Low-shrink thermosetting polyesters
Assignee: Owens Corning
•
Filing: 1977-11-14
•
Granted: 1979-12-11
•
Expires: 1997-11-14
Abstract
Abstract This invention pertains to low-shrink polyester molding resin mixtures primarily based on a certain low-shrink thermoplastic additive produced by synthesizing the vinyl copolymer thermoplastic additive in a hydroxyl terminated polymeric diluent. The resulting vinyl copolymer is dispersed in the hydroxyl containing polymeric diluent which can be post reacted with isocyanate material to produce a polyurethane-vinyl copolymer thermoplastic additive. This thermoplastic additive can be added directly to the thermosetting polyester polymer and monomer mixture to provide a low-shrink molding resin system.
Inventors
- 👤 Donald R. Stevenson
- 👤 David A. Schmidt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:14
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/52; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/24; C08K3/26; C08L67/02; C08L71/00; C08L75/00; C08L75/04
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
122 words
A low-shrink polyester molding resin composition for thickening with Group II metal oxides, hydroxides, or alkoxides, and thermosetting to form low-profile molded structures, wherein the resin composition comprises by weight at least about 25% ethylenically unsaturated thermosetting polyester polymer, about 5% to 20% of an acid functional thermoplastic polymer, and about 40% to 60% of an ethylenically unsaturated monomer copolymerizable with said thermosetting polyester polymer, the improvement comprising: said thermoplastic polymer comprising a polymer mixture of vinyl copolymer dispersed in a polymeric diluent wherein the mixture contains by weight between about 60% and 90% vinyl copolymer, said polymeric diluent having number average molecular weight of between about 500 and 5,000 and said polymeric diluent is a linear saturated polyester or polyalkylene oxide.
Claim 2
Dependent Claim
122 words
A low-shrink polyester molding resin composition for thickening with Group II metal oxides, hydroxides, or alkoxides, and thermosetting to form low-profile molded structures, wherein the resin composition comprises by weight at least about 25% ethylenically unsaturated thermosetting polyester polymer, about 5% to 20% of an acid functional thermoplastic polymer, and about 40% to 60% of an ethylenically unsaturated monomer copolymerizable with said thermosetting polyester polymer, the improvement comprising: said thermoplastic polymer comprising a polymer mixture of vinyl copolymer dispersed in a polymeric diluent wherein the mixture contains by weight between about 60% and 90% vinyl copolymer, said polymeric diluent having number average molecular weight of between about 500 and 5,000 and said polymeric diluent is a linear saturated polyester or polyalkylene oxide.
Claim 3
Dependent Claim
47 words
The composition in claim 1 wherein the thermosetting polyester is a dicyclopentadiene modified polyester containing 0.1 to 0.4 moles of dicyclopentadiene per mole of unsaturated dicarboxylic acid wherein the dicyclopentadiene is esterified with carboxyl groups of said dicarboxylic acid, and said composition is a stabilized resin emulsion.
Claim 4
Dependent Claim
51 words
The composition in claim 2 wherein said thermoplastic polymer mixture contains a vinyl copolymer comprising by weight between about 5% and 50% of a lower alkyl ester of acrylic acid or methacrylic acid, between 0.5% and 5% acrylic acid or 0.6% and 6% methacrylic acid, and the balance being vinyl acetate.
Claim 5
Dependent Claim
47 words
The composition in claim 2 wherein the polymeric diluent in said thermoplastic polymer mixture is a hydroxyl terminated polymeric diluent containing between about 0.6% and 8% by weight hydroxyl groups wherein said hydroxyl groups are post-reacted with isocyanate to produce a polyurethane copolymer of said polymeric diluent.
Claim 6
Dependent Claim
21 words
The composition in claim 4 wherein said polyurethane copolymer of diluent contains between about 3% and 20% by weight copolymerized isocyanate.
Claim 7
Dependent Claim
15 words
The composition in claim 4 wherein the polyurethane copolymer of diuent contains copolymerized toluene diisocyanate.
Claim 8
Independent Claim
147 words
A method of producing a low-shrink resin composition suitable for thickening with Group II metal oxides, hydroxides, and alkoxides, and thermosetting to form a low profile molded structure, the resin mixture comprising by weight at least about 25% of a thermosetting ethylenically unsaturated polyester polymer, about 5% to 20% of an acid functional thermoplastic polymer, and about 40% to 60% of an ethylenically unsaturated monomer copolymerizable with said thermosetting polyester, the improvement comprising: providing a thermoplastic mixture of vinyl copolymer and polymeric diluent containing by weight between about 60% and 90% of said vinyl copolymer produced by synthesizing said vinyl copolymer in said diluent as a reaction medium, said polymeric diluent having a molecular weight of between about 500 and 5,000, by heating said polymeric diluent to at least about 75° C. and copolymerizing therein ethylenically unsaturated monomers to form a vinyl copolymer dispersed in said diluent.
Claim 9
Independent Claim
147 words
A method of producing a low-shrink resin composition suitable for thickening with Group II metal oxides, hydroxides, and alkoxides, and thermosetting to form a low profile molded structure, the resin mixture comprising by weight at least about 25% of a thermosetting ethylenically unsaturated polyester polymer, about 5% to 20% of an acid functional thermoplastic polymer, and about 40% to 60% of an ethylenically unsaturated monomer copolymerizable with said thermosetting polyester, the improvement comprising: providing a thermoplastic mixture of vinyl copolymer and polymeric diluent containing by weight between about 60% and 90% of said vinyl copolymer produced by synthesizing said vinyl copolymer in said diluent as a reaction medium, said polymeric diluent having a molecular weight of between about 500 and 5,000, by heating said polymeric diluent to at least about 75° C. and copolymerizing therein ethylenically unsaturated monomers to form a vinyl copolymer dispersed in said diluent.
Claim 10
Dependent Claim
79 words
The method of claim 7 wherein the polymeric diluent is liquid and has a viscosity of between about 80 and 800 centipoises at 25° C., and is heated to between about 100° C. and 200° C. wherein said vinyl copolymer synthesized from ethylenically unsaturated monomers comprising by weight between about 5% and 50% of a lower alkyl ester of acrylic or methacrylic acid, 0.5% to 5% acrylic or 0.6% to 6% methacrylic acid, and the balance being vinyl acetate.
Claim 11
Dependent Claim
48 words
The method of claim 7 wherein the thermosetting polyester is a dicyclopentadiene terminated ethylenically unsaturated polyester polymer containing dicyclopentadiene esterified with carboxylic acid and containing between about 0.1 to 0.4 moles of dicyclopentadiene per 1 mole of dicarboxylic acid, and said resin mixture is a stabilized resin emulsion.
Claim 12
Dependent Claim
40 words
The method of claim 7 wherein the polymeric diluent is a hydroxyl terminated polymeric diluent containing between about 0.6% and 8% hydroxyl groups, and said hydroxyl terminated polymeric diluent is post-reacted with isocyanate to form a polyurethane copolymer of diluent.
Claim 13
Dependent Claim
19 words
The method of claim 7 wherein the polymeric diluent is a polyalkylene oxide polymer or a saturated polyester polymer.
Claim 14
Dependent Claim
11 words
The product produced in accordance with the method of claim 7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-10 | 1983-06-11 | 1983-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-10 | 1987-06-11 | 1987-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-10 | 1991-06-11 | 1991-12-11 | $7700.00 | Window Closed / Lapsed |