Fast curing coating composition
Assignee: Vishay Intertechnology Inc
•
Filing: 1974-07-08
•
Granted: 1979-12-18
•
Expires: 1994-07-08
Abstract
Abstract A rapid curing polybutadiene resin system dielectric coating composition suitable for coating electrical components such as thin film resistors is disclosed. This composition cures very rapidly and greatly improves adhesion to the coated article.
Inventors
- 👤 Lawrence G. Bockstie, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:24
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31645
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
140 words
A dielectric coating composition consisting essentially of (a) from about 35 to 90 parts by weight of a polybutadiene resin system consisting essentially of 45 to 85 parts by weight of a polybutadiene resin having a molecular weight between about 750 to about 14,000, at least about 75 percent concentration of pendant vinyl groups and a molecular structure of ##STR3## 1to 5 parts by weight of at least one catalyst selected from the group consisting of dicumyl peroxide, benzoyl peroxide, lauroyl peroxide, and t-butyl hydroperoxide, and up to 40 parts by weight of at least one reactive monomer selected from the group consisting of vinyl toluene, t-butylstyrene, alkyl substituted styrene and diallyl maleate, and (b) from about 10 to 65 parts by weight of at least one silane selected from the group consisting of vinyltriethoxysilane, vinyl silane, vinyltriacetoxysilane, and vinyltrimethoxysilane.
Claim 2
Dependent Claim
140 words
A dielectric coating composition consisting essentially of (a) from about 35 to 90 parts by weight of a polybutadiene resin system consisting essentially of 45 to 85 parts by weight of a polybutadiene resin having a molecular weight between about 750 to about 14,000, at least about 75 percent concentration of pendant vinyl groups and a molecular structure of ##STR3## 1to 5 parts by weight of at least one catalyst selected from the group consisting of dicumyl peroxide, benzoyl peroxide, lauroyl peroxide, and t-butyl hydroperoxide, and up to 40 parts by weight of at least one reactive monomer selected from the group consisting of vinyl toluene, t-butylstyrene, alkyl substituted styrene and diallyl maleate, and (b) from about 10 to 65 parts by weight of at least one silane selected from the group consisting of vinyltriethoxysilane, vinyl silane, vinyltriacetoxysilane, and vinyltrimethoxysilane.
Claim 3
Dependent Claim
30 words
The dielectric coating composition of claim 1 wherein said at least one monomer is present in the amount of 10 to 40 parts by weight of the polybutadiene resin system.
Claim 4
Dependent Claim
24 words
The dielectric coating composition of claim 1 wherein said polybutadiene resin has a molecular weight of about 10,000 and the catalyst is dicumyl peroxide.
Claim 5
Dependent Claim
35 words
The dielectric coating composition of claim 3 wherein said at least one monomer is present in an amount of about 10 to 40 parts by weight of the polybutadiene resin system and is vinyl toluene.
Claim 6
Dependent Claim
12 words
The dielectric coating composition of claim 4 wherein said silane is vinyltriethoxysilane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-17 | 1983-06-18 | 1983-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-17 | 1987-06-18 | 1987-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-17 | 1991-06-18 | 1991-12-18 | $7700.00 | Window Closed / Lapsed |