US4173685A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Coating material and method of applying same for producing wear and corrosion resistant coated articles
Assignee: Praxair ST Technology Inc
•
Filing: 1978-05-23
•
Granted: 1979-11-06
•
Expires: 1998-05-23
Abstract
Abstract Wear and corrosion resistant coatings are obtained using the plasma or d-gun techniques and applying a coating material consisting of carbides and nickel-containing base alloy having 6-18 wt.% boron.
Inventors
- 👤 Merle H. Weatherly
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 09:03
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/04; C23C4/06; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/32; B23K35/327; C23C4/18; Y; Y10; Y10S; Y10S417/00; Y10S417/01; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/934; Y10S428/935; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12063; Y10T428/12069; Y10T428/12076; Y10T428/12083; Y10T428/12097; Y10T428/12139
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
133 words
A powder composition for deposition by a method producing a coating having an as-deposited density greater than 75 percent theoretical on a metal substrate, such coating having high wear and corrosion resistance comprising two or more components (a) the first component consisting of 0-25 wt.% of at least one binder taken from the class consisting of cobalt, iron, nickel and alloys thereof and at least one metal carbide taken from the class consisting of tungsten, chromium, vanadium, hafnium, titanium, zirconium, niobium, molybdenum, tantalum carbides, and compounds thereof; (b) the second component consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% boron; 0-6 wt.% silicon; 0-20 wt.% chromium; 0-5 wt.% iron; balance nickel; said first component comprising 40-75 wt.% of the entire composition.
Claim 2
Dependent Claim
133 words
A powder composition for deposition by a method producing a coating having an as-deposited density greater than 75 percent theoretical on a metal substrate, such coating having high wear and corrosion resistance comprising two or more components (a) the first component consisting of 0-25 wt.% of at least one binder taken from the class consisting of cobalt, iron, nickel and alloys thereof and at least one metal carbide taken from the class consisting of tungsten, chromium, vanadium, hafnium, titanium, zirconium, niobium, molybdenum, tantalum carbides, and compounds thereof; (b) the second component consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% boron; 0-6 wt.% silicon; 0-20 wt.% chromium; 0-5 wt.% iron; balance nickel; said first component comprising 40-75 wt.% of the entire composition.
Claim 3
Dependent Claim
56 words
A powder composition for deposition over a metal carbide coating having a density greater than 75 percent theoretical on a metallic substrate, such powder consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% B; 0-6 wt.% Si; 0-20 wt.% Cr; 0-5 wt.% Fe; balance nickel.
Claim 4
Dependent Claim
56 words
A powder composition for deposition over a metal carbide coating having a density greater than 75 percent theoretical on a metallic substrate, such powder consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% B; 0-6 wt.% Si; 0-20 wt.% Cr; 0-5 wt.% Fe; balance nickel.
Claim 5
Dependent Claim
14 words
A powder composition according to claim 1 wherein the metal carbide is tungsten carbide.
Claim 6
Dependent Claim
14 words
A powder composition according to claim 1 wherein the metal carbide is titanium carbide.
Claim 7
Dependent Claim
14 words
A powder composition according to claim 1 wherein the metal carbide is vanadium carbide.
Claim 8
Dependent Claim
22 words
A powder composition according to claim 1 wherein the metal carbide is a mixture and/or compound of vanadium carbide and tungsten carbide.
Claim 9
Dependent Claim
21 words
A powder composition according to claim 3 wherein the tungsten carbide is formed from 3.20 to 6.13 wt.% carbon; balance tungsten.
Claim 10
Dependent Claim
18 words
A powder composition according to claim 3 wherein the tungsten carbide is 75-55 wt.% of the total composition.
Claim 11
Dependent Claim
24 words
A powder composition according to claim 1 wherein the metal carbide is tungsten carbide and the boron content of the powder is 6-11 wt.%.
Claim 12
Independent Claim
212 words
A method for producing a coating on a metallic substrate, such coating having high wear and corrosion resistance comprising (a) depositing by a method capable of producing a coating having an as-deposited density greater than 75 percent theoretical, a composition comprising two or more components; the first component consisting of 0-25 wt.% of at least one binder taken from the class consisting of cobalt, iron, nickel and alloys thereof and at least one metal carbide taken from the class consisting of tungsten, chromium, vanadium, hafnium, titanium, zirconium, niobium, molybdenum, tantalum carbides, and compounds thereof; the second component consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% boron; 0-6 wt.% silicon; 0-20 wt.% chromium; 0-5 wt.% iron; balance nickel; said first component comprising 40-75 wt.% of the entire composition; (b) heating such deposited coating at a temperature greater than 950° C. and for a time sufficient to cause substantial melting of said second component and reaction of said second component with a substantial portion of said first component; (c) cooling the coating allowing the formation of borides, carbides and intermetallic phases resulting in a coating having a hardness greater than 1000 DPH 300 and being virtually fully dense with no interconnected porosity.
Claim 13
Independent Claim
212 words
A method for producing a coating on a metallic substrate, such coating having high wear and corrosion resistance comprising (a) depositing by a method capable of producing a coating having an as-deposited density greater than 75 percent theoretical, a composition comprising two or more components; the first component consisting of 0-25 wt.% of at least one binder taken from the class consisting of cobalt, iron, nickel and alloys thereof and at least one metal carbide taken from the class consisting of tungsten, chromium, vanadium, hafnium, titanium, zirconium, niobium, molybdenum, tantalum carbides, and compounds thereof; the second component consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% boron; 0-6 wt.% silicon; 0-20 wt.% chromium; 0-5 wt.% iron; balance nickel; said first component comprising 40-75 wt.% of the entire composition; (b) heating such deposited coating at a temperature greater than 950° C. and for a time sufficient to cause substantial melting of said second component and reaction of said second component with a substantial portion of said first component; (c) cooling the coating allowing the formation of borides, carbides and intermetallic phases resulting in a coating having a hardness greater than 1000 DPH 300 and being virtually fully dense with no interconnected porosity.
Claim 14
Dependent Claim
29 words
A method according to claim 12 wherein step (a) is carried out by the plasma technique and the deposited coating has a density greater than 75 percent of theoretical.
Claim 15
Dependent Claim
29 words
A method according to claim 10 wherein step (a) is carried out by the d-gun technique and the deposited coating has a density of greater than 95 percent theoretical.
Claim 16
Independent Claim
205 words
A method for producing a coating on a metallic substrate, such coating having high wear and corrosion resistance comprising (a) depositing by a method capable of producing a coating having an as-deposited density greater than 75 percent theoretical, a composition consisting of 0-25 wt.% of at least one of a binder taken from the class consisting of cobalt, iron, nickel and alloys thereof and at least one metal carbide taken from the class consisting of tungsten, chromium, vanadium, hafnium, titanium, zirconium, niobium, molybdenum, tantalum carbides, and compounds thereof; (b) depositing over said coating deposited by step (a) a composition consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% boron; 0-6 wt.% silicon; 0-20 wt.% chromium; 0-5 wt.% iron; balance nickel; (c) heating the so-deposited coating of steps (a) and (b) at a temperature greater than 950° C. and for a time sufficient to cause the coating of step (b) to penetrate and react with the coating of step (a); and (d) cooling the coating allowing the formation of borides, carbides and intermetallic phases resulting in a coating having a hardness greater than 1000 DPH 300 and being virtually fully dense with no interconnected porosity.
Claim 17
Independent Claim
205 words
A method for producing a coating on a metallic substrate, such coating having high wear and corrosion resistance comprising (a) depositing by a method capable of producing a coating having an as-deposited density greater than 75 percent theoretical, a composition consisting of 0-25 wt.% of at least one of a binder taken from the class consisting of cobalt, iron, nickel and alloys thereof and at least one metal carbide taken from the class consisting of tungsten, chromium, vanadium, hafnium, titanium, zirconium, niobium, molybdenum, tantalum carbides, and compounds thereof; (b) depositing over said coating deposited by step (a) a composition consisting essentially of a single alloy or a mixture of alloys with a total composition of 6.0 to 18.0 wt.% boron; 0-6 wt.% silicon; 0-20 wt.% chromium; 0-5 wt.% iron; balance nickel; (c) heating the so-deposited coating of steps (a) and (b) at a temperature greater than 950° C. and for a time sufficient to cause the coating of step (b) to penetrate and react with the coating of step (a); and (d) cooling the coating allowing the formation of borides, carbides and intermetallic phases resulting in a coating having a hardness greater than 1000 DPH 300 and being virtually fully dense with no interconnected porosity.
Claim 18
Dependent Claim
15 words
A method according to claim 13 wherein step (a) is performed by the plasma technique.
Claim 19
Dependent Claim
15 words
A method according to claim 13 wherein step (a) is performed by the d-gun technique.
Claim 20
Dependent Claim
38 words
A method according to claim 13 wherein the binder is cobalt and the metal carbide is tungsten carbide and the weight ratio of the coating of step (b) to the coating of step (a) is 0.09 to 0.65.
Claim 21
Dependent Claim
28 words
A method according to claim 16 wherein the cobalt is 10-25 wt.% and the tungsten carbide is 90 to 75 wt.% of the coating deposited by step (a).
Claim 22
Dependent Claim
50 words
A method according to claim 17 wherein the coating deposited by step (a) is deposited by the plasma technique and the composition of the coating deposited by step (b) is 6.0 to 11.0 boron; 2.0 to 4.0 Si; 3.0 to 15.0 Cr; 0 to 2.0 Fe; and the balance Ni.
Claim 23
Dependent Claim
50 words
A method according to claim 17 wherein the coating deposited by step (a) is deposited by the d-gun technique and the composition of the coating deposited by step (b) is 6.0 to 11.0 boron; 2.0 to 4.0 Si; 3.0 to 15.0 Cr; 0 to 2.0 Fe and the balance Ni.
Claim 24
Dependent Claim
14 words
A method according to claim 16 wherein the weight ratio is 0.35 to 0.40.
Claim 25
Dependent Claim
67 words
A coating on a metallic substrate, said coating consisting of an interdiffusion zone with said substrate, and intermediate zone consisting of a gradient of borides, carbides and intermetallics in a metal matrix and a hard outer zone which may consist of one or more layers, said outer zone containing large, angular borides, carbides and intermetallic particles, and having a hardness of 1000 to 2200 DPH 300 .
Claim 26
Dependent Claim
67 words
A coating on a metallic substrate, said coating consisting of an interdiffusion zone with said substrate, and intermediate zone consisting of a gradient of borides, carbides and intermetallics in a metal matrix and a hard outer zone which may consist of one or more layers, said outer zone containing large, angular borides, carbides and intermetallic particles, and having a hardness of 1000 to 2200 DPH 300 .
References Cited (Backward Citations)
US2899338A
Cited
US1342801A
Cited
US2401221A
Cited
US2581252A
Cited
US2612442A
Cited
US2752666A
Cited
US2942970A
Cited
US2875043A
Cited
US3025182A
Cited
US2936229A
Cited
US3305326A
Cited
US3341337A
Cited
US3743556A
Cited
US3936295A
Cited
US4013453A
Cited
US4075371A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-05 | 1983-05-07 | 1983-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-05 | 1987-05-07 | 1987-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-05 | 1991-05-07 | 1991-11-06 | $7700.00 | Window Closed / Lapsed |