Composition and method for coating metal surfaces
Assignee: Union Carbide Corp
•
Filing: 1978-01-30
•
Granted: 1980-01-15
•
Expires: 1998-01-30
Abstract
Abstract This application is concerned with the treatment of metal surfaces with stable solutions of hexavalent chromium, trivalent chromium, phosphoric acid, polyacrylic acid and water dispersible acrylic emulsion polymer to enhance the corrosion resistance and paint adhesion properties of the metal; the coating uniquely having generally universal utility under a wide variety of paint systems and paint types.
Inventors
- 👤 James W. Davis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 04:35
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/12; C23; C23C; C23C22/00; C23C22/05; C23C22/06; C23C22/24; C23C22/33
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
121 words
The method of making a stable aqueous composition for coating metal surfaces to enhance the corrosion resistance and paint adhesion properties thereof, said composition containing, as the coating forming ingredients: hexavalent chromium, trivalent chromium, phosphoric acid, polyacrylic acid, and an acrylic emulsion polymer, and said method comprising: (1) forming an aqueous solution of the chromium trioxide and the phosphoric acid; (2) reducing about 40 to 60% of the hexavalent chromium to trivalent chromium under conditions adapted to completely dissolve all of the reaction products; (3) adding the polyacrylic acid to the partially reduced chromium solution under conditions adapted to insure complete interaction of the reactants present; and (4) adding the acrylic emulsion polymer to the partially reduced chromium polyacrylic acid solution.
Claim 2
Independent Claim
121 words
The method of making a stable aqueous composition for coating metal surfaces to enhance the corrosion resistance and paint adhesion properties thereof, said composition containing, as the coating forming ingredients: hexavalent chromium, trivalent chromium, phosphoric acid, polyacrylic acid, and an acrylic emulsion polymer, and said method comprising: (1) forming an aqueous solution of the chromium trioxide and the phosphoric acid; (2) reducing about 40 to 60% of the hexavalent chromium to trivalent chromium under conditions adapted to completely dissolve all of the reaction products; (3) adding the polyacrylic acid to the partially reduced chromium solution under conditions adapted to insure complete interaction of the reactants present; and (4) adding the acrylic emulsion polymer to the partially reduced chromium polyacrylic acid solution.
Claim 3
Dependent Claim
34 words
The method according to claim 1 wherein from about 46 to 50% of the hexavalent chromium is reduced by means of a reducing agent that will not form objectionable reaction products in the solution.
Claim 4
Dependent Claim
12 words
The method according to claim 2 where the reducing agent is formaldehyde.
Claim 5
Independent Claim
187 words
The method of making a stable aqueous composition for coating metal surfaces to enhance the corrosion resistance and paint adhesion properties thereof and which comprises: (a) dissolving about 41.5 grams chromium trioxide and about 14.5 grams phosphoric acid (100% H 3 PO 4 ) in about 250 to 300 ml water; (b) adding about 4.4 grams formaldehyde (100% HCHO) under conditions adapted to prevent boilover; (c) maintaining the reactants at about 180°-190° F. for sufficient time to effect completion of the partial reduction of the chromium, to eliminate any unreacted formaldehyde and to insure the complete dissolution of the resulting reaction products; (d) diluting the resulting solution with about 300-350 ml water; (e) adding thereto about 76 grams of a polyacrylic acid solution (25% solids weight/volume) in a manner adapted to complete the reaction between the phosphoric acid and chromium values and the polyacrylic acid; (f) bringing the total solution volume to about 800 ml with added water; and (g) thereafter, adding 160 grams of acrylic emulsion polymer dispersion (containing about 46-47% solids weight/volume) diluted to 200 ml with water, to the partially reduced chromium-polyacrylic acid solution.
Claim 6
Independent Claim
187 words
The method of making a stable aqueous composition for coating metal surfaces to enhance the corrosion resistance and paint adhesion properties thereof and which comprises: (a) dissolving about 41.5 grams chromium trioxide and about 14.5 grams phosphoric acid (100% H 3 PO 4 ) in about 250 to 300 ml water; (b) adding about 4.4 grams formaldehyde (100% HCHO) under conditions adapted to prevent boilover; (c) maintaining the reactants at about 180°-190° F. for sufficient time to effect completion of the partial reduction of the chromium, to eliminate any unreacted formaldehyde and to insure the complete dissolution of the resulting reaction products; (d) diluting the resulting solution with about 300-350 ml water; (e) adding thereto about 76 grams of a polyacrylic acid solution (25% solids weight/volume) in a manner adapted to complete the reaction between the phosphoric acid and chromium values and the polyacrylic acid; (f) bringing the total solution volume to about 800 ml with added water; and (g) thereafter, adding 160 grams of acrylic emulsion polymer dispersion (containing about 46-47% solids weight/volume) diluted to 200 ml with water, to the partially reduced chromium-polyacrylic acid solution.
Claim 7
Dependent Claim
12 words
As a composition of matter the stable solution produced by claim 1.
Claim 8
Dependent Claim
96 words
A stable aqueous solution for coating metal surfaces to enhance their corrosion resistance and paint adhesion properties, said solution containing: (a) about 10 parts by weight of chromium trioxide, about 40-55% of which has been reduced to the trivalent state; (b) about 3 to 4 parts by weight of phosphoric acid (100% H 3 PO 4 ); (c) about 4 to 5 parts by weight of polyacrylic acid; (d) about 17 to 20 parts by weight of acrylic emulsion polymer solids: and (e) water to make from about 200 to 4000 parts by weight of solution.
Claim 9
Dependent Claim
96 words
A stable aqueous solution for coating metal surfaces to enhance their corrosion resistance and paint adhesion properties, said solution containing: (a) about 10 parts by weight of chromium trioxide, about 40-55% of which has been reduced to the trivalent state; (b) about 3 to 4 parts by weight of phosphoric acid (100% H 3 PO 4 ); (c) about 4 to 5 parts by weight of polyacrylic acid; (d) about 17 to 20 parts by weight of acrylic emulsion polymer solids: and (e) water to make from about 200 to 4000 parts by weight of solution.
Claim 10
Dependent Claim
90 words
A stable aqueous solution for coating metal surfaces to enhance their corrosion resistance and paint adhesion properties, said solution having a pH between about 1 and 2 and containing: (a) about 8.3 grams of chromium trioxide, about 46-50% of which has been reduced to the trivalent state; (b) about 2.9 grams of phosphoric acid (100% H 3 PO 4 ); (c) about 3.8 grams of polyacrylic acid; (d) about 14.9 grams of acrylic emulsion polymer solids; and (e) water to make from about 200 ml to 4 liters of solution.
Claim 11
Dependent Claim
90 words
A stable aqueous solution for coating metal surfaces to enhance their corrosion resistance and paint adhesion properties, said solution having a pH between about 1 and 2 and containing: (a) about 8.3 grams of chromium trioxide, about 46-50% of which has been reduced to the trivalent state; (b) about 2.9 grams of phosphoric acid (100% H 3 PO 4 ); (c) about 3.8 grams of polyacrylic acid; (d) about 14.9 grams of acrylic emulsion polymer solids; and (e) water to make from about 200 ml to 4 liters of solution.
Claim 12
Independent Claim
38 words
The method of improving the corrosion resistance of a metal surface which comprises contacting the metal surface with the aqueous solutions according to any of claims 5 through 7 and drying and heat curing the thus formed coating.
Claim 13
Dependent Claim
29 words
The method of improving the corrosion resistance and paint adhesion properties of a metal surface according to claim 8 wherein the coated metal surface is iron, aluminum or zinc.
Claim 14
Dependent Claim
13 words
A metal product having a surface treated by the method of claim 8.
Claim 15
Independent Claim
49 words
The method of applying protective coatings to metal surfaces which comprises contacting the metal surface with the aqueous solution according to any of claims 5 through 7, drying the thus treated surface to remove the adhering carrier water, and applying a coating of paint to the thus treated surface.
Claim 16
Dependent Claim
22 words
The method of applying protective coatings to metal surfaces according to claim 11 wherein the paint is a solvent type paint system.
Claim 17
Dependent Claim
22 words
The method of applying protective coatings to metal surfaces according to claim 11 wherein the paint is a water base paint system.
References Cited (Backward Citations)
US3063877A
Cited
US3185596A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |