Assignee: AT&T Inc
•
Filing: 1978-12-27
•
Granted: 1979-11-27
•
Expires: 1998-12-27
Abstract
Abstract A process is described for loading nickel electrodes in porous plaques using an electrolytic technique. The process involves use of a counter electrolyte covered with a cobalt compound. This process is highly efficient because less hydrogen ions are liberated during the impregnation process and less buffering substance is needed to stabilize the pH of the solution.
Inventors
- 👤 Thomas D. O'Sullivan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:59
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/26; H01M4/28; H01M4/29; H01M4/32; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
65 words
A process for producing alkaline batteries with nickel electrodes in which the nickel electrodes are made by electrolytic loading of a porous structure including the step of passing current through the porous structure, an aqueous electrolyte comprising nickel ions, and a counter electrode characterized in that the counter electrode is at least partially coated with a substance comprising cobalt compound with 50-60 weight percent cobalt.
Claim 2
Dependent Claim
65 words
A process for producing alkaline batteries with nickel electrodes in which the nickel electrodes are made by electrolytic loading of a porous structure including the step of passing current through the porous structure, an aqueous electrolyte comprising nickel ions, and a counter electrode characterized in that the counter electrode is at least partially coated with a substance comprising cobalt compound with 50-60 weight percent cobalt.
Claim 3
Dependent Claim
46 words
The process of claim 1 in which the electrolyte loading is carried out with a current density in the range from 0.05-5.0 Amperes per square inch, for a time period of 20 minutes to 4 hours and an electrolyte temperature from 80 degrees C. to boiling.
Claim 4
Dependent Claim
28 words
The process of claim 2 in which the initial concentration of nickel ions is from 0.1 M to saturation and the initial pH is from 0.5 to 5.0.
Claim 5
Dependent Claim
25 words
The process of claim 3 in which the electrolyte initially comprises nitrate ions to control pH in the concentration range from 0.1 M to saturation.
Claim 6
Dependent Claim
21 words
The process of claim 1 in which the remainder of the cobalt compound comprises oxygen and hydrogen chemically bonded to cobalt.
Claim 7
Dependent Claim
17 words
The process of claim 5 in which the weight percent cobalt in the cobalt compound is 56±2.
Claim 8
Dependent Claim
30 words
The process of claim 1 in which the aqueous electrolyte comprises nickel and cobalt ions with cobalt ion concentration between 1 and 30 mole percent of the nickel ion concentration.
Claim 9
Dependent Claim
86 words
A process for producing alkaline batteries with nickel electrodes in which the nickel electrodes are made by electrolytic loading of a porous structure including the step of passing current through the porous structure, an aqueous electrolyte comprising nickel ions and a counter electrode characterized in that the counter electrode is at least partially coated with a substance comprising cobalt compound made by an electrolytic process including the step of passing current through the counter electrode, an aqueous bath comprising soluble cobalt ions and an inert anode.
Claim 10
Dependent Claim
86 words
A process for producing alkaline batteries with nickel electrodes in which the nickel electrodes are made by electrolytic loading of a porous structure including the step of passing current through the porous structure, an aqueous electrolyte comprising nickel ions and a counter electrode characterized in that the counter electrode is at least partially coated with a substance comprising cobalt compound made by an electrolytic process including the step of passing current through the counter electrode, an aqueous bath comprising soluble cobalt ions and an inert anode.
Claim 11
Dependent Claim
22 words
The process of claim 8 in which the aqueous bath contains cobalt nitrate in the concentration range from 0.1 M to saturation.
Claim 12
Dependent Claim
20 words
The process of claim 9 in which the concentration range of cobalt nitrate is from 0.5 molar to 4 molar.
Claim 13
Dependent Claim
28 words
The process of claim 10 in which the process for preparing the counter electrode is carried out at a current density of from 0.1-5.0 Amperes per square inch.
Claim 14
Dependent Claim
27 words
The process of claim 11 in which the process for preparing the counter electrode is carried out at a temperature ranging from 80 degrees C. to boiling.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-26 | 1983-05-28 | 1983-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-26 | 1987-05-28 | 1987-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-26 | 1991-05-28 | 1991-11-27 | $7700.00 | Window Closed / Lapsed |