Silicon nitride-silicon carbide composite material
Assignee: Westinghouse Electric Corp
•
Filing: 1977-12-13
•
Granted: 1980-01-22
•
Expires: 1997-12-13
Abstract
Abstract A densified silicon nitride-silicon carbide composite material formed by hot-pressing a mixture of silicon nitride (Si3N4) powder, which forms the matrix, up to 40 volume percent and preferably from 5-30 volume percent silicon carbide (SiC) powder, and a densification aid such as magnesium oxide (MgO). The average size of the silicon carbide particles is to be less than about 5 microns. The densified composite material is characterized by higher thermal conductivity and strength at high temperatures relative to silicon nitride. The flexural strength at 1400 DEG C. of the composite material being at least double that of sintered silicon nitride.
Inventors
- 👤 Frederick F. Lange
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:31
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
91 words
A composite material formed from sintering and densification under pressure of a mixture of silicon nitride (Si 3 N 4 ) powder, silicon carbide (SiC) powder and an effective amount of a densification aid, the silicon carbide powder being present in the mixture in an amount less than 40 percent by volume and having an average particle size not exceeding about 5 microns, the mixture containing less than about 200 ppm calcium, the densified composite material characterized by improved high temperature flexural strength and thermal conductivity relative to sintered silicon nitride.
Claim 2
Dependent Claim
91 words
A composite material formed from sintering and densification under pressure of a mixture of silicon nitride (Si 3 N 4 ) powder, silicon carbide (SiC) powder and an effective amount of a densification aid, the silicon carbide powder being present in the mixture in an amount less than 40 percent by volume and having an average particle size not exceeding about 5 microns, the mixture containing less than about 200 ppm calcium, the densified composite material characterized by improved high temperature flexural strength and thermal conductivity relative to sintered silicon nitride.
Claim 3
Dependent Claim
27 words
The composite material of claim 1 wherein the densification aid is magnesium oxide (MgO), present in an amount between about 1 percent and 10 percent by weight.
Claim 4
Dependent Claim
19 words
The composite material of claim 2 containing between about 5 percent and about 30 percent by volume silicon carbide.
Claim 5
Dependent Claim
88 words
A hot-pressed, composite material suitable for use as a structural component in gas-turbines consisting essentially of a silicon nitride matrix containing from about 5 percent to about 30 percent by volume of silicon carbide and containing an effective amount of a densification aid, the silicon carbide having an average particle size prior to hot-pressing not in excess of 5 microns and containing less than 200 ppm calcium, the composite material having a density of at least 3.1 grams/cm 3 and a thermal conductivity of at least 0.42 watts/cm°K.
Claim 6
Dependent Claim
88 words
A hot-pressed, composite material suitable for use as a structural component in gas-turbines consisting essentially of a silicon nitride matrix containing from about 5 percent to about 30 percent by volume of silicon carbide and containing an effective amount of a densification aid, the silicon carbide having an average particle size prior to hot-pressing not in excess of 5 microns and containing less than 200 ppm calcium, the composite material having a density of at least 3.1 grams/cm 3 and a thermal conductivity of at least 0.42 watts/cm°K.
Claim 7
Dependent Claim
26 words
The composite material of claim 4 wherein the densification aid is magnesium oxide, present in an amount between about 1 percent and 10 percent by weight.
References Cited (Backward Citations)
US3833389A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-21 | 1983-07-23 | 1984-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-21 | 1987-07-23 | 1988-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-21 | 1991-07-23 | 1992-01-22 | $7700.00 | Window Closed / Lapsed |