Assignee: Shell USA Inc
•
Filing: 1978-10-02
•
Granted: 1980-01-08
•
Expires: 1998-10-02
Abstract
Abstract Polyepoxide resins are reacted with a molar excess of a primary amine to form an amine terminated resin, the amine groups of which are then reacted with a monoepoxide. The primary amine is a mixture of an aliphatic monoamine and an aliphatic diamine which contains one primary amine group and one tertiary amine group. The resinous reaction products can be salted with an acid and can be dissolved or dispersed in water. The aqueous dispersions or solutions can then be formulated into primer coatings for metal objects.
Inventors
- 👤 Darrel D. Hicks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:44
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; C09D5/443; C09D5/4434; C08; C08G; C08G59/00; C08G59/14; C08G59/1433; C08G59/1438; C08G59/145; C08G59/18; C08G59/40; C08G59/50; C08G59/5006; C09D163/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522; Y10T428/31529; Y10T428/31678; Y10T428/31688
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
186 words
A soluble and fusible resinous composition comprising the reaction product of (A) a polyepoxide resin derived from a dihydric phenol or a dihydric alcohol and an epihalohydrin, said polyepoxide resin having a 1,2-epoxide equivalent weight of about 180 to about 650; (B) an amine mixture of (1) an aliphatic monoamine containing about 8 to about 18 carbon atoms, one primary amine group and no other groups reactive with epoxy groups, and (2) an aliphatic diamine containing one primary amine group and one tertiary amine group and no other groups reactive with epoxide groups wherein the molar ratio of (1) and (2) in the mixture varies from about 2:1 to about 1:3, and (C) a monoepoxide which contains one 1,2-epoxide group and no other groups reactive with amine groups, said monoepoxide having about 8 to 24 carbon atoms wherein A, B and C are reacted in the mol ratio of 5:6:2 to 2:3:2, and wherein A and C are added to B at a reaction temperature of about 50° C. to about 150° C. at an addition rate which does not substantially exceed the epoxy-amine reaction rate.
Claim 2
Dependent Claim
186 words
A soluble and fusible resinous composition comprising the reaction product of (A) a polyepoxide resin derived from a dihydric phenol or a dihydric alcohol and an epihalohydrin, said polyepoxide resin having a 1,2-epoxide equivalent weight of about 180 to about 650; (B) an amine mixture of (1) an aliphatic monoamine containing about 8 to about 18 carbon atoms, one primary amine group and no other groups reactive with epoxy groups, and (2) an aliphatic diamine containing one primary amine group and one tertiary amine group and no other groups reactive with epoxide groups wherein the molar ratio of (1) and (2) in the mixture varies from about 2:1 to about 1:3, and (C) a monoepoxide which contains one 1,2-epoxide group and no other groups reactive with amine groups, said monoepoxide having about 8 to 24 carbon atoms wherein A, B and C are reacted in the mol ratio of 5:6:2 to 2:3:2, and wherein A and C are added to B at a reaction temperature of about 50° C. to about 150° C. at an addition rate which does not substantially exceed the epoxy-amine reaction rate.
Claim 3
Dependent Claim
17 words
The composition of claim 1 wherein the reaction temperature is about 75° C. to about 100° C.
Claim 4
Dependent Claim
17 words
The composition of claim 1 wherein (A) and (B) are reacted first followed by reaction with (C).
Claim 5
Dependent Claim
17 words
The composition of claim 1 wherein the polyepoxide resin is derived from a dihydric phenol and epichlorohydrin.
Claim 6
Dependent Claim
27 words
The composition of claim 4 wherein the dihydric phenol is p,p'-dihydroxydiphenyl propane and the polyepoxide resin has an epoxide equivalent weight of about 350 to about 650.
Claim 7
Dependent Claim
16 words
The composition of claim 5 wherein the epoxide equivalent weight is about 425 to about 500.
Claim 8
Dependent Claim
42 words
The composition of claim 1 wherein the aliphatic diamine has the formula ##STR3## wherein R is an alkyl group which contains 2 to 6 carbon atoms and R 1 is hydrogen or an alkyl group which contains one to 2 carbon atoms.
Claim 9
Dependent Claim
11 words
The composition of claim 7 wherein the aliphatic diamine is 3-diethylaminopropylamine.
Claim 10
Dependent Claim
15 words
The composition of claim 1 wherein the aliphatic monoamine contains 12 to 16 carbon atoms.
Claim 11
Dependent Claim
37 words
The composition of claim 1 wherein the monoepoxide is an epoxidized unsaturated hydrocarbon, an epoxidized monoalcohol ester of an unsaturated fatty acid, a monoglycidyl ether of a monohydric alcohol, or a monoglycidyl ester of a monocarboxylic acid.
Claim 12
Dependent Claim
23 words
The composition of claim 1 wherein the polyepoxide resin, the amine mixture and the monoepoxide are reacted in the molar ratio of 3:4:2.
References Cited (Backward Citations)
US2772248A
Cited
US3023190A
Cited
US3278488A
Cited
US3336253A
Cited
US3367991A
Cited
US3719626A
Cited
US3709847A
Cited
US3728302A
Cited
US3801348A
Cited
US3947338A
Cited
US3954762A
Cited
DE2426996A1
Cited
US4093594A
Cited
US4116900A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-07 | 1983-07-09 | 1984-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-07 | 1987-07-09 | 1988-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-07 | 1991-07-09 | 1992-01-08 | $7700.00 | Window Closed / Lapsed |