US4176104A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polystyrene phonograph record injection molding compositions of improved transparency
Assignee: Polysar Inc
•
Filing: 1978-07-07
•
Granted: 1979-11-27
•
Expires: 1998-07-07
Abstract
Abstract Phonograph record molding compositions having polystyrene as the major constituent are formulated to have wear resistance properties superior to other polystyrene injection molded compositions while generally retaining the transparency of unmodified polystryene. Ethylene-bis-stearamide or a homolog or analog thereof is dissolved within styrene monomer and then the monomer is polymerized to obtain a polystryene matrix having a molecular distribution of ethylene-bis-stearamide or the like within and throughout the matrix. Preferably, the ethylene-bis-stearamide or the like is combined with a wax such as an olefin-based wax or a microcrystalline wax.
Inventors
- 👤 Henry Alsberg
- 👤 Dale Skalla
- 👤 William C. Meisenhelder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 14:13
CPC Classifications
G; G11; G11B; G11B3/00; G11B3/68; G11B3/70; G11B3/705; C; C08; C08K; C08K5/00; C08K5/16; C08K5/20
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
97 words
A phonograph record injection molding composition comprising a modified styrene polymer composition, said modified styrene polymer being a polymerization product of styrene polymerized with a lubricity-enhancing modifier dissolved therewithin, said lubricity-enhancing modifier having the following structure: ##STR2## wherein R is alkyl having from about 14 to about 19 carbon atoms and R' is alkane having from about 2 to about 5 carbon atoms, said modified styrene polymer being a polystyrene matrix having said lubricity-enhancing modifier generally molecularly distributed within and throughout said matrix, and said modified styrene polymer being a substantially transparent phonograph record injection molding composition.
Claim 2
Dependent Claim
97 words
A phonograph record injection molding composition comprising a modified styrene polymer composition, said modified styrene polymer being a polymerization product of styrene polymerized with a lubricity-enhancing modifier dissolved therewithin, said lubricity-enhancing modifier having the following structure: ##STR2## wherein R is alkyl having from about 14 to about 19 carbon atoms and R' is alkane having from about 2 to about 5 carbon atoms, said modified styrene polymer being a polystyrene matrix having said lubricity-enhancing modifier generally molecularly distributed within and throughout said matrix, and said modified styrene polymer being a substantially transparent phonograph record injection molding composition.
Claim 3
Dependent Claim
11 words
The molding composition of claim 1, wherein R is straight-chain alkyl.
Claim 4
Dependent Claim
32 words
The molding composition of claim 1, wherein said modified styrene polymer includes from about 0.5 to about 4 weight percent of said lubricity-enhancing modifier, based on the total weight of the polymer.
Claim 5
Dependent Claim
32 words
The molding composition of claim 1, wherein said modified styrene polymer includes from about 1 to about 3 weight percent of said lubricity-enhancing modifier, based on the total weight of the polymer.
Claim 6
Dependent Claim
12 words
The molding composition of claim 1, wherein said lubricity-enhancing modifier is ethylene-bis-stearamide.
Claim 7
Dependent Claim
56 words
The molding composition of claim 1, wherein said modified styrene polymer further includes dissolved therein a secondary lubricating agent additive in an amount such that the total quantity of said lubricity-enhancing modifier and said secondary lubricating agent additive together is between about 1 and about 6 weight percent, based on the total weight of the polymer.
Claim 8
Dependent Claim
20 words
The molding composition of claim 6, wherein said total quantity together is between about 3 and about 5 weight percent.
Claim 9
Dependent Claim
28 words
The molding composition of claim 6, wherein said secondary lubricating agent additive is a wax selected from the group consisting of a microcrystalline wax and an olefin-based wax.
Claim 10
Dependent Claim
32 words
The molding composition of claim 1, wherein said modified styrene polymer further includes dissolved therein up to about 2 weight percent of a flow promoter, based on the weight of the polymer.
Claim 11
Dependent Claim
37 words
The molding composition of claim 1, wherein said modified styrene polymer further includes dissolved therein between about 0.25 and about 1 weight percent of a mineral oil flow promoter, based on the total weight of the polymer.
Claim 12
Dependent Claim
56 words
The molding composition of claim 1, wherein said injection molding composition exhibits wear resistance in the absence of a metal stearate within said modified styrene polymer, said wear resistance being substantially equal to that of said injection molding composition that has been modified to contain a metal stearate therewithin and to exclude said lubricity-enhancing modifier therewithin.
Claim 13
Dependent Claim
103 words
The molding composition of claim 1, comprising between about 1 to about 3 weight percent of ethylene-bis-stearamide as said lubricity-enhancing modifier, wherein said modified styrene polymer further includes dissolved therein between about 1 to about 3 weight percent of a wax selected from the group consisting of microcrystalline wax and olefin-based wax, and wherein said injection molding composition exhibits wear resistance in the absence of a metal stearate within said modified styrene polymer, said wear resistance being substantially equal to that of said injection molding composition that has been modified to contain a metal stearate therewithin and to exclude said lubricity-enhancing modifier therewithin.
Claim 14
Independent Claim
77 words
A method for preparing phonograph record injection molding compositions, comprising providing a styrene monomer, dissolving a lubricity-enhancing modifier within said styrene monomer to form a modified styrene formulation, said lubricity-enhancing modifier having the structure: ##STR3## wherein R is alkyl having from about 14 to about 19 carbon atoms and R' is alkane having from about 2 to about 5 carbon atoms, and polymerizing said modified styrene formulation into a composition for injection molding substantially transparent phonograph records.
Claim 15
Independent Claim
77 words
A method for preparing phonograph record injection molding compositions, comprising providing a styrene monomer, dissolving a lubricity-enhancing modifier within said styrene monomer to form a modified styrene formulation, said lubricity-enhancing modifier having the structure: ##STR3## wherein R is alkyl having from about 14 to about 19 carbon atoms and R' is alkane having from about 2 to about 5 carbon atoms, and polymerizing said modified styrene formulation into a composition for injection molding substantially transparent phonograph records.
Claim 16
Dependent Claim
28 words
The method of claim 13, wherein said dissolving step incorporates from about 0.5 to about 4 weight percent of said lubricity enhancing modifier into said modified styrene formulation.
Claim 17
Dependent Claim
54 words
The method of claim 13, further comprising dissolving a secondary lubricating agent additive into said modified styrene formulation in an amount such that the total quantity of said lubricity-enhancing modifier and said secondary lubricating agent additive together is between about 1 and about 6 weight percent, based on the total weight of the formulation.
Claim 18
Dependent Claim
31 words
The method of claim 13, further comprising dissolving up to about 2 weight percent of a flow promoter into said modified styrene formulation, based on the total weight of the formulation.
Claim 19
Dependent Claim
51 words
The method of claim 13, further comprising avoiding addition of a metal stearate to said modified styrene formulation while simultaneously maintaining phonograph record wear resistance properties substantially equal to those of said phonograph record molding composition which has been modified to contain a metal stearate and to exclude said lubricity-enhancing modifier.
Claim 20
Dependent Claim
23 words
The method of claim 13, further comprising injection molding said phonograph record molding composition into a substantially transparent and wear resistant phonograph record.
Claim 21
Dependent Claim
36 words
The method of claim 18, wherein said injection molding step includes injecting said molding composition at a temperature between about 400° and 450° F. and quenching same at a temperature of about 77° to 150° F.
Claim 22
Dependent Claim
93 words
A injection molded phonograph record comprising a substantially transparent matrix of polymerized, injection molded modified styrene polymer, said polymer being a polymerization product of styrene polymerized with a lubricity-enhancing modifier dissolved therewithin, said matrix having generally molecularly distributed within and throughout said matrix from about 0.5 to about 4 weight percent, based on the total weight of the matrix, of said lubricity-enhancing modifier of the following structure: ##STR4## wherein R is alkyl having from about 14 to about 19 carbon atoms and R' is alkane having from about 2 to 5 carbon atoms.
Claim 23
Dependent Claim
93 words
A injection molded phonograph record comprising a substantially transparent matrix of polymerized, injection molded modified styrene polymer, said polymer being a polymerization product of styrene polymerized with a lubricity-enhancing modifier dissolved therewithin, said matrix having generally molecularly distributed within and throughout said matrix from about 0.5 to about 4 weight percent, based on the total weight of the matrix, of said lubricity-enhancing modifier of the following structure: ##STR4## wherein R is alkyl having from about 14 to about 19 carbon atoms and R' is alkane having from about 2 to 5 carbon atoms.
Claim 24
Dependent Claim
77 words
The phonograph record of claim 20, wherein said substantially transparent matrix further includes from about 1 to about 3 weight percent, based on the total weight of the matrix, of a microcrystalline wax or an olefin-based wax, and wherein the molded phonograph record has wear resistance properties substantially equal to non-transparent phonograph records that are injection molded from said modified sytrene polymer which has been modified to contain a metal stearate and to exclude said lubricity-enhancing modifier.
Claim 25
Dependent Claim
24 words
The phonograph record of claim 20, wherein said lubricity-enhancing modifier is ethylene-bis-stearamide which is present at from about 1 to about 3 weight percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-26 | 1983-05-28 | 1983-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-26 | 1987-05-28 | 1987-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-26 | 1991-05-28 | 1991-11-27 | $7700.00 | Window Closed / Lapsed |