US4173466A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Magnesium-containing treatment agents
Assignee: Foseco International Ltd
•
Filing: 1977-12-06
•
Granted: 1979-11-06
•
Expires: 1997-12-06
Abstract
Abstract Treatment agents are described for use in nodularizing cast iron in the production of ductile iron and also useful in deoxidizing steel and desulphurizing cast iron. The agents take the form of a compacted mixture comprising particulate iron, magnesium and calcium, and are distinguished by (a) a magnesium content of 5 to 15% by weight (b) a weight ratio of magnesium to calcium in the range of from 1:1 to 8:1 (c) the iron having a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (d) being compacted into a body of density at least 4.3 gm/cm3. The high density allows the agent to be used effectively by a simple overpour technique.
Inventors
- 👤 John R. McLaughlin
- 👤 Michael D. Bryant
- 👤 Manfred Fessel
- 👤 Kenneth C. Taylor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:21
CPC Classifications
C; C21; C21C; C21C7/00; C21C7/04; C21C7/06; C21C1/00; C21C1/02; C21C1/025; C21C1/10; C21C1/105
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
81 words
A treatment agent which is a compacted mixture comprising particulate iron, magnesium and calcium, wherein (1) the magnesium content is 5 to 15% by weight (2) the weight ratio of magnesium to calcium is in the range of from 1:1 to 8:1 (3) the iron has a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (4) the mixture is compacted into a body of density at least 4.3 gm/cm 3 .
Claim 2
Dependent Claim
81 words
A treatment agent which is a compacted mixture comprising particulate iron, magnesium and calcium, wherein (1) the magnesium content is 5 to 15% by weight (2) the weight ratio of magnesium to calcium is in the range of from 1:1 to 8:1 (3) the iron has a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (4) the mixture is compacted into a body of density at least 4.3 gm/cm 3 .
Claim 3
Dependent Claim
22 words
The treatment agent of claim 1 wherein the weight ratio of magnesium to calcium is in the range of 4.5:1 to 1:1.
Claim 4
Dependent Claim
18 words
The treatment agent of claim 1 wherein the magnesium is of particle size all less than 0.7 mm.
Claim 5
Dependent Claim
26 words
The treatment agent of claim 1 wherein the magnesium is of purity at least 99% by weight and all of particle size 0.15 to 0.40 mm.
Claim 6
Dependent Claim
17 words
The treatment agent of claim 1 wherein the calcium is present in the form of calcium silicide.
Claim 7
Dependent Claim
25 words
The treatment agent of claim 1 wherein the iron is in the form of sponge iron with a particle size all less than 0.2 mm.
Claim 8
Dependent Claim
25 words
The treatment agent of claim 1 wherein the iron is in the the form of steel with a particle size all less than 0.2 mm.
Claim 9
Dependent Claim
29 words
The treatment agent of claim 1 and including at least one component selected from the class consisting of alkaline earth metals other than calcium, rare earth metals and tin.
Claim 10
Dependent Claim
15 words
The treatment agent of claim 1 and including up to 5% by weight of carbon.
Claim 11
Dependent Claim
20 words
The treatment agent of claim 1 in the form of tablets each of volume 0.5 to 10 cm 3 .
Claim 12
Dependent Claim
117 words
In the method of nodularising molten iron in the production of ductile iron which comprises locating in a metallurgical vessel a quantity of a treatment agent and pouring molten iron into the vessel, the improvement comprising using as the treatment agent a compacted mixture comprising particulate iron, magnesium and calcium, wherein (1) the magnesium content is 5 to 15% by weight (2) the weight ratio of magnesium to calcium is in the range of from 1:1 to 8:1 (3) the iron has a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (4) the mixture is compacted into a body of density at least 4.3 gm/cm 3 .
Claim 13
Dependent Claim
117 words
In the method of nodularising molten iron in the production of ductile iron which comprises locating in a metallurgical vessel a quantity of a treatment agent and pouring molten iron into the vessel, the improvement comprising using as the treatment agent a compacted mixture comprising particulate iron, magnesium and calcium, wherein (1) the magnesium content is 5 to 15% by weight (2) the weight ratio of magnesium to calcium is in the range of from 1:1 to 8:1 (3) the iron has a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (4) the mixture is compacted into a body of density at least 4.3 gm/cm 3 .
Claim 14
Dependent Claim
28 words
The method of claim 11 wherein the quantity of treatment agent placed in the vessel is 0.5 to 3.0% by weight of the molten metal to be treated.
Claim 15
Dependent Claim
114 words
In a method of deoxidising steel or desulphurising iron which comprises locating in a metallurgical vessel a quantity of treatment agent and pouring steel or iron respectively into the vessel, the improvement comprising using as the treatment agent a compacted mixture comprising particulate iron, magnesium and calcium, wherein (1) the magnesium content is 5 to 15% by weight (2) the weight ratio of magnesium to calcium is in the range of from 1:1 to 8:1 (3) the iron has a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (4) the mixture is compacted into a body of density at least 4.3 gm/cm 3 .
Claim 16
Dependent Claim
114 words
In a method of deoxidising steel or desulphurising iron which comprises locating in a metallurgical vessel a quantity of treatment agent and pouring steel or iron respectively into the vessel, the improvement comprising using as the treatment agent a compacted mixture comprising particulate iron, magnesium and calcium, wherein (1) the magnesium content is 5 to 15% by weight (2) the weight ratio of magnesium to calcium is in the range of from 1:1 to 8:1 (3) the iron has a purity of at least 95% by weight and a particle size of all less than 0.5 mm and (4) the mixture is compacted into a body of density at least 4.3 gm/cm 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-05 | 1983-05-07 | 1983-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-05 | 1987-05-07 | 1987-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-05 | 1991-05-07 | 1991-11-06 | $7700.00 | Window Closed / Lapsed |