Polyurethane coating compositions from dicyclopentenyl acrylate and/or methacrylate
Assignee: Rohm and Haas Co
•
Filing: 1978-05-22
•
Granted: 1979-12-25
•
Expires: 1998-05-22
Abstract
Abstract This invention is concerned with autoxidizable coating compositions which contain (a) a member selected from the group consisting of an organic polyisocyanate, a urethane oil, and a uralkyd; (b) at least one non-volatile reactive liquid monomer selected from the group consisting of dicyclopentenyl acrylate and dicyclopentenyl methacrylate; and (c) an effective amount of a polyvalent metal-containing complex or salt that catalyzes the curing of (a) and (b). Use of the non-volatile reactive liquid component enables the production of coating compositions having high application solids content and yet having suitable viscosity for efficient handling. The coatings obtained from the compositions of the present invention combine the typical desirable properties including durability, weather-resistance, etc. of polyurethane coatings and often with unexpected enhancement of the quality of the coatings, such as in respect to toughness, while providing such compositions having higher solids content to facilitate the coating operations therewith.
Inventors
- 👤 William D. Emmons
- 👤 Kayson Nyi
- 👤 Peter R. Sperry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:30
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/30; C08G18/32; C08G18/3271; C08G18/3296; C08G18/04; C08G18/83
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
75 words
A composition having a film-forming binder comprising: (a) a member selected from the group consisting of an organic polyisocyanate, a urethane oil, and a uralkyd; (b) at least one non-volatile reactive liquid monomer selected from the group consisting of dicyclopentenyl acrylate and dicyclopentenyl methacrylate; and (c) an effective amount of a polyvalent metalcontaining complex or salt that catalyzes the curing of (a) and (b), compound (b) being 5 to 95% by weight of the binder.
Claim 2
Dependent Claim
75 words
A composition having a film-forming binder comprising: (a) a member selected from the group consisting of an organic polyisocyanate, a urethane oil, and a uralkyd; (b) at least one non-volatile reactive liquid monomer selected from the group consisting of dicyclopentenyl acrylate and dicyclopentenyl methacrylate; and (c) an effective amount of a polyvalent metalcontaining complex or salt that catalyzes the curing of (a) and (b), compound (b) being 5 to 95% by weight of the binder.
Claim 3
Dependent Claim
16 words
A composition according to claim 1 wherein component (a) is a polyisocyanate comprising an isocyanate-terminated prepolymer.
Claim 4
Dependent Claim
22 words
A composition according to claim 1 wherein component (a) is a urethane oil, wherein the urethane oil is an isocyanate-modified drying oil.
Claim 5
Dependent Claim
20 words
A composition according to claim 1 wherein component (a) is a uralkyd, wherein the uralkyd is an isocyanate-modified alkyd resin.
Claim 6
Dependent Claim
56 words
A composition according to claim 1 having a film-forming binder further comprising: (d) a member selected from the group consisting of (i) an organic compound having a plurality of groups containing a reactive hydrogen atom and (ii) an organic compound having plurality of oxazolidine groups that are moisture-activatable to a condition containing a reactive hydrogen atom.
Claim 7
Dependent Claim
18 words
A composition according to claim 1 wherein component (b) is 10 to 60% by weight of the binder.
Claim 8
Dependent Claim
45 words
A composition according to claim 5 wherein the proportions of binder components (a), (d), and (b) are from about 5% to 95% by weight, up to 80% by weight, and 5% to 95% by weight respectively of the several components based on total binder weight.
Claim 9
Dependent Claim
42 words
A composition according to claim 5 in which the proportions of binder components (a), (d), and (b) are from about 15% to 70%, up to 70%, and 10% to 60% by weight respectively of the several components based on total binder weight.
Claim 10
Dependent Claim
15 words
A composition according to claim 7 wherein component (d) is a hydroxy-terminated polyester or polyether.
Claim 11
Dependent Claim
21 words
A composition according to claim 7 wherein component (d) is a vinyl addition polymer having hydroxyl groups in polymerized units thereof.
Claim 12
Dependent Claim
18 words
A composition according to claim 7 wherein component (d) is a compound containing a plurality of oxazolidine groups.
Claim 13
Dependent Claim
15 words
A composition according to claim 7 wherein component (d) is a polymer of oxazolidinylalkyl (meth)acrylate.
References Cited (Backward Citations)
US2503209A
Cited
US2879248A
Cited
GB794585A
Cited
US3008917A
Cited
DE1492502A1
Cited
US3396210A
Cited
US3642750A
Cited
US3644569A
Cited
US3694389A
Cited
FR2256189A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-24 | 1983-06-25 | 1983-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-24 | 1987-06-25 | 1987-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-24 | 1991-06-25 | 1991-12-25 | $7700.00 | Window Closed / Lapsed |