Method of forming a fire-resistant silicate coating
Assignee: Battelle Memorial Institute Inc
•
Filing: 1977-06-03
•
Granted: 1979-12-18
•
Expires: 1997-06-03
Abstract
Abstract A method of protecting an object from fire damage by coating the object with a slurry made from hydrated metal silicate particles and an aqueous alkali metal silicate solution. The slurry is applied before there is significant absorption of water into the particles from the solution. Upon heating, the coating expands to form a foam which, because of the equilibrium of water formed between the particles of sodium silicate, is rigid at high temperatures.
Inventors
- 👤 Reinhard Kalbskopf
- 👤 Felix Trojer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:41
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18; C09D5/185; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/5076; C04B41/5089; C09D1/00; C09D1/02; C09K; C09K21/00; C09K21/02; Y; Y10; Y10T; Y10T156/00; Y10T156/10
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
118 words
A method for protecting a substrate from fire damage by coating said substrate with a tumescent material, said method comprising the steps of: (a) mixing hydrated alkali-metal silicate particles in an aqueous solution of alkali metal silicate to form a suspension of said particles, said particles containing 15 to 20 weight percent of water as water of hydration prior to said mixing step, said aqueous solution containing 40 to 80 weight percent dissolved alkali-metal silicate and 60 to 20 weight percent water prior to said mixing step (b) applying a layer of said suspension to said substrate to form a coating thereon prior to significant absorption of water from said solution portion of said suspension by said particles.
Claim 2
Independent Claim
118 words
A method for protecting a substrate from fire damage by coating said substrate with a tumescent material, said method comprising the steps of: (a) mixing hydrated alkali-metal silicate particles in an aqueous solution of alkali metal silicate to form a suspension of said particles, said particles containing 15 to 20 weight percent of water as water of hydration prior to said mixing step, said aqueous solution containing 40 to 80 weight percent dissolved alkali-metal silicate and 60 to 20 weight percent water prior to said mixing step (b) applying a layer of said suspension to said substrate to form a coating thereon prior to significant absorption of water from said solution portion of said suspension by said particles.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said alkali-metal silicate is sodium silicate having an SiO 2 /Na 2 O molar ratio in the range of from 2 to 3.5.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein said mixing step includes preventing exposure of said suspension to oxygen.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein said alkali-metal particles were formed by drying an aqueous solution of alkali-metal silicate.
Claim 6
Dependent Claim
31 words
The method of claim 4 wherein said coating is rendered substantially opaque to visible light by drying the aqueous solution used to form said particles in a stream of warm air.
Claim 7
Dependent Claim
46 words
The method of claim 4 wherein said coating is rendered substantially transparent to visible light by drying the aqueous solution used to form said particles in the form of a film on a heated solid surface and thereafter fracturing said film to form said particles therefrom.
Claim 8
Dependent Claim
20 words
The method of claim 1, including the step of adhering a protective coating to the outer surface of said coating.
Claim 9
Dependent Claim
14 words
The method of claim 1 wherein reinforcing fibers are also mixed into said suspension.
Claim 10
Dependent Claim
21 words
The method of claim 8 wherein said fibers comprise 2 to 20 weight percent of the total weight of said coating.
Claim 11
Dependent Claim
21 words
The method of claim 1 including the step of adding a layer of fibers to the outer surface of said coating.
Claim 12
Dependent Claim
33 words
The method of claim 10 including the step of soaking said fibers in a solution having a composition substantially similar to said aqueous solution prior to adding said fibers to said outer surface.
Claim 13
Independent Claim
26 words
The method of claims 8 and 10 wherein said fibers are composed of a material selected from the group consisting of glass, rock wool and carbon.
Claim 14
Dependent Claim
22 words
The method of claim 10 including the step of adhering a protective coating to the outer surface of said layer of fibers.
Claim 15
Independent Claim
158 words
A method for protecting a glass substrate from fire damage by coating said substrate with a tumescent material that is substantially transparent to visible light, said method comprising the steps of: (a) mixing hydrated alkali-metal silicate particles in a first aqueous solution of alkali-metal silicate to form a suspension of said particles, said particles having been formed by the drying of an aqueous alkali-metal solution on a heated solid surface to form a solid substantially transparent film thereon, said film containing 15 to 20 weight percent water as water of hydration, said film being fractured to form said particles, said first aqueous solution containing 40 to 80 weight percent dissolved alkali-metal silicate and 20 to 60 weight percent water prior to said mixing step (b) applying a layer of said suspension to said glass substrate to form a substantially transparent coating thereon prior to significant absorption of water from said solution portion of said suspension by said particles.
Claim 16
Independent Claim
158 words
A method for protecting a glass substrate from fire damage by coating said substrate with a tumescent material that is substantially transparent to visible light, said method comprising the steps of: (a) mixing hydrated alkali-metal silicate particles in a first aqueous solution of alkali-metal silicate to form a suspension of said particles, said particles having been formed by the drying of an aqueous alkali-metal solution on a heated solid surface to form a solid substantially transparent film thereon, said film containing 15 to 20 weight percent water as water of hydration, said film being fractured to form said particles, said first aqueous solution containing 40 to 80 weight percent dissolved alkali-metal silicate and 20 to 60 weight percent water prior to said mixing step (b) applying a layer of said suspension to said glass substrate to form a substantially transparent coating thereon prior to significant absorption of water from said solution portion of said suspension by said particles.
Claim 17
Dependent Claim
38 words
The method of claim 14 wherein said alkali-metal silicate is sodium silicate, said silicate of said first aqueous solution and said particles having an SiO 2 /Na 2 O ratio in the range of from 2 to 3.5.
Claim 18
Dependent Claim
21 words
The method of claim 14 including the step of applying a protective coating to the outer surface of said transparent coating.
Claim 19
Dependent Claim
14 words
The method of claim 16 wherein said protective coating is a layer of glass.
References Cited (Backward Citations)
US2046296A
Cited
US2429946A
Cited
GB1006917A
Cited
GB1007485A
Cited
GB1181432A
Cited
US3585052A
Cited
GB1384285A
Cited
US3854987A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-17 | 1983-06-18 | 1983-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-17 | 1987-06-18 | 1987-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-17 | 1991-06-18 | 1991-12-18 | $7700.00 | Window Closed / Lapsed |