A. an amino silicate compound, C. furfural in the ratio of 1 mol of amino silicate compound to 1 to 5 mols of furfural, D. a blowing agent, a halogenated hydrocarbon with a boiling point below 100° C., E. a curing agent is added in the amount to adjust the pH to 4 to 6.5 and is selected from the group consisting of mineral acids, hydrogen-containing acid salts, organic acids, carboxylic acid chlorides, sulphonic acid chlorides and mixtures thereof.
Claim 9
Dependent Claim
23 words
The foamed poly(aldehyde amino silicate) resinous product of claim 4 wherein the mixture contains an inorganic or organic particulate, powder, or fibrous material.
Claim 10
Dependent Claim
56 words
The foamed poly(aldehyde amino silicate) resinous product of claim 3 wherein an inorganic water-binding component, being capable of absorbing water to form a solid or gel, is added in the amount up to 95% by weight, based on the reactants, and is selected from the group consisting of hydraulic cement, synthetic anhydride, gypsum or burnt line.
Claim 11
Dependent Claim
25 words
The foamed poly(aldehyde amino silicate) resinous product of claim 6 wherein the blowing agent is a halogenated hydrocarbon with a boiling point below 100° C.
Claim 12
Dependent Claim
19 words
The foamed poly(aldehyde amino silicate) resinous product of claim 1 wherein compressed air is used to foam the mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |