Electrochemical cell and method of assembly
Assignee: United States Department of Energy
•
Filing: 1978-06-29
•
Granted: 1979-10-30
•
Expires: 1998-06-29
Abstract
Abstract A method of preparing an electrochemical cell is disclosed which permits the assembly to be accomplished in air. The cell includes a metal sulfide as the positive electrode reactant, lithium alloy as the negative electrode reactant and an alkali metal, molten salt electrolyte. Positive electrode reactant is introduced as Li2FeS2, a single-phase compound produced by the reaction of Li2S and FeS. The use of this compound permits introduction of lithium in an oxidized form. Additional lithium can be introduced in the negative electrode structure enclosed within an aluminum foil envelope between layers of porous aluminum. Molten salt electrolyte is added after assembly and evacuation of the cell by including an interelectrode separator that has been prewet with an organic solution of KCl.
Inventors
- 👤 Hiroshi Shimotake
- 👤 Ernst C. H. Voss
- 👤 Louis G. Bartholme
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 02:52
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/399; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
132 words
A method of assembling an electrochemical cell in air, the cell including a metal sulfide positive electrode, a lithium alloy negative electrode, a porous and electrically insulative interelectrode separator and an electrolytic salt mixture including alkali metal halides comprising: preparing a positive electrode including reactant material in the form of Li 2 FeS 2 , preparing a negative electrode including a layer of porous metalloid or lithium-metalloid alloy, the metalloid being selected from the group consisting of aluminum and silicon; prewetting a porous electrically insulative separator layer with an organic solution of an alkali metal halide; sealing the positive electrode, negative electrode, and interelectrode separator within a cell housing; evacuating the housing and filling with molten electrolytic salt mixture; and electrically cycling the cell to form lithium-metalloid alloy in the negative electrode.
Claim 2
Independent Claim
132 words
A method of assembling an electrochemical cell in air, the cell including a metal sulfide positive electrode, a lithium alloy negative electrode, a porous and electrically insulative interelectrode separator and an electrolytic salt mixture including alkali metal halides comprising: preparing a positive electrode including reactant material in the form of Li 2 FeS 2 , preparing a negative electrode including a layer of porous metalloid or lithium-metalloid alloy, the metalloid being selected from the group consisting of aluminum and silicon; prewetting a porous electrically insulative separator layer with an organic solution of an alkali metal halide; sealing the positive electrode, negative electrode, and interelectrode separator within a cell housing; evacuating the housing and filling with molten electrolytic salt mixture; and electrically cycling the cell to form lithium-metalloid alloy in the negative electrode.
Claim 3
Dependent Claim
36 words
The method of claim 1 wherein said positive electrode reactant material is provided in particulate form and is blended with an alkali metal halide consisting of particulate KCl for incorporation into an integral, positive electrode structure.
Claim 4
Dependent Claim
40 words
The method of claim 1 wherein said negative electrode is prepared by sealing a layer of lithium or lithium-metalloid alloy within an envelope of metalloid foil and assembling said sealed layer with a layer of porous metalloid or lithium-metalloid alloy.
Claim 5
Dependent Claim
38 words
The method of claim 1 wherein said negative electrode is prepared by sealing a layer of lithium metal within an aluminum foil envelope and assembling said envelope between two layers of porous aluminum to provide an electrode structure.
Claim 6
Dependent Claim
65 words
The method of claim 1 wherein said negative electrode is prepared by pressing together a layer of lithium foil with a layer of aluminum foil at a temperature above the melting point of lithium followed by sealing the resulting alloy in an envelope of aluminum foil, the sealed aluminum foil envelope is pressed between two layers of porous aluminum to form an integral electrode structure.
Claim 7
Dependent Claim
33 words
The method of claim 1 wherein said organic solution comprises an alcohol selected from the group consisting of methanol, ethanol, propanol and isopropanol and said alkali metal halide dissolved therein consists of KCl.
Claim 8
Dependent Claim
18 words
The method of claim 1 wherein said cell is assembled in air having less than 30% relative humidity.
Claim 9
Dependent Claim
15 words
The method of claim 1 wherein said molten electrolytic salt mixture comprises LiCl and KCl.
Claim 10
Dependent Claim
117 words
An electrochemical cell including a metal sulfide as a positive electrode reactant and lithium as a negative electrode reactant assembled in less than the fully charged state comprising: in the positive electrode, reactant material consisting essentially of Li 2 FeS 2 blended with an alkali metal halide consisting essentially of KCl; in the negative electrode a compact formed of a first layer consisting essentially of porous aluminum and a second layer comprising lithium or lithium-aluminum alloy sealed within an envelope of aluminum foil; a porous, electrically insulative separator permeated with an alkali metal halide consisting essentially of KCl disposed between the positive and negative electrode; and electrolytic salt including an alkali metal halide between the two electrodes.
Claim 11
Dependent Claim
117 words
An electrochemical cell including a metal sulfide as a positive electrode reactant and lithium as a negative electrode reactant assembled in less than the fully charged state comprising: in the positive electrode, reactant material consisting essentially of Li 2 FeS 2 blended with an alkali metal halide consisting essentially of KCl; in the negative electrode a compact formed of a first layer consisting essentially of porous aluminum and a second layer comprising lithium or lithium-aluminum alloy sealed within an envelope of aluminum foil; a porous, electrically insulative separator permeated with an alkali metal halide consisting essentially of KCl disposed between the positive and negative electrode; and electrolytic salt including an alkali metal halide between the two electrodes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-29 | 1983-04-30 | 1983-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-29 | 1987-04-30 | 1987-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-29 | 1991-04-30 | 1991-10-30 | $7700.00 | Window Closed / Lapsed |