US4172318A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of joining manganese zinc ferrite pole pieces
Assignee: Skyworks Solutions Inc
•
Filing: 1977-08-17
•
Granted: 1979-10-30
•
Expires: 1997-08-17
Abstract
Abstract A method of joining two manganese zinc ferrite pole pieces, to form a product suitable for use in radio frequency recording apparatus, and especially for multi-core magnetic heads, is disclosed. Chromium layers are formed on each manganese zinc ferrite pole piece, on opposed faces thereof, and then the chromium layers are bonded together by means of a suitable adhesive, such as a high strength epoxy adhesive.
Inventors
- 👤 Robert L. Huntt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:23
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/127; G11B5/187; G11B5/23; G11B5/235; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/4902; Y10T29/49021; Y10T29/49032; Y10T29/49036; Y10T29/49039
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
126 words
A process for increasing the wear resistance of a magnetic recording/reproducing head, said head comprising a core of magnetic hot-pressed manganese zinc ferrite material having opposed pole faces defining at least one gap therein between, said process comprising first forming a layer of chromium on each of said pole faces by R.F. sputtering the chromium thereon, with the two chromium layers being of a thickness of at least 90% of the width of said gap, and thereafter adhering the resulting chromium layers together by applying a high termperature epoxy adhesive at least 1 microinch thick to the area of the gap between said chromium layers, and curing the epoxy adhesive at a temperature below 400° C. to adhere the chromium layers together by the epoxy adhesive.
Claim 2
Dependent Claim
126 words
A process for increasing the wear resistance of a magnetic recording/reproducing head, said head comprising a core of magnetic hot-pressed manganese zinc ferrite material having opposed pole faces defining at least one gap therein between, said process comprising first forming a layer of chromium on each of said pole faces by R.F. sputtering the chromium thereon, with the two chromium layers being of a thickness of at least 90% of the width of said gap, and thereafter adhering the resulting chromium layers together by applying a high termperature epoxy adhesive at least 1 microinch thick to the area of the gap between said chromium layers, and curing the epoxy adhesive at a temperature below 400° C. to adhere the chromium layers together by the epoxy adhesive.
Claim 3
Dependent Claim
16 words
Process of claim 1, wherein the epoxy adhesive is cured at a temperature of 250°-350° C.
Claim 4
Dependent Claim
17 words
Process of claim 1, wherein the width of said gap is about 10 to about 500 microinches.
Claim 5
Dependent Claim
21 words
Process of claim 3, wherein each chromium layer has a thickness of about 45 to about 49.9% of the gap thickness.
Claim 6
Dependent Claim
17 words
Process according to claim 4, wherein the maximum thickness of said adhesive layer is about 10 microinches.
Claim 7
Dependent Claim
16 words
Process of claim 5, wherein each of said chromium layers is of substantially the same thickness.
Claim 8
Dependent Claim
18 words
Process of claim 6, wherein the total thickness of said gap is about 40 to about 200 microinches.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-29 | 1983-04-30 | 1983-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-29 | 1987-04-30 | 1987-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-29 | 1991-04-30 | 1991-10-30 | $7700.00 | Window Closed / Lapsed |