Olefin Polymerization catalyst
Assignee: National Petro-Chemicals Corp
•
Filing: 1977-06-29
•
Granted: 1980-01-15
•
Expires: 1997-06-29
Abstract
Abstract Olefin polymerization catalysts are prepared by depositing an organophosphoryl chromium product and an aluminum compound on an inorganic support material, and heating the support material in a non-reducing atmosphere at a temperature above about 300° C. up to the decomposition temperature of the support material.
Inventors
- 👤 Louis J. Rekers
- 👤 Stanley J. Katzen
- 👤 Jerome H. Krekeler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:36
CPC Classifications
C; C08; C08F; C08F110/00; C08F10/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
137 words
A process for the polymerization of 1-olefins comprising providing at least one 1-olefin to an enclosed polymerization zone maintained at elevated temperature and pressure and comprising an olefin polymerization catalyst system consisting essentially of: (a) a solid inorganic support material having surface hydroxyl groups, (b) an organophosphoryl chromium reaction product of chromium trioxide and a phosphorus compound having the formula: ##STR2## wherein R is alkyl, aralkyl, aryl, cycloalkyl or hydrogen, but at least one R is other than hydrogen, said reaction product being deposited on said support (c) an aluminum compound deposited on said support, said aluminum compound being capable of reacting with said surface hydroxyl groups, said supported chromium containing compound and aluminum compound having been heated in a non-reducing atmosphere at a temperature above 300° C. up to the decomposition temperature of the support material.
Claim 2
Dependent Claim
137 words
A process for the polymerization of 1-olefins comprising providing at least one 1-olefin to an enclosed polymerization zone maintained at elevated temperature and pressure and comprising an olefin polymerization catalyst system consisting essentially of: (a) a solid inorganic support material having surface hydroxyl groups, (b) an organophosphoryl chromium reaction product of chromium trioxide and a phosphorus compound having the formula: ##STR2## wherein R is alkyl, aralkyl, aryl, cycloalkyl or hydrogen, but at least one R is other than hydrogen, said reaction product being deposited on said support (c) an aluminum compound deposited on said support, said aluminum compound being capable of reacting with said surface hydroxyl groups, said supported chromium containing compound and aluminum compound having been heated in a non-reducing atmosphere at a temperature above 300° C. up to the decomposition temperature of the support material.
Claim 3
Dependent Claim
56 words
The process of claim 1 wherein the aluminum compound is represented by the formula: Al(X).sub.a (Y).sub.b (Z).sub.c wherein X is R, Y is OR and Z is H or halogen; a is 0-3, b is 0-3, c is 0-3, and a+b+c=3; and R is an alkyl or aryl group having from one to eight carbon atoms.
Claim 4
Dependent Claim
49 words
The process of claim 1 wherein the inorganic support material is a silica gel having a surface area of 200 to 500 m 2 /g, a pore volume above 2.0 cc/g, a major portion of the pore volume being provided by pores having diameters of 300 to 600 A.
Claim 5
Dependent Claim
62 words
The process of claim 1 wherein the chromium containing compound is present in an amount sufficient to provide about 0.25 to about 2.5% by weight of Cr based upon the weight of the support and the aluminum compound is present in an amount sufficient to provide about 0.10 to about 10% by weight of Al based upon the weight of the support.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein the chromium containing compound is the reaction product of chromium trioxide and triethyl phosphate.
Claim 7
Dependent Claim
27 words
The process of claim 1 wherein the chromium containing compound is the reaction product of chromium trioxide and triethyl phosphate and the aluminum compound is aluminum sec-butoxide.
Claim 8
Dependent Claim
29 words
The process of claim 1 wherein the polymerization temperature ranges from about 40° to about 200° C. and the polymerization pressure ranges from about 200 to about 1000 psig.
References Cited (Backward Citations)
US3474080A
Cited
US3704287A
Cited
US3969272A
Cited
US3985676A
Cited
US3901825A
Cited
US4008359A
Cited
US3984351A
Cited
US4049896A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |