Method of producing glass mats using novel glass fiber dispersion composition
Assignee: Building Materials Corp of America
•
Filing: 1978-07-11
•
Granted: 1980-01-15
•
Expires: 1998-07-11
Abstract
Abstract This invention describes an aqueous, glass fiber dispersion composition for making uniform, high strength glass mats which comprises a plurality of glass fibers dispersed in an aqueous system comprising an effective amount of an amine oxide and a derivatized guar gum. A wet-laid process for making such mats using said dispersion composition also is described.
Inventors
- 👤 A. A. Bondoc
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:12
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/61; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/25; D06; D06N; D06N5/00; D21H13/00; D21H13/36; D21H13/38; D21H13/40; D21H23/00; D21H23/02; D21H23/04; D21H23/06; D21H23/08; D21H23/10; D21H5/00; D21H5/12; D21H5/1254; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/26; Y10T428/266; Y10T428/268; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
102 words
A method of producing uniform, high-strength glass mats which comprises: a. dispersing a plurality of glass fibers bundles in an aqueous dispersion comprising an effective amount of an amine oxide surfactant and a derivatized guar gum which is at least about 5 ppm of said amine oxide and at least about 0.05 percent of said guar gum by weight of the aqueous dispersion containing said glass fibers to substantially filamentize said bundles and uniformly disperse the fibers; b. passing said dispersion through a mat-forming screen to form said glass mat while removing said aqueous system therefrom, and; c. recovering said glass mat.
Claim 2
Independent Claim
102 words
A method of producing uniform, high-strength glass mats which comprises: a. dispersing a plurality of glass fibers bundles in an aqueous dispersion comprising an effective amount of an amine oxide surfactant and a derivatized guar gum which is at least about 5 ppm of said amine oxide and at least about 0.05 percent of said guar gum by weight of the aqueous dispersion containing said glass fibers to substantially filamentize said bundles and uniformly disperse the fibers; b. passing said dispersion through a mat-forming screen to form said glass mat while removing said aqueous system therefrom, and; c. recovering said glass mat.
Claim 3
Dependent Claim
22 words
A method according to claim 1 which includes the additional step of recycling the removed aqueous material through the mat forming screen.
Claim 4
Dependent Claim
26 words
A method according to claim 1 wherein said dispersion is diluted to a fiber consistency of about 0.01-1% by weight before being passed through said screen.
Claim 5
Dependent Claim
53 words
A method according to claim 1 wherein said fibers are dispersed to a fiber consistency of about 0.1-2% by weight, said amine oxide is present in said dispersion in an amount of about 5-500 ppm., and said derivatized guar gum is present in a concentration of about 0.05-0.5% by weight of said dispersion.
Claim 6
Dependent Claim
31 words
A method according to claim 1 in which said fiber consistency is about 0.2-1%, said amine oxide concentration is about 10-200 ppm., and said derivatized guar gum concentration is about 0.1-0.3.
Claim 7
Dependent Claim
39 words
A method according to claim 1 in which said fiber dispersion consistency is 0.5%, said amine oxide concentration is 20 ppm of dimethyl hydrogenation tallow amine oxide, and said derivatized guar gum concentration is 0.2% of carboxymethylhydroxypropylated guar gum.
Claim 8
Dependent Claim
15 words
A method according to claim 3 wherein said diluted fiber formation consistency is about 0.02-0.5%.
Claim 9
Dependent Claim
11 words
A method according to claim 3 wherein said consistency is 0.03%.
Claim 10
Dependent Claim
34 words
A method according to claim 1 wherein said fibers are dry or wet chopped fibers having a length of about 1/8-3 inches, a diameter of about 3-20 microns and are sized or unsized fibers.
References Cited (Backward Citations)
CA787649A
Cited
US2599620A
Cited
US2906660A
Cited
US3723409A
Cited
US4052257A
Cited
BE838373A
Cited
US4049491A
Cited
US4031307A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |