Abstract
Abstract A silicon nitride base sintered body having high strength and high density is formed by a normal sintering, namely by sintering without pressure. The sintered body is produced of silicon nitride and the metal oxides yttrium oxide and cerium oxide. A silicon nitride base sintered body having yet a higher strength and higher density can be produced by heating yttrium oxide and cerium oxide together for forming Y2O3.2CeO2 before sintering.
Inventors
- 👤 Hideyuki Masaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:08
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
88 words
A method for producing a silicon nitride base sintered body of high strength and density comprising the steps of combining essentially 65 to 96 mol % of silicon nitride powder and 4 to 35 mol % of metal oxides powder composed of yttrium oxide and cerium oxide, the mol ratio of said yttrium oxide to said cerium oxide ranging from 3:7 to 7:3, mixing said combined powdered materials, forming said powdered materials into a green compact and sintering said green compact in a non-oxidizing atmosphere without applying pressure.
Claim 2
Independent Claim
88 words
A method for producing a silicon nitride base sintered body of high strength and density comprising the steps of combining essentially 65 to 96 mol % of silicon nitride powder and 4 to 35 mol % of metal oxides powder composed of yttrium oxide and cerium oxide, the mol ratio of said yttrium oxide to said cerium oxide ranging from 3:7 to 7:3, mixing said combined powdered materials, forming said powdered materials into a green compact and sintering said green compact in a non-oxidizing atmosphere without applying pressure.
Claim 3
Dependent Claim
29 words
The method according to claim 1, wherein said green compact is sintered in a nitrogen atmosphere at a temperature between 1700° and 1900° C. for 3 to 5 hours.
Claim 4
Dependent Claim
21 words
The method according to claim 1, wherein said green compact is formed at a pressure of about 500 kg/cm 2 .
Claim 5
Dependent Claim
18 words
The method according to claim 1, wherein said silicon nitride powder particles have a mean diameter of 3μ.
Claim 6
Dependent Claim
25 words
The method according to claim 4, wherein said yttrium oxide powder and said cerium oxide powder have a mean diameter of 4μ and 7μ respectively.
Claim 7
Dependent Claim
22 words
The method according to claim 1, wherein said metal oxide powder is a compound powder consisting of yttrium oxide and cerium oxide.
Claim 8
Dependent Claim
23 words
The method according to claim 1, wherein said metal oxide powder is a bound powder of yttrium oxide powder and cerium oxide powder.
Claim 9
Dependent Claim
19 words
The method according to claim 1, wherein the ratio of yttrium oxide to cerium oxide, in mols, is 1:2.
Claim 10
Dependent Claim
19 words
The method according to claim 1, wherein the major portion of said silicon nitride is of the alpha type.
Claim 11
Dependent Claim
29 words
The method according to claim 1, further comprising the step of mixing said metal oxides with a binder and drying the resultant bound powder prior to said combining step.
Claim 12
Dependent Claim
61 words
The method according to claim 1, further comprising the step of heating said metal oxide powder prior to combining same with said silicon nitride, said metal oxide powder being heated to a temperature high enough and for a sufficiently long period to produce a quantity of a thermal reaction product effective in increasing the strength and density of said sintered body.
Claim 13
Dependent Claim
45 words
The method according to claim 8, further comprising the steps of heating said metal oxide powder to a temperature high enough and for a period long enough to convert same at least partially to Y 2 O 3 .CeO 2 prior to said combining step.
Claim 14
Dependent Claim
19 words
The method according to claim 12, wherein said metal oxide powder is heated to 1500° C. for 12 hours.
Claim 15
Dependent Claim
34 words
The method according to claim 1, further comprising the step of ball-milling said metal oxides powder in a liquid medium and drying the ball-milled powder prior to combining same with said silicon nitride powder.
Claim 16
Dependent Claim
16 words
The method according to claim 14, wherein said liquid medium contains a binder for said powder.
Claim 17
Dependent Claim
12 words
The method according to claim 15, wherein said binder is polyvinyl alcohol.
Claim 18
Dependent Claim
83 words
The method according to claim 14, further comprising the steps of heating said milled and dried powder to a temperature high enough and for a long enough period to convert at least a portion of said metal oxides to Y 2 O 3 .CeO 2 , the quantity of said double oxide being great enough to yield an increase in the strength and density of said body, and crushing said heated metal oxide powder prior to combining same with said silicon nitride powder.
Claim 19
Dependent Claim
25 words
The method according to claim 17, wherein said heating step consists of heating said metal oxides powder at about 1400° C. for about six hours.
Claim 20
Dependent Claim
21 words
The method according to claim 17, wherein said metal oxide powder is heated to about 1500° C. for about 12 hours.
Claim 21
Dependent Claim
35 words
The method according to claim 19, wherein said heated metal oxide powder is crushed to a mean particle diameter of about 5μ and mixed with silicon nitride in a ball mill using a liquid medium.
Claim 22
Dependent Claim
16 words
The method according to claim 20, wherein said silicon nitride is principally of the alpha type.
Claim 23
Independent Claim
145 words
A method of producing a silicon nitride base sintered body of high strength and density, comprising the steps of combining 65 to 96 mol % of silicon nitride powder with 4 to 35 mol % of metal oxide powder, compacting said powder mixture and sintering same without applying pressure at an effective temperature for a sufficient period of time to effect sintering, said metal oxide powder consisting of oxide of yttrium and cerium, the mol ratio of yttrium to cerium ranging from 3:7 to 7:3, said metal oxide being selected from the group consisting of yttrium oxide together with cerium oxide; yttrium oxide with cerium oxide and the thermal reaction product of yttrium oxide with cerium oxide; and the thermal reaction product of yttrium oxide with cerium oxide; said 4 to 35 mol % of said metal oxides being based on the individual unreacted oxides.
Claim 24
Independent Claim
145 words
A method of producing a silicon nitride base sintered body of high strength and density, comprising the steps of combining 65 to 96 mol % of silicon nitride powder with 4 to 35 mol % of metal oxide powder, compacting said powder mixture and sintering same without applying pressure at an effective temperature for a sufficient period of time to effect sintering, said metal oxide powder consisting of oxide of yttrium and cerium, the mol ratio of yttrium to cerium ranging from 3:7 to 7:3, said metal oxide being selected from the group consisting of yttrium oxide together with cerium oxide; yttrium oxide with cerium oxide and the thermal reaction product of yttrium oxide with cerium oxide; and the thermal reaction product of yttrium oxide with cerium oxide; said 4 to 35 mol % of said metal oxides being based on the individual unreacted oxides.
Claim 25
Dependent Claim
93 words
A composition suitable for production of a sintered body of high strength and density and complex profile by normal sintering, normal sintering being taken to means sintering without the application of pressure, said composition consisting essentially, except for minor impurities, of 65 to 96 mol % of silicon nitride and 4 to 35 mol % of yttrium oxide and cerium oxide in a range of mol ratios from 3:7 to 7:3 where the metals may be present as the single oxides, the double oxide Y 2 O 3 .CeO 2 , or both.
Claim 26
Dependent Claim
93 words
A composition suitable for production of a sintered body of high strength and density and complex profile by normal sintering, normal sintering being taken to means sintering without the application of pressure, said composition consisting essentially, except for minor impurities, of 65 to 96 mol % of silicon nitride and 4 to 35 mol % of yttrium oxide and cerium oxide in a range of mol ratios from 3:7 to 7:3 where the metals may be present as the single oxides, the double oxide Y 2 O 3 .CeO 2 , or both.
Claim 27
Dependent Claim
39 words
A silicon nitride base body, comprising the thermal reaction product of 65 to 96 mol % of silicon nitride, and 4 to 35 mol % of yttrium oxide and cerium oxide in a ratio ranging from 3:7 to 7:3.
Claim 28
Dependent Claim
39 words
A silicon nitride base body, comprising the thermal reaction product of 65 to 96 mol % of silicon nitride, and 4 to 35 mol % of yttrium oxide and cerium oxide in a ratio ranging from 3:7 to 7:3.
References Cited (Backward Citations)
JPS5210462A
Cited
US4043381A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-24 | 1983-06-25 | 1983-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-24 | 1987-06-25 | 1987-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-24 | 1991-06-25 | 1991-12-25 | $7700.00 | Window Closed / Lapsed |