Method for polishing cadmium sulfide semiconductors
Assignee: United States Department of the Navy
•
Filing: 1978-10-05
•
Granted: 1980-01-22
•
Expires: 1998-10-05
Abstract
Abstract A method for polishing semiconductors, particularly surfaces of CdS. The method is comprised of polishing a substrate with a pad charged with Transene and Cab-O-Sil while an iodine solution is added in small quantities. The last period of polishing is done while flushing the polishing pad with Transene. Upon completion of polishing, the substrate is given an immediate wash with Transene, followed by ultrasonic cleaning in Transene. After the ultrasonic cleaning, the substrate is again rinsed in Transene and then spun dried. The cleaning process is continuous and the cleaning solutions are kept in active contact with the substrate in order to provide a haze-free product.
Inventors
- 👤 Anne M. Lackner
- 👤 Phillip G. Reif
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:01
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P52/00; H10P95/00; H10P95/70
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
53 words
A process for preparing a haze-free cadmium sulfide surface on a substrate by polishing which comprises subjecting said surface to the polishing action of a solution containing submicroscopic silica and simultaneously, while polishing, etching said surface with an iodine solution, and then cleaning said surface before said iodine solution dries on said surface.
Claim 2
Dependent Claim
53 words
A process for preparing a haze-free cadmium sulfide surface on a substrate by polishing which comprises subjecting said surface to the polishing action of a solution containing submicroscopic silica and simultaneously, while polishing, etching said surface with an iodine solution, and then cleaning said surface before said iodine solution dries on said surface.
Claim 3
Dependent Claim
43 words
A process for preparing a haze-free cadmium sulfide surface on a substrate as set forth in claim 1 wherein the last stage of polishing is done without adding said iodine solution and, while polishing, the polishing pads are flushed with a cleaning solvent.
Claim 4
Dependent Claim
28 words
A process for preparing a haze-free cadmium sulfide surface on a substrate as set forth in claim 1 wherein said iodine solution contains about 2 percent of iodine.
Claim 5
Dependent Claim
30 words
A process for preparing a haze-free cadmium sulfide surface on a substrate as set forth in claim 1 wherein said solution containing submicroscopic silica contains about 20 percent of silica.
Claim 6
Dependent Claim
47 words
A process for preparing a haze-free cadmium sulfide surface on a substrate as set forth in claim 1 including the steps of immediately removing said substrate upon completion of polishing, then flushing said cadmium sulfide surface with a cleaning solution and then immediately ultrasonically cleaning said surface.
Claim 7
Dependent Claim
42 words
A process for preparing a haze-free cadmium sulfide surface on a substrate as set forth in claim 5 including the steps of again flushing said surface with a cleaning fluid after ultrasonic cleaning has been completed and then spin drying said substrate.
Claim 8
Dependent Claim
27 words
A process for preparing a haze-free cadmium sulfide surface on a substrate as set forth in claim 1 wherein said polishing is done with a polishing machine.
References Cited (Backward Citations)
US3156596A
Cited
US3262825A
Cited
US3595718A
Cited
US3629023A
Cited
US4070797A
Cited
US4064660A
Cited
US4108716A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |