Assignee: National Research Development Corp UK
•
Filing: 1978-07-17
•
Granted: 1979-10-30
•
Expires: 1998-07-17
Abstract
Abstract Solid aluminum nitride, deposited for example, in epitaxial layers, is prepared by reacting aluminum and selenium to form aluminum monoselenide, and transporting the aluminum monoselenide in an inert carrier gas to a heated deposition zone where it is contacted with and reacts with nitrogen to give the aluminum nitride, the carrier gas flushing away elemental selenium also produced in the deposition zone.
Inventors
- 👤 Peter M. Dryburgh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:56
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/02; C01; C01B; C01B21/00; C01B21/06; C01B21/072; C30B29/00; C30B29/10; C30B29/40; C30B29/403
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
94 words
A process for the production of aluminum nitride including the steps of heating aluminum and selenium at a temperature at which they react together to form aluminum monoselenide, transporting aluminum monoselenide so formed in an inert carrier gas to a reaction zone heated at a temperature in the order of 1500° C., at which aluminum monoselenide reacts with nitrogen to yield aluminum nitride, introducing nitrogen into said zone together with said aluminum monoselenide to form solid aluminum nitride, and flushing away elemental selenium produced by said reaction in said zone by said inert gas.
Claim 2
Dependent Claim
94 words
A process for the production of aluminum nitride including the steps of heating aluminum and selenium at a temperature at which they react together to form aluminum monoselenide, transporting aluminum monoselenide so formed in an inert carrier gas to a reaction zone heated at a temperature in the order of 1500° C., at which aluminum monoselenide reacts with nitrogen to yield aluminum nitride, introducing nitrogen into said zone together with said aluminum monoselenide to form solid aluminum nitride, and flushing away elemental selenium produced by said reaction in said zone by said inert gas.
Claim 3
Dependent Claim
15 words
A process as in claim 1 and wherein said inert gas is a noble gas.
Claim 4
Dependent Claim
13 words
A process as in claim 1 and wherein said inert gas is helium.
Claim 5
Dependent Claim
20 words
A process as in claim 1 and wherein said nitrogen is supplied to said reaction zone with said inert gas.
Claim 6
Dependent Claim
35 words
A process as in claim 4 wherein the rate of flow of said inert gas is about 1 liter per minute and the rate of flow of said nitrogen is about 1 liter per minute.
Claim 7
Dependent Claim
17 words
A process as in claim 1 wherein the temperature of said reaction zone is about 1550° C.
Claim 8
Dependent Claim
16 words
A process as in claim 1 wherein said aluminum nitride is deposited epitaxially on a substrate.
Claim 9
Dependent Claim
13 words
A process as in claim 7 and wherein said substrate is aluminum oxide.
Claim 10
Dependent Claim
21 words
A process as in claim 1 wherein said aluminum and selenium are in the relative molar proportions of 2 to 1.
Claim 11
Dependent Claim
41 words
The process of claim 1 wherein said reaction of aluminum and selenium and said reaction of aluminum monoselenide and nitrogen take place in a single reaction vessel, the temperature of said vessel being in the range 1500° C. to 1600° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-29 | 1983-04-30 | 1983-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-29 | 1987-04-30 | 1987-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-29 | 1991-04-30 | 1991-10-30 | $7700.00 | Window Closed / Lapsed |