Soft-seeded tougheners for polyvinyl chloride

Claim 1

A composition comprising polymer particles prepared by (a) providing a seed latex wherein the polymer particles have an average size in the range of from about 200 to 2000 A and a T g less than about 20° C., said seed consisting essentially of a polymer derived from an alkyl acrylate monomer and from about 0.1 to about 5 weight percent cross-linking monomer or a copolymer derived from a major amount, by weight, of an alkyl acrylate monomer, a minor amount, by weight, of an addition monomer and from about 0.1 to about 5 weight percent cross-linking monomer, the alkyl moiety of the alkyl acrylate monomer comprising an aliphatic or alicyclic hydrocarbon radical having 3 to 12 carbon atoms and the addition monomer being selected from the group consisting of vinyl, acrylic acid ester and nitrile functional monomers derived from acrylic acid esters; (b) contacting said polymer particles within the latex with butadiene monomer or a monomer mixture containing butadiene and an alkyl acrylate ester or butadiene and an addition monomer under conditions designed for the overpolymerization of said monomers on the polymer particles of the latex to the substantial exclusion of the formation of new polymer particles therefrom; and (c) contacting the overpolymerized polymer particles of said latex formed in step (b) with a monomer mixture containing an α-aryl substituted monoolefin and an α-alkyl alkylacrylate ester monomer under conditions designed for overpolymerization of said monomers on the polymer particles of the latex to the substantial exclusion of the formation of new polymer particles within said latex; the relative proportion of structural units in the copolymer component of step (b) being adjusted to insure that such component is elastomeric in nature, and the relative proportion of structural units in the copolymer component of step (c) being adjusted to insure that such component is harder than the component of step (b); and the relative concentration in the composition of the component of step (a) being in the range of from about 5 to about 20 weight percent; the concentration of the component of step (b) being in the range of from about 50 to about 75 weight percent; and, the concentration of components of step (c) being in the range of from about 15 to about 40 weight percent.

Claim 11

A method for extending the useful life of rigid polymers by enhancing their impact resistance, said method comprising modifying said rigid polymer by incorporation therein an impact modifier effective amount of polymer particles prepared by (a) providing a seed latex wherein the polymer particles have an average size in the range of from about 200 to 2000 A and a T g less than about 20° C., said seed consisting essentially of a polymer derived from an alkyl acrylate monomer and from about 0.1 to about 5 weight percent cross-linking monomer or a copolymer derived from a major amount, by weight, of an alkyl acrylate monomer, a minor amount, by weight, of an addition monomer and from about 0.1 to about 5 weight percent cross-linking monomer, the alkyl moiety of the alkyl acrylate monomer comprising an aliphatic or alicyclic hydrocarbon radical having 3 to 12 carbon atoms and the addition monomer being selected from the group consisting of vinyls, acrylic acid esters and nitrile functional monomers derived from acrylic acid esters; (b) contacting said polymer particles within the latex with butadiene monomer or a monomer mixture containing butadiene and an alkyl acrylate ester or butadiene and an addition monomer under conditions designed for overpolymerization of said monomers on the polymer particles of the latex to the substantial exclusion of the formation of new polymer particles therefrom; and (c) contacting the overpolymerized polymer particles of said latex formed in step (b) with a monomer mixture containing an α-aryl substituted monoolefin and an α-alkyl alkylacrylate ester monomer under conditions designed for overpolymerization of said monomers on the polymer particles of the latex to the substantial exclusion of the formation of new polymer particles within said latex; the relative proportion of structural units in the copolymer component of step (b) being adjusted to insure that such components is elastomeric in nature, and the relative proportion of structural units in the copolymer component of step (c) being adjusted to insure that such component is harder than the component of step (b); and the relative concentration in the thermoplastic composition of the component of step (a) being in the range of from about 5 to about 20 weight percent; the concentration of the component of step (b) being in the range of from about 50 to about 75 weight percent; and, the concentration of components of step (c) being in the range of from about 15 to about 40 weight percent.

Claim 12

A method for extending the useful life of rigid polymers by enhancing their impact resistance, said method comprising modifying said rigid polymer by incorporation therein an impact modifier effective amount of polymer particles prepared by (a) providing a seed latex wherein the polymer particles have an average size in the range of from about 200 to 2000 A and a T g less than about 20° C., said seed consisting essentially of a polymer derived from an alkyl acrylate monomer and from about 0.1 to about 5 weight percent cross-linking monomer or a copolymer derived from a major amount, by weight, of an alkyl acrylate monomer, a minor amount, by weight, of an addition monomer and from about 0.1 to about 5 weight percent cross-linking monomer, the alkyl moiety of the alkyl acrylate monomer comprising an aliphatic or alicyclic hydrocarbon radical having 3 to 12 carbon atoms and the addition monomer being selected from the group consisting of vinyls, acrylic acid esters and nitrile functional monomers derived from acrylic acid esters; (b) contacting said polymer particles within the latex with butadiene monomer or a monomer mixture containing butadiene and an alkyl acrylate ester or butadiene and an addition monomer under conditions designed for overpolymerization of said monomers on the polymer particles of the latex to the substantial exclusion of the formation of new polymer particles therefrom; and (c) contacting the overpolymerized polymer particles of said latex formed in step (b) with a monomer mixture containing an α-aryl substituted monoolefin and an α-alkyl alkylacrylate ester monomer under conditions designed for overpolymerization of said monomers on the polymer particles of the latex to the substantial exclusion of the formation of new polymer particles within said latex; the relative proportion of structural units in the copolymer component of step (b) being adjusted to insure that such components is elastomeric in nature, and the relative proportion of structural units in the copolymer component of step (c) being adjusted to insure that such component is harder than the component of step (b); and the relative concentration in the thermoplastic composition of the component of step (a) being in the range of from about 5 to about 20 weight percent; the concentration of the component of step (b) being in the range of from about 50 to about 75 weight percent; and, the concentration of components of step (c) being in the range of from about 15 to about 40 weight percent.