Temperature sensing resistance device
Assignee: Johnson Service Co
•
Filing: 1977-08-03
•
Granted: 1980-01-15
•
Expires: 1997-08-03
Abstract
Abstract A temperature sensitive thick film resistor unit for use in detecting and control systems is formed employing thick film plating technology. A final sized negative is formed from enlarged artwork and transferred to a photosensitive emulsion supported on a stainless steel screen to form a printing stencil. A fritted molecular bonding nickel paste including finely divided vitreous and nickel particles in a solvent carrier is screen printed onto an alumina substrate by a pressure printer in which the paste is forced through the screen to control the thickness of the deposited nickel paste. The deposited nickel is allowed to settle and partially heated to remove gases and organic solvents. A highly conductive film is overlaid on tab connecting ends and the unit is fired to intimately attach the nickel paste to the substrate by the formation of a chemical bond. Nickel in appropriate form for printing is a readily available material and also provides a significant and linear change in resistance per unit of temperature change.
Inventors
- 👤 Jeannine O. Colla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:23
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/06; H01C17/065; H01C7/00; H01C7/003; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49099; Y10T29/49101; Y10T29/49117; Y10T29/49124; Y10T29/4913; Y10T29/49133; Y10T29/49135; Y10T29/49155; Y10T29/49163
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
113 words
The method of forming a temperature sensitive thick film resistance sensor comprising forming a masking means defining a grid pattern, aligning said masking means on a base member formed of a high temperature, electrical insulating material, forcing an air fireable molecular bonding metallic paste including finely divided metal particles of a pure metal having a high temperature coefficient of resistance through said masking means onto said surface to form a deposited conductive thick film as a grid, and firing at an elevated bonding temperature the subassembly to form the paste to a selected resistivity and temperature coefficient and to sinter the grid and thereby molecularly bonding the thick film to the base member.
Claim 2
Independent Claim
113 words
The method of forming a temperature sensitive thick film resistance sensor comprising forming a masking means defining a grid pattern, aligning said masking means on a base member formed of a high temperature, electrical insulating material, forcing an air fireable molecular bonding metallic paste including finely divided metal particles of a pure metal having a high temperature coefficient of resistance through said masking means onto said surface to form a deposited conductive thick film as a grid, and firing at an elevated bonding temperature the subassembly to form the paste to a selected resistivity and temperature coefficient and to sinter the grid and thereby molecularly bonding the thick film to the base member.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein said paste is a frittless bonding nickel.
Claim 4
Dependent Claim
30 words
The method of claim 1 including the steps of depositing a highly conductive metal film on spaced portions of the thick film, and joining connector leads to the conductive films.
Claim 5
Dependent Claim
23 words
The method of claim 3 wherein said highly conductive metal film is selected from the group consisting of silver, silver-platinum, silver-palladium and gold-palladium.
Claim 6
Dependent Claim
54 words
The method of claim 1 wherein said masking means is formed by providing a printing screen unit including an emulsion film of a preselected thickness attached to a screen of preselected thickness and mesh opening and exposed to a positive image pattern of resistance grid and removing of the unexposed portions of the emulsion.
Claim 7
Dependent Claim
33 words
In the method of claim 5 including the steps of removing the screen unit and allowing the thick film to level, and heating the subassembly to remove volatile materials from the thick film.
Claim 8
Dependent Claim
38 words
In the method of claim 6 including screen printing the conductive metal film onto the thick film after said heating, removing the metal film printing screen and allowing the metal film to level, and again heating the subassembly.
Claim 9
Dependent Claim
23 words
The method of claim 7 wherein said highly conductive metal film is selected from the group consisting of silver, silver-platinum, silver-palladium and gold-palladium.
Claim 10
Dependent Claim
25 words
The method of claim 1 wherein said paste is fritted finely divided vitreous particles and nickel particles uniformly dispersed within an organic binder and solvent.
Claim 11
Dependent Claim
18 words
The method of claim 9 wherein said nickel particles have an average size of less than 20 microns.
Claim 12
Dependent Claim
16 words
The method of claim 3 including the step of attaching connector leads to the nickel grid.
Claim 13
Dependent Claim
28 words
The method of claim 6 including trimming the fired nickel grid to a reference resistance at a preselected temperature, and encapsulating the trimmed subassembly in a protective coating.
Claim 14
Dependent Claim
28 words
The method of claim 3 including trimming the fired nickel grid to a reference resistance at a preselected temperature, and encapsulating the trimmed subassembly in a protective coating.
Claim 15
Dependent Claim
42 words
The method of claim 13 wherein said coating includes forming a bath of polyurethane and a solvent in a viscous state, dipping the trimmed subassembly in the viscous polyurethane, drying said dipped assembly including a final elevated temperature to form said coating.
Claim 16
Independent Claim
202 words
The method of forming a temperature sensitive thick film resistance sensor comprising forming a printing screen unit including an emulsion film of a preselected thickness attached to a screen of preselected thickness and mesh opening and exposed to a positive image pattern of a resistance grid and removing of the unexposed portions of the emulsion, cleaning a high temperature base member formed of a high temperature electric insulating material to remove contaminant thereon, aligning said screen on said base member, forming an air firable nickel paste including finely divided nickel particles thoroughly mixed with vitreous particles and organic binders and solvents forcing said paste through said screen onto said base member to form a nickel grid of a deposited nickel thick film, allowing the deposited nickel thick film to set to promote leveling of the film, heating the subassembly to outgas the deposited nickel thick film, firing the subassembly in a bell-shaped, heat-temperature pattern including a first relatively low temperature period to remove said organic binders and solvents followed by a high temperature period to form the nickel to a selective resistivity and temperature coefficient and to sinter the nickel particles and thereby anchoring the nickel thick film to the base member.
Claim 17
Independent Claim
202 words
The method of forming a temperature sensitive thick film resistance sensor comprising forming a printing screen unit including an emulsion film of a preselected thickness attached to a screen of preselected thickness and mesh opening and exposed to a positive image pattern of a resistance grid and removing of the unexposed portions of the emulsion, cleaning a high temperature base member formed of a high temperature electric insulating material to remove contaminant thereon, aligning said screen on said base member, forming an air firable nickel paste including finely divided nickel particles thoroughly mixed with vitreous particles and organic binders and solvents forcing said paste through said screen onto said base member to form a nickel grid of a deposited nickel thick film, allowing the deposited nickel thick film to set to promote leveling of the film, heating the subassembly to outgas the deposited nickel thick film, firing the subassembly in a bell-shaped, heat-temperature pattern including a first relatively low temperature period to remove said organic binders and solvents followed by a high temperature period to form the nickel to a selective resistivity and temperature coefficient and to sinter the nickel particles and thereby anchoring the nickel thick film to the base member.
Claim 18
Dependent Claim
30 words
The method of claim 15 including the step of screen printing a highly conductive metal film on spaced portions of said nickel thick film and allowing the subassembly to set.
Claim 19
Dependent Claim
23 words
The method of claim 16 wherein said highly conductive metal film is selected from the group consisting of silver, silver-platinum, silver-palladium and gold-palladium.
Claim 20
Dependent Claim
14 words
The method of claim 15 wherein connector leads are joined to the nickel grid.
Claim 21
Dependent Claim
40 words
The method of claim 18 including the step of joining connector leads to the conductive films, trimming the fired nickel grid to a reference resistance at a preselected temperature, and encapsulating the trimmed subassembly in a thin protective conformal coating.
Claim 22
Dependent Claim
41 words
The method of claim 19 wherein said coating includes forming a viscous polyurethane bath of polyurethane and a solvent, dipping the trimmed subassembly in the viscous polyurethane bath, drying said dipped assembly including a final elevated temperature to remove the solvents.
Claim 23
Dependent Claim
14 words
The method of claim 19 wherein said coating is a low temperature glass glaze.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |