Abstract
Abstract In an acidic aqueous coating composition containing dispersed particles of an organic coating-forming material and of the type which forms on a metallic surface immersed therein an organic coating which increases in thickness the longer the surface is immersed in the composition, the improvement comprising including in said composition an acid inhibitor thereby improving the quality of said coating, including reducing or preventing the tendency of said composition to form coatings which contain pinholes or blisters.
Inventors
- 👤 Frank P. Lochel, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:45
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B05D7/142; C; C09; C09D; C09D5/00; C09D5/08; C09D5/088; C23; C23F; C23F11/00; C23F11/08; C23F11/10
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
119 words
In a coating process wherein an autodeposited coating is formed on a metal surface by contacting said surface with an autodepositing composition and wherein the nature of said surface is such that coatings formed from said composition tend to have defects such as pinholes, blisters, craters or bridges, the improvement comprising contacting said surface with an autodepositing composition containing an acid inhibitor soluble in said composition in an amount sufficient to reduce or prevent the tendency of said composition to form coatings which have defects such as pinholes, blisters, craters or bridges, said amount being less than that amount which substantially deters or prevents said composition from forming an autodeposited coating or an autodeposited coating having the desired thickness.
Claim 2
Dependent Claim
119 words
In a coating process wherein an autodeposited coating is formed on a metal surface by contacting said surface with an autodepositing composition and wherein the nature of said surface is such that coatings formed from said composition tend to have defects such as pinholes, blisters, craters or bridges, the improvement comprising contacting said surface with an autodepositing composition containing an acid inhibitor soluble in said composition in an amount sufficient to reduce or prevent the tendency of said composition to form coatings which have defects such as pinholes, blisters, craters or bridges, said amount being less than that amount which substantially deters or prevents said composition from forming an autodeposited coating or an autodeposited coating having the desired thickness.
Claim 3
Dependent Claim
19 words
A process according to claim 1 wherein at least a portion of said surface is a worked metal surface.
Claim 4
Dependent Claim
18 words
A process according to claim 1 wherein at least a portion of said surface is roughened and unworked.
Claim 5
Dependent Claim
39 words
A process according to claim 1 wherein said surface includes intersecting surfaces lying in different planes and wherein said defect includes bridging of that portion of the coating overylying that portion of the metal surface where said surfaces intersect.
Claim 6
Dependent Claim
118 words
In an autodeposition coating process wherein a resinous coating is applied to a metallic surface by immersing said surface in an autodepositing coating composition and wherein the nature of said surface is such that coatings formed from said composition tend to have defects such as pinholes, blisters, craters or bridges, the improvement comprising including in said composition an acid inhibitor soluble in said composition in an amount sufficient to reduce or prevent the tendency of said composition to form coatings which have defects such as pin-holes, blisters, craters or bridges, said amount being less than that amount which substantially deters or prevents said composition from forming an autodeposited coating or an autodeposited coating having the desired thickness. PG,40
Claim 7
Dependent Claim
118 words
In an autodeposition coating process wherein a resinous coating is applied to a metallic surface by immersing said surface in an autodepositing coating composition and wherein the nature of said surface is such that coatings formed from said composition tend to have defects such as pinholes, blisters, craters or bridges, the improvement comprising including in said composition an acid inhibitor soluble in said composition in an amount sufficient to reduce or prevent the tendency of said composition to form coatings which have defects such as pin-holes, blisters, craters or bridges, said amount being less than that amount which substantially deters or prevents said composition from forming an autodeposited coating or an autodeposited coating having the desired thickness. PG,40
Claim 8
Dependent Claim
35 words
A process according to claim 5 wherein said inhibitor is selected from the group consisting of aldehydes, ketones, amines, thiols, mercaptans, sulfides, thioreas, silicates phosphates, carbonates, nitrites, chromates, dichromates, oximes and alkynols and mixtures thereof.
Claim 9
Dependent Claim
21 words
A process according to claim 5 wherein the amount of inhibitor included in said composition is at least about 25 ppm.
Claim 10
Dependent Claim
26 words
A process according to claim 6 wherein the amount of inhibitor included in said composition is within the range of about 25 to about 5000 ppm.
Claim 11
Dependent Claim
20 words
A process according to claim 5 wherein said composition is prepared from styrene/butadiene latex, a soluble ferric-containing compound and HF.
Claim 12
Dependent Claim
13 words
A process according to claim 9 wherein said ferric-containing compound is ferric fluoride.
Claim 13
Dependent Claim
13 words
A process according to claim 10 wherein said composition includes a black pigment.
Claim 14
Dependent Claim
46 words
A process according to claim 5 wherein said acid inhibitor is a mixture of thiourea and the product of a Mannich reaction in which there is reacted, in the presence of hydroxyacetic acid, amines derived from pine resin acids, including mainly dehydroabietylamine, acetophenone, acetone and formaldehyde.
Claim 15
Dependent Claim
19 words
A process according to claim 12 wherein the amount of said inhibitor is about 100 to about 3000 ppm.
Claim 16
Dependent Claim
13 words
A process according to claim 5 wherein said acid inhibitor is propargyl alcohol.
Claim 17
Dependent Claim
20 words
A process according to claim 14 wherein the amount of said propargyl alcohol is about 100 to about 500 ppm.
Claim 18
Dependent Claim
14 words
A process according to claim 5 wherein said metallic surface is a ferriferous surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-10 | 1983-06-11 | 1983-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-10 | 1987-06-11 | 1987-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-10 | 1991-06-11 | 1991-12-11 | $7700.00 | Window Closed / Lapsed |