Method of manufacturing high strength low alloys steel plates with superior low temperature toughness
Assignee: JFE Engineering Corp
•
Filing: 1978-07-11
•
Granted: 1980-01-22
•
Expires: 1998-07-11
Abstract
Abstract A steel slab or bloom containing 0.3 DIFFERENCE 0.15% by weight of C, 0.05 DIFFERENCE 0.60% by weight of Si, 0.60 DIFFERENCE 2.5% by weight of Mn, 0.010 DIFFERENCE 0.15% by weight of Nb, 0.005 DIFFERENCE 0.10% by weight of soluble Al and the remainder of iron is heated to such a temperature region above 1050 DEG C. and below the reheating temperature where the austenitic grain size would be 150 mu . The heated slab or bloom is then hot rolled with total rolling reduction of more than 40% with respect to a finished thickness at the non-recrystallized austenitic region and the hot rolled stocks are subjected to accelerated cooling at a rate of 5 DEG DIFFERENCE 20 DEG C./sec. from a temperature higher than the Ar3 transformation point to a temperature within 550 DEG DIFFERENCE 650 DEG C. Finally the stocks are air cooled.
Inventors
- 👤 Chiaki Ouchi
- 👤 Tomoyoshi Okita
- 👤 Kazuaki Matsumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:01
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/02; C21D8/0221; C21D8/0226; C21D2211/00; C21D2211/002; C21D2211/005
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
160 words
A method of manufacturing high tensile strength and high toughness steel plates comprising the steps of reheating a steel slab or bloom comprising containing 0.03˜0.15% by weight of C, 0.04˜0.60% by weight of Si, 0.60˜2.5% by weight of Mn, 0.010˜0.15% by weight of Nb, 0.005˜0.10% by weight of soluble Al and the remainder iron to a temperature above 1050° C. and below the reheating temperature at which the austenite grain size would be 150μ or higher, hot rolling the heated steel slab or bloom in the temperature range between the temperature at which recrystallization of the austenite grains begins and the Ar 3 transformation point temperature sufficient to obtain a total reduction by said rolling of more than 40% with reference to the finished thickness, acceleratedly cooling said hot rolled steel at a rate of 5°˜20° C./sec. from a temperature higher than Ar 3 transformation point to a temperature within 550°˜650° C., and then air cooling said hot rolled steel.
Claim 2
Independent Claim
160 words
A method of manufacturing high tensile strength and high toughness steel plates comprising the steps of reheating a steel slab or bloom comprising containing 0.03˜0.15% by weight of C, 0.04˜0.60% by weight of Si, 0.60˜2.5% by weight of Mn, 0.010˜0.15% by weight of Nb, 0.005˜0.10% by weight of soluble Al and the remainder iron to a temperature above 1050° C. and below the reheating temperature at which the austenite grain size would be 150μ or higher, hot rolling the heated steel slab or bloom in the temperature range between the temperature at which recrystallization of the austenite grains begins and the Ar 3 transformation point temperature sufficient to obtain a total reduction by said rolling of more than 40% with reference to the finished thickness, acceleratedly cooling said hot rolled steel at a rate of 5°˜20° C./sec. from a temperature higher than Ar 3 transformation point to a temperature within 550°˜650° C., and then air cooling said hot rolled steel.
Claim 3
Dependent Claim
47 words
The method according to claim 1 wherein said steel slab or bloom also contains at least one of less than 0.025% by weight of Ti, less than 0.50% by weight of Cu, less than 0.60% by weight of Mo, and less than 0.50% by weight of Ni.
Claim 4
Dependent Claim
21 words
The method according to claim 1 wherein said reheating temperature is such that the austenite grain size is smaller than 120μ.
Claim 5
Dependent Claim
25 words
The method according to claim 1 wherein said hot rolled steel is cooled from a temperature higher than Ar 3 transformation point plus 20° C.
Claim 6
Dependent Claim
25 words
The method according to claim 3 wherein said hot rolled steel is cooled from a temperature higher than Ar 3 transformation point plus 20° C.
Claim 7
Dependent Claim
69 words
An improved steel having high tensile strength and high toughness characteristics having a two-phase microstructure of fine ferrite and bainite consisting essentially of between 0.03 and 0.15% by weight carbon, 0.05 and 0.60% by weight silicon, 0.60 and 2.5% by weight manganese, 0.1 and 0.15% by weight niobium, 0.005 and 0.10% by weight soluble aluminum, and the remainder essentially iron, produced in accordance with the method of claim 1.
Claim 8
Dependent Claim
55 words
The steel of claim 6, which also contains at least one element selected from the group consisting of titanium in an amount less than 0.025% by weight, copper in an amount less than 0.50% by weight, molybdenum in an amount less than 0.60% by weight, and nickel in an amount less than 0.50% by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |