US4177157A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Precoagulated PTFE-bound electrodes
Assignee: Motors Liquidation Co
•
Filing: 1978-04-05
•
Granted: 1979-12-04
•
Expires: 1998-04-05
Abstract
Abstract Non-sintered PTFE-bound electrodes for alkaline storage batteries are made by coagulating polytetrafluoroethylene (i.e. PTFE) particles from an aqueous dispersion thereof to form a gelatinous coagulum, mechanically dispersing the coagulum in water such that the coagulum is subdivided into small, sticky clots of PTFE particles which are suspended in the water, mixing the suspension with comminuted electrochemically active material to form a slurry of active material and active-material-coated clots, filtering the slurry to separate the solids (i.e. as a filter cake) therefrom, integrating (e.g. sandwiching) an electrically conductive current collector with the filter cake, compressing the thusly formed composite, and drying the compress.
Inventors
- 👤 Richard L. Adams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:48
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/04; H01M4/0402; H01M4/0404; H01M4/0416; H01M4/043; H01M4/0433; H01M4/24; H01M4/26; H01M4/32; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
159 words
In the process of making alkaline battery electrodes of the non-sintered, polymer-bound type including the principal steps of slurrying comminuted electrode active material and coagulated binder in a suitable suspension medium, filtering the slurry to remove said active material and binder from said medium as a filter cake, integrating said filter cake with a conductive current collector, compressing the current collector and cake, and drying the thusly formed compress, the improvement comprising: mixing a coagulant with an aqueous dispersion of fine polytetrafluoroethylene particles to form a coagulum of said particles; mechanically dispersing said coagulum in water such as to subdivide said coagulum into small irregularly shaped, sticky clots of said particles and suspend them in the water; and mixing the thusly formed aqueous suspension with said active material to form said slurry, whereby said clots become coated with said active material during said slurrying, and said coated clots interlock together during said compressing for forming a coherent mass thereof.
Claim 2
Dependent Claim
159 words
In the process of making alkaline battery electrodes of the non-sintered, polymer-bound type including the principal steps of slurrying comminuted electrode active material and coagulated binder in a suitable suspension medium, filtering the slurry to remove said active material and binder from said medium as a filter cake, integrating said filter cake with a conductive current collector, compressing the current collector and cake, and drying the thusly formed compress, the improvement comprising: mixing a coagulant with an aqueous dispersion of fine polytetrafluoroethylene particles to form a coagulum of said particles; mechanically dispersing said coagulum in water such as to subdivide said coagulum into small irregularly shaped, sticky clots of said particles and suspend them in the water; and mixing the thusly formed aqueous suspension with said active material to form said slurry, whereby said clots become coated with said active material during said slurrying, and said coated clots interlock together during said compressing for forming a coherent mass thereof.
Claim 3
Dependent Claim
145 words
A process for making non-sintered, polytetrafluoroethylene-bound nickel electrodes for alkaline storage batteries comprising the steps of: mixing a coagulant with an aqueous dispersion of polytetrafluoroethylene particles to form a coagulum of said particles; mechanically stirring said coagulum in water such as to disperse and suspend said coagulum therein as small irregularly-shaped, sticky clots of said particles; slurrying the thusly formed suspension together with comminuted nickel hydroxide and graphite such that said nickel hydroxide and graphite adhere as a coating to the surface of said clots; filtering the coated clots from the slurry and forming a filter cake therefrom; integrating a conductive current collector with said filter cake; compressing said cake and current collector to densify the cake, to enhance the electrical conductivity within the compress and to interlock the coated clots one with the other into a coherent mass; and drying the thusly formed compress.
Claim 4
Dependent Claim
145 words
A process for making non-sintered, polytetrafluoroethylene-bound nickel electrodes for alkaline storage batteries comprising the steps of: mixing a coagulant with an aqueous dispersion of polytetrafluoroethylene particles to form a coagulum of said particles; mechanically stirring said coagulum in water such as to disperse and suspend said coagulum therein as small irregularly-shaped, sticky clots of said particles; slurrying the thusly formed suspension together with comminuted nickel hydroxide and graphite such that said nickel hydroxide and graphite adhere as a coating to the surface of said clots; filtering the coated clots from the slurry and forming a filter cake therefrom; integrating a conductive current collector with said filter cake; compressing said cake and current collector to densify the cake, to enhance the electrical conductivity within the compress and to interlock the coated clots one with the other into a coherent mass; and drying the thusly formed compress.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-03 | 1983-06-04 | 1983-12-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-03 | 1987-06-04 | 1987-12-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-03 | 1991-06-04 | 1991-12-04 | $7700.00 | Window Closed / Lapsed |